Effect of tensile cracks on the corrosion protection properties of anodic oxide films on 5083 Al alloy
Source abstract
Abstract
Sulphuric Acid Anodic Oxide (AAO) film is a common method for corrosion protection of 5083 Al alloys, and cracks may occur in the AAO film due to stress damage. In this study, cracks in the AAO film on 5083 Al alloy were pre-prepared by mechanical tension, and the cracks on the corrosion protection property of AAO film were in-situ investigated by scanning electrochemical microscopy (SECM). The morphology and composition of the AAO film were measured by SEM, XRD and XPS. The results show that the corrosion protection performance of AAO film for 5083 Al alloy decreases with the increase of cracks, which is due to the fact that cracks can act as diffusion channels for corrosive media, resulting in serious corrosion reaction. SECM shows the local current at the cracks of the AAO film first increases and then decreases due to the cracks being gradually repaired by the deposited corrosion products (Al(OH) 3, Al(OH) 2Cl, and AlOOH). A repair mechanism of cracks in AAO film on 5083 Al alloys is revealed during the corrosion process.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Anodic Oxide Films and Nanostructures · Corrosion Behavior and Inhibition · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (43)
Show source-provided references
1. Mechanical, fatigue and microstructural properties of friction stir welded 5083-H111 and 6082-T651 aluminum alloys10.1016/j.matdes.2013.10.090 ↗
2. The strength and thermal stability of Al–5Mg alloys nano-engineered using methods of metal forming10.1016/j.msea.2012.06.068 ↗
3. A comparative study of 5083 aluminium alloy and 316L stainless steel for shipbuilding material
4. Surface modification of 5083 aluminum-magnesium induced by marine microorganisms10.1016/j.corsci.2021.109934 ↗
5. Mechanical and corrosion behaviour of aluminum alloy 5083 and its weldment for marine applications
6. Optimization of corrosion protection potential for stress corrosion cracking and hydrogen embrittlement of 5083-H112 alloy in seawater10.3365/met.mat.2008.04.203 ↗
7. Influence of an anodized layer on the adhesion and surface protective performance of organic coatings on AA2024 aerospace Al alloy
8. The adhesion properties and corrosion performance of differently pretreated epoxy coatings on an aluminium alloy10.1016/j.corsci.2010.02.014 ↗
9. Enhanced surface properties of aluminum by PVD-TiN coating combined with cathodic cage plasma nitriding10.1016/j.surfcoat.2017.08.015 ↗
10. Essential anti-corrosive behavior of anodized Al alloy by applied current density10.1016/j.apsusc.2019.03.155 ↗
11. Changes in the structure and corrosion protection ability of porous anodic oxide films on pure Al and Al alloys by pore sealing treatment10.3390/ma15238544 ↗
12. Corrosion-fatigue property of anodic oxidation coated 6082-T6 aluminium alloy: effect of substrate residual stress and microstructure beneath coating-substrate interface10.1016/j.ijfatigue.2023.107803 ↗
13. The impact of temperature and mechanical load on corrosion resistance of anodized aluminum EN AW-6063 (T6 temper) alloy for potential architectonic application
14. Influence of micro-arc oxidation coatings on stress corrosion of AlMg6 alloy10.3390/ma13020356 ↗
15. Coating residual stress effects on fatigue performance of 7050-T7451 aluminum alloy10.1016/j.surfcoat.2007.03.032 ↗
16. Failure behavior of anodized coating-magnesium alloy substrate structures10.4028/www.scientific.net/KEM.261-263.363 ↗
17. Influence of anodic coatings on stress corrosion behaviour of 7017 aluminium alloy10.1108/ACMM-12-2012-1226 ↗
18. Effects of pore parameters on performance of anodic film on 2024 aluminum alloy10.1016/j.matchemphys.2019.04.008 ↗
