Magnetic characterization of Bi₂FeMnO₆ film grown on (100) SrTiO₃ substrate

Abstract Single phase Bi₂FeMnO₆ films on (100) SrTiO₃ substrate were fabricated using a pulsed laser deposition method through optimization of the preparation conditions. The magnetic moment is 0.30μ_B at 5 K in the magnetic field of 1 T, indicating that B site cations of Fe and Mn are disordered in the sample. The zero‐field‐cooling (ZFC) and field‐cooling (FC) magnetization curves measured from 2 K to 400 K coincide at 360 K. This is consistent with the observation that hysteresis disappears at 360 K, revealing the antiferromagnetic transition at this temperature. A spin‐glass‐like behaviour was observed at low temperature (∼100 K) with a cusp of 25 K. Mn shows multiple valence states in the film. It is possibly because Mn²⁺ and Mn⁴⁺ could decrease the Jahn–Teller effect from Mn³⁺ in the film which results in less lattice distortion. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)