Criteria for laves-phase formation in refractory high-entropy alloys
Source abstract
Abstract
The refractory high-entropy alloys (RHEAs) have been the subject of considerable research in recent years. Since the Laves phase usually leads to a dramatic decrease in the malleability of RHEAs at ambient temperatures, it is critical to identifying the Laves-phase formation. Here, a facile and effective criterion is proposed to predict the phase stability based on the empirical parameters of reported RHEAs. The results indicate that the small atomic size difference is a sufficient condition for determining the stability of solid solution but not a necessary one. In general, the Laves-phase precipitates can be inhibited by decreasing the atomic-size difference, the enthalpy of mixing, and the valence electron concentration. These criteria can be easily adapted to design new RHEAs with the desired phase structure.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian, China
State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi’an, People’s Republic of China
Ningbo Institute of Dalian University of Technology, Ningbo, People’s Republic of China
Funding
National Magnetic Confinement Fusion Energy Research · National Key Research and Development Program of China · Liao Ning Revitalization Talents Program · State Key Laboratory of Solidification Processing · program of China Scholarships Council
References (81)
Show source-provided references
1. 10.1016/j.msea.2003.10.25710.1016/j.msea.2003.10.257 ↗
2. 10.1002/adem.20030056710.1002/adem.200300567 ↗
3. 10.1002/adem.20070024010.1002/adem.200700240 ↗
4. 10.1016/j.matchemphys.2011.11.02110.1016/j.matchemphys.2011.11.021 ↗
5. 10.1016/j.intermet.2013.05.00210.1016/j.intermet.2013.05.002 ↗
6. 10.1016/j.scriptamat.2014.09.01010.1016/j.scriptamat.2014.09.010 ↗
7. 10.1016/j.scriptamat.2015.03.02310.1016/j.scriptamat.2015.03.023 ↗
8. 10.1080/02670836.2016.115327710.1080/02670836.2016.1153277 ↗
9. 10.1557/jmr.2018.15310.1557/jmr.2018.153 ↗
10. 10.1016/j.scriptamat.2020.06.04810.1016/j.scriptamat.2020.06.048 ↗
11. 10.1016/j.intermet.2004.02.01010.1016/j.intermet.2004.02.010 ↗
12. 10.1002/crat.1971006040210.1002/crat.19710060402 ↗
13. 10.1016/S0966-9795(00)00109-610.1016/S0966-9795(00)00109-6 ↗
14. 10.1063/1.358722810.1063/1.3587228 ↗
15. Okamoto H. · 2000 · 44
16. 10.1016/j.jmrt.2020.05.07110.1016/j.jmrt.2020.05.071 ↗
17. Wu S.Y. · J. Mater. Res. Technol · 2022 · 97 · 229
18. 10.1007/s12540-016-6034-510.1007/s12540-016-6034-5 ↗
19. 10.1016/j.jallcom.2019.05.04310.1016/j.jallcom.2019.05.043 ↗
20. 10.1007/s11837-015-1617-z10.1007/s11837-015-1617-z ↗
21. 10.1016/j.msea.2012.12.01810.1016/j.msea.2012.12.018 ↗
22. 10.1016/j.msea.2011.09.03310.1016/j.msea.2011.09.033 ↗
23. 10.1016/j.ijrmhm.2014.07.00910.1016/j.ijrmhm.2014.07.009 ↗
24. 10.1016/j.matdes.2015.06.07210.1016/j.matdes.2015.06.072 ↗
25. 10.1557/jmr.2018.24110.1557/jmr.2018.241 ↗
26. 10.1016/j.intermet.2018.11.00110.1016/j.intermet.2018.11.001 ↗
27. 10.1016/j.jallcom.2019.15335210.1016/j.jallcom.2019.153352 ↗
28. 10.1016/j.ijrmhm.2018.05.01410.1016/j.ijrmhm.2018.05.014 ↗
29. 10.1016/j.matlet.2016.11.03010.1016/j.matlet.2016.11.030 ↗