19. The effect of exposure conditions on performance evaluation of post-treated anodic oxides on an aerospace aluminium alloy: Comparison between salt spray and immersion testing10.1016/j.surfcoat.2020.126157 ↗
20. The electrochemical corrosion behavior of plasma electrolytic oxidation coatings fabricated on aluminum in silicate electrolyte10.1007/s11665-019-04099-8 ↗
21. Research on corrosion resistance of anodized and sealed 6061 aluminum alloy in 3.5% sodium chloride solution10.1016/j.ijoes.2023.100092 ↗
22. Anodizing of 2024-T3 aluminum alloy in sulfuric-boric-phosphoric acids and its corrosion behavior10.1016/S1003-6326(13)62767-3 ↗
23. Wear and corrosion of Co-Cr coatings electrodeposited from a trivalent chromium solution: Effect of heat treatment temperature10.1016/j.surfcoat.2021.127535 ↗
24. Structures and characteristics of Cr(III)-based conversion coatings on electrogalvanized steels10.1016/j.surfcoat.2008.09.006 ↗
25. SECM in situ investigation of corrosion and self-healing behavior of trivalent chromium conversion coating on the zinc10.1016/j.surfcoat.2023.129411 ↗
26. Microstructure evolution and fracture mechanism of the interfacial region between MAO ceramic film and Al-Mg-Sc alloy substrate
27. Construction of anodizing/ silane / graphene oxide composite film and its corrosion resistance mechanism on aluminum alloy surface
28. Corrosion resistance of Cr(III) conversion treatments applied on electrogalvanised steel and subjected to chloride containing media10.1016/j.matchemphys.2009.07.041 ↗
29. EIS characterisation of anodic films formed on 2024 aluminium alloy, in sulphuric acid containing molybdate or permanganate species10.1016/j.corsci.2004.06.019 ↗
30. Study on the effect of acetate ions on the sealing treatment for anodic oxide film of 6063 aluminum alloy10.1016/j.surfcoat.2023.129961 ↗
31. The correlation between the coating structure and the corrosion behavior of the plasma electrolytic oxidation coating on aluminum10.1016/j.surfcoat.2015.12.040 ↗
32. Characterization of anodized and sealed aluminium by EIS10.1016/S0010-938X(02)00137-3 ↗
33. Sealing of tartaric sulfuric (TSA) anodized AA2024 with nanostructured LDH layers10.1039/C5RA27286F ↗
34. FESEM and EIS Study of Sealed AA2024 T3 Anodized in Sulfuric Acid Electrolytes: Influence of Tartaric Acid10.1149/1.2969277 ↗
35. Investigating local corrosion behavior and mechanism of MAO coated 7075 aluminum alloy10.1016/j.jallcom.2020.153976 ↗
36. Effect of different sealing treatments of oxide films on corrosion resistance of anodized ZL101A aluminum alloy in aimulated marine atmospheric environment10.20964/2022.08.51 ↗
37. Effect of voltage on structure and properties of 2024 aluminum alloy surface anodized aluminum oxide films10.1016/j.surfcoat.2024.130508 ↗
38. Effect of anodizing temperature and organic acid addition on the structure and corrosion resistance of anodic aluminum oxide films10.1016/j.tsf.2020.138359 ↗
39. Corrosion and pitting behavior of pure aluminum 1060 exposed to Nansha Islands tropical marine atmosphere10.1016/S1003-6326(22)65806-0 ↗
40. Microstructure and high-temperature oxidation resistance of in-situ Al2O3 reinforced AlCrFeTiV high-entropy alloy with boron microalloying
41. Galvanic corrosion of the anodized 7050 aluminum alloy coupled with the low hydrogen embrittlement Cd Ti plated 300M steel in an industrial-marine atmospheric environment10.1016/j.surfcoat.2019.125171 ↗
42. Effect of thermo-mechanical treatments on corrosion behavior of Cu-15Ni-8Sn alloy in 3.5 wt% NaCl solution10.1016/j.matchemphys.2017.06.041 ↗
43. Characterization and corrosion behavior of anodized Aluminum alloys for military industries applications in artificial seawater10.1016/j.surfin.2018.08.001 ↗