Deformation and failure of a heterogeneous high explosive

The deformation and failure of the pristine PBX 9501 high explosive are studied experimentally by combining Brazilian disk compression with the digital image correlation (DIC) technique. The Brazilian disk specimen was loaded by a pair of compressive forces across the diameter. The full-field deformation on the surface of the disk, during the loading process, was obtained using DIC on a series of random speckle images acquired during the test. In this series of experiments, we focused on the effect of temperature while keeping the loading speed quasi-static. Tests were conducted under three different temperatures, −15°C, 23°C, and 50°C. For all testing conditions, it was observed that as the applied load reaches maximum, localized deformation starts at the two regions near the loading points. The localized deformation then proceeds along an irregular path toward the center of the specimen and coalesces. Finally, deformation of the Brazilian disk subjected to cyclic compressive load at ambient temperature was also measured and studied.