30. 10.1016/j.jallcom.2015.08.22410.1016/j.jallcom.2015.08.224 ↗
31. 10.1016/j.intermet.2011.01.00410.1016/j.intermet.2011.01.004 ↗
32. 10.1016/j.intermet.2017.01.00710.1016/j.intermet.2017.01.007 ↗
33. 10.1007/s11661-017-4386-110.1007/s11661-017-4386-1 ↗
34. 10.1007/s11837-014-1066-010.1007/s11837-014-1066-0 ↗
35. 10.1016/j.matdes.2015.05.01910.1016/j.matdes.2015.05.019 ↗
36. 10.1007/s10853-012-6260-210.1007/s10853-012-6260-2 ↗
37. 10.1016/j.intermet.2015.03.01310.1016/j.intermet.2015.03.013 ↗
38. 10.1016/j.proeng.2012.03.04310.1016/j.proeng.2012.03.043 ↗
39. 10.3390/e1602087010.3390/e16020870 ↗
40. 10.1016/j.actamat.2014.01.02910.1016/j.actamat.2014.01.029 ↗
41. 10.1016/j.jallcom.2013.08.10210.1016/j.jallcom.2013.08.102 ↗
42. 10.1016/j.jallcom.2014.11.01210.1016/j.jallcom.2014.11.012 ↗
43. 10.1016/j.jallcom.2014.11.06410.1016/j.jallcom.2014.11.064 ↗
44. 10.1016/j.calphad.2015.09.00710.1016/j.calphad.2015.09.007 ↗
45. 10.1016/j.jallcom.2015.11.09110.1016/j.jallcom.2015.11.091 ↗
46. 10.1016/j.intermet.2015.09.01110.1016/j.intermet.2015.09.011 ↗
47. 10.3390/e1805018910.3390/e18050189 ↗
48. 10.1063/1.496665910.1063/1.4966659 ↗
49. 10.1016/j.matlet.2016.03.13310.1016/j.matlet.2016.03.133 ↗
50. 10.1016/j.actamat.2016.01.01810.1016/j.actamat.2016.01.018 ↗
51. 10.1016/j.msea.2016.07.10210.1016/j.msea.2016.07.102 ↗
52. 10.1016/j.scriptamat.2016.10.02810.1016/j.scriptamat.2016.10.028 ↗
53. Qiao D.X. · Trans Tech Publ · 2017 · 898 · 638
54. 10.1002/adma.20170167810.1002/adma.201701678 ↗
55. 10.1016/j.jallcom.2016.11.18810.1016/j.jallcom.2016.11.188 ↗
56. 10.1016/j.jallcom.2016.09.18910.1016/j.jallcom.2016.09.189 ↗
57. 10.1007/s11669-017-0565-410.1007/s11669-017-0565-4 ↗
58. 10.1016/j.msea.2017.12.00410.1016/j.msea.2017.12.004 ↗
59. 10.1016/j.jmrt.2020.06.03610.1016/j.jmrt.2020.06.036 ↗
60. 10.1016/j.ijrmhm.2018.05.00610.1016/j.ijrmhm.2018.05.006 ↗
61. 10.1016/j.msea.2018.03.07110.1016/j.msea.2018.03.071 ↗
62. 10.1016/j.msea.2020.13940910.1016/j.msea.2020.139409 ↗
63. 10.1016/j.jallcom.2019.06.13810.1016/j.jallcom.2019.06.138 ↗
64. 10.1016/j.intermet.2018.01.01710.1016/j.intermet.2018.01.017 ↗
65. 10.3390/e2203028210.3390/e22030282 ↗
66. 10.1016/j.msea.2019.03.05410.1016/j.msea.2019.03.054 ↗
67. 10.3390/e2105048310.3390/e21050483 ↗
68. 10.1007/s11665-019-04540-y10.1007/s11665-019-04540-y ↗
69. 10.1016/j.actamat.2019.11.02610.1016/j.actamat.2019.11.026 ↗
70. 10.1016/j.scriptamat.2020.01.02810.1016/j.scriptamat.2020.01.028 ↗
71. 10.1016/j.jallcom.2020.15430110.1016/j.jallcom.2020.154301 ↗
72. 10.1016/j.msea.2018.11.05410.1016/j.msea.2018.11.054 ↗
73. 10.1016/j.mtcomm.2018.06.00410.1016/j.mtcomm.2018.06.004 ↗
74. 10.1016/j.jallcom.2016.10.01410.1016/j.jallcom.2016.10.014 ↗
75. 10.3390/ma1102020810.3390/ma11020208 ↗
76. 10.3103/S106836661405006710.3103/S1068366614050067 ↗
77. 10.1016/j.matchemphys.2017.09.05910.1016/j.matchemphys.2017.09.059 ↗
78. 10.1016/j.msea.2020.13977410.1016/j.msea.2020.139774 ↗
79. 10.1016/j.jallcom.2020.15600410.1016/j.jallcom.2020.156004 ↗
80. 10.1007/s40195-019-00921-310.1007/s40195-019-00921-3 ↗
81. 10.1016/j.jnucmat.2019.15195510.1016/j.jnucmat.2019.151955 ↗