The effect of direct aging treatment on microstructure and mechanical properties of the GH4099 superalloys produced by selective laser melting

The effect of direct aging (DA) treatment on microstructure and mechanical properties of the GH4099 superalloys produced by selective laser melting (SLM) was investigated by the microhardness tests, room- (RT) and high-temperature (HT) tensile tests, field emission scanning electron microscopy (FE-SEM), and electron backscattered diffraction (EBSD) in this study. Both microhardness and RT tensile results show that DA treatment improves mechanical properties more than solution-aging (SA) treatment. By analyzing the effect of the microstructural features on the yield strength, we found that the dominant strengthening mechanisms responsible for higher yield strength of the DA specimens are the grain size hardening of fine γ matrix, high-density dislocation strengthening, Orowan dislocation bypass strengthening of smaller but dense M ₂₃C ₆-type carbides, and chemical strengthening of smaller but dense γ΄ nanoprecipitates. Furthermore, a transgranular fracture is a dominant fracture type for RT tensile specimens produced by DA treatment. Conversely, the failure type of SA tensile specimens is a typical intergranular fracture mechanism. The underlying mechanism for the above phenomenon is attributed to the effects of transgranular and intergranular M ₂₃C ₆-type carbides.