Effect of Ni-alloys on thermal decomposition of ammonia borane
Source abstract
Abstract
Abstract The principal disadvantage of thermal decomposition of ammonia borane is release of borazine during generation of hydrogen gas. In the current work, ZrNi, FeNi and CuNi alloys have been synthesized and used as additives to decrease the amount of borazine release. It was observed that ZrNi was most efficient resulting in ∼22% decrease in the borazine release. The effect of the additives in decreasing the borazine release was observed to be in the order of ZrNi > FeNi > CuNi.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Hydrogen Storage and Materials · Ammonia Synthesis and Nitrogen Reduction · Catalytic Processes in Materials Science
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (18)
Show source-provided references
1. Hydrogen storage materials: present scenarios and future directions
2. Hydrogen storage materials for mobile applications10.1038/35104634 ↗
3. Nanoscaffold mediates hydrogen release and the reactivity of ammonia borane10.1002/anie.200462602 ↗
4. An experimental study of neat and ionic liquid-aided ammonia borane thermolysis10.1016/j.jpowsour.2010.07.085 ↗
5. Effect of zeolites on thermal decomposition of ammonia borane10.1016/j.ijhydene.2011.04.011 ↗
6. Metal chloride-doped ammonia borane thermolysis: positive effect on induction period as well as hydrogen and borazine release10.1016/j.tca.2010.06.007 ↗
7. Base-promoted ammonia borane hydrogen-release10.1021/ja905015x ↗
8. Coherent carbon cryogel-ammonia borane nanocomposites for H2 storage10.1021/jp072448t ↗
9. Improved dehydrogenation of ammonia borane over Co–P–B coating on Ni: a single catalyst for both hydrolysis and thermolysis10.1016/j.apcatb.2011.09.032 ↗
10. The effects of chemical additives on the induction phase in solid-state thermal decomposition of ammonia borane10.1021/cm801253u ↗
11. Cu2+-induced room temperature hydrogen release from ammonia borane10.1039/b909448m ↗
12. Hydrogen storage behavior of ZrNi70/30 and ZrNi 30/70 composites10.1016/j.jallcom.2007.04.012 ↗
13. Synthesis of FeNi3 alloyed nanoparticles by hydrothermal reduction10.1021/jp0625154 ↗
14. Synthesis and characterization of magnetic FeNi3 particles obtained by hydrazine reduction in aqueous solution10.1016/j.mseb.2007.01.055 ↗
15. Hydrothermal formation of magnetic Ni–Cu alloy nanocrystallites at low temperatures10.1088/0957-4484/15/8/034 ↗
16. One-step, solid-state reaction to the synthesis of copper oxide nanorods in the presence of a suitable surfactant10.1039/b008215p ↗
17. Synthesis and electrochemical properties of mesoporous nickel oxide10.1016/j.jpowsour.2004.03.038 ↗
18. Transmission infrared spectroscopy of ammonia borane