Electrospinning fabrication and luminescent properties of SrMoO4:Sm3+ nanofibers

Abstract Samarium ions doped strontium molybdate (SrMoO 4 :Sm 3+ ) nanofibers (NFs) were fabricated by a simple electrospinning process. The obtained SrMoO 4 :Sm 3+ NFs are composed of scheelite-type tetragonal SrMoO 4 phase, and the NFs have an average diameter of ca. 90 nm. Under 275 nm ultraviolet (UV) excitation, the NFs show an orange-red fluorescent property symbolized by a characteristic emission (606 nm) resulting from the 4 G 5/2 → 6 H 7/2 energy level transition of Sm 3+ . And the photoluminescence (PL) emissi on intensity of the SrMoO 4 :Sm 3+ NFs is superior to that of the nanoparticles (NPs) counterpart under the same doping concentrations. The effect of Sm 3+ concentrations on the 4 G 5/2 → 6 H 7/2 emission intensity was also investigated. The result reveals that the concentration quenching will occur when the Sm 3+ content exceeds 2 at.%. In other words, the SrMoO 4 :Sm 3+ NFs have an optimal luminescent performance under such a doping concentration.