Abnormal thermal conductivity of [720]‐oriented BaTiO₃ single crystal

Abstract The 3ω ‐scanning thermal microscopy and piezoresponse force microscopy techniques were combined to characterize the local thermal conductivity (λ) of ferroelastic domains in [720]‐oriented and [001]‐oriented BaTiO₃ single crystal. The [720]‐oriented BaTiO₃ showed a local λ value of 3.39 W/m·K, while it was 5.95 W/m·K for [001]‐oriented BaTiO₃. The underlying mechanism for such drastic thermal conductivity reduction in [720]‐oriented BaTiO₃ is ascribed to a stronger phonon‐scattering effect due to the high strains appearing in [720]‐oriented BaTiO₃ single crystals. (© 2014 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)