Improved dehydrogenation properties of lithium alanate (LiAlH4) doped by low energy grinding

Abstract LiAlH4 is an attractive hydrogen storage material because of its high gravimetric hydrogen storage capacity of 10.5 wt.%. There are various reports in the literature on doping LiAlH4 with transition metals in order to improve its dehydrogenation kinetics. However, very often it was found that LiAlH4 starts dehydrogenating already during doping, thereby, reducing the usable hydrogen storage capacity considerably. In this study, LiAlH4 was doped by low-energy grinding with different transition metal chlorides (ZrCl4, TiCl3 and NiCl2). Thus, unwanted dehydrogenation during doping could be prevented. The positive effect of the dopants on promoting the dehydrogenation of LiAlH4 was systematically studied by thermal analysis. In addition, the crystal phases were characterized by X-ray diffraction. In view of long-term storability of suchlike doped LiAlH4, the weight change was monitored at room temperature up to seven months.