Effect of pretreated Al-Si alloy powder on the microstructure and properties of Al2O3-SiC-C castables for iron runner
Source abstract
Abstract
In ferrotitanium slag-based Al 2O 3-SiC-C castables, owing to the presence of more impurities in the ferrotitanium slag, the liquid content at high temperatures is extremely high, which reduces the performance of the material. In this study, the Al-Si alloy powder was hydrated, and then pretreated Al-Si alloy powder (PASAP) was used to replace Si powder and micro-silica to reduce the content of liquid in the ferrotitanium slag-based Al 2O 3-SiC-C castables. Compared with the sample without PASAP, the sample with 5 wt% PASAP formed numerous whiskers in situ, and the hot modulus of rupture increased by 167%. Moreover, the decrease in the liquid content of the material and the dissolution of the molten slag by Al 2O 3 led to an increase in the slag viscosity. The slag corrosion index of the sample with 5 wt% PASAP is decreased by 67%.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Advanced ceramic materials synthesis · Advanced materials and composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (32)
Show source-provided references
1. Microstructure and enhanced slag resistance of Al2O3-SiC-C refractory castables with addition of ammonium metatungstate10.1016/j.ceramint.2023.04.190 ↗
2. Advanced Al2O3-SiC-SiO2-C refractories with B2O3 addition10.1016/j.ceramint.2021.06.243 ↗
3. Synthesis of CA6/AlON composite with enhanced slag resistance10.1007/s12613-022-2435-2 ↗
4. Effect of modified coal tar pitch addition on the microstructure and properties of Al2O3-SiC-C castables for solid waste incinerators10.1016/j.ceramint.2022.04.060 ↗
5. Effect of firing atmosphere on the microstructure and properties of Al2O3-SiC-C castables10.1016/j.ceramint.2021.01.290 ↗
6. Corrosion resistance and anti-reaction mechanism of Al2O3-based refractory ceramic under weak static magnetic field10.1111/jace.18259 ↗
7. Characterization and mechanism of dissolution behavior of Al2O3/MgO oxides in molten slags10.1007/s42243-022-00847-8 ↗
8. Radical reaction-induced Turing pattern corrosion of alumina refractory ceramics with CaO-Al2O3-SiO2-MgO slags10.1016/j.jeurceramsoc.2022.09.044 ↗
9. Slag corrosion characteristics of MgO-based refractories under vacuum electromagnetic field10.1007/s41779-019-00323-9 ↗
10. Revealing of rich living radicals in oxide melts via weak magnetic effect on alumina dissolution reaction10.1016/j.molliq.2023.121391 ↗
11. Application of calcium alumino-titanate to taphole clay10.1007/s42243-021-00664-5 ↗
12. Preparation and characterization of low-cost refractories for aluminum-melting-furnace linings from ferrotitanium slag10.1016/j.ceramint.2022.06.035 ↗
13. The restructuring-sintering mechanism of calcium alumino-titanate in tundish permanent lining castables10.1016/j.ceramint.2020.08.102 ↗
14. Microstructure and properties of high alumina castables containing calcium alumino-titanate10.1111/ijac.13016 ↗
15. Sintering and microstructural characterization of calcium alumino-titanate-bauxite-SiC composite refractories10.1016/j.ceramint.2018.03.157 ↗
16. Sintering and characterization of calcium alumino-titanate-SiC composite refractory fired in reducing and oxidizing atmospheres10.1016/j.ceramint.2019.06.053 ↗
17. Mechanism and kinetic analysis of vacuum aluminothermic reduction for preparing TiAl intermetallics powder10.1016/j.jallcom.2020.157546 ↗
18. Effect of the calcium alumino-titanate particle size on the microstructure and properties of bauxite-SiC composite refractories10.1016/j.ceramint.2018.01.059 ↗
19. Improved slag resistance of taphole clay due to in situ formation of TiCN from ferrotitanium slag10.1016/j.ceramint.2021.05.082 ↗
20. Effect of partial substitution of calcium alumino-titanate for bauxite on the microstructure and properties of bauxite-SiC composite refractories10.1016/j.ceramint.2017.11.045 ↗
21. Effect of different metal powder anti-oxidants on N220 nano carbon containing low carbon MgO-C refractory: An in-depth investigation10.1016/j.ceramint.2016.08.185 ↗
22. The effect of antioxidants on the oxidation behaviour of magnesia-carbon refractory bricks10.1016/j.ceramint.2006.10.004 ↗
23. Reaction of aluminum powder with water in cement-containing refractory castables10.1016/j.jeurceramsoc.2004.07.004 ↗
24. Characterization of alumina-magnesia-carbon refractory bricks containing aluminium and silicon10.1016/j.ceramint.2018.02.069 ↗
25. Applications and research progress of metals in refractories
26. Aluminum-containing refractory castables
27. Effect of dispersants, fine powders on aluminum-containing refractory castables
28. Enhancement and explosion-proof mechanism of aluminum fiber addition in Al2O3-SiC-C castables for iron runner10.1016/j.ceramint.2019.07.310 ↗
29. Analysis on mechanism of explosive spalling resistance of aluminum powder on ladle corundum-based refractory castable10.1016/j.ceramint.2020.04.220 ↗
30. Effect of Composite antioxidant on properties of Al2O3-SiC-C brick
31. Insight into the corrosion failure of mullite thermal insulation materials in carbon monoxide10.1111/ijac.13795 ↗
32. Effect of firing on physical properties and microstructure of Al2O3-C refractory