3D processing map and hot deformation behaviour of a new type Al–Zn–Mg alloy

Ke Deng, Daxiang Sun, Weixue Tang, Zhizhi Cai, Ruoju Zheng, Jinghui Zhou

Philosophical Magazine· Volume 100· Issue 13
Publisher page

Abstract

The thermal compression behaviour of Al–Zn–Mg alloy was studied on a thermal simulator machine at the temperature range of 380–540°C and strain rate range of 0.01–10 s−1. The constitutive equation and 3D processing map of the alloys were established. The microstructure characteristics of the alloy were studied by metallographic observation, electron back-scatter diffraction (EBSD) analysis and transmission electron microscopy (TEM) microstructure analysis. The results show that the peak stress of high-temperature deformation of alloy decreases with the increase of deformation temperature and increases with the increase of strain rate. The dynamic recovery of the alloy occurs at the temperature range of 380–460°C and the strain rate range of 0.01–0.1 s−1. The dynamic recrystallization of the alloy occurs at the temperature range of 460–500°C and the strain rate range of 0.01–0.1 s−1. The alloy maintains fine and uniform recrystallized grains at a temperature range of 460–480°C and a strain rate range of 0.01–0.1 s−1, which is suitable for hot working.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Metallurgy and Material Forming · Microstructure and mechanical properties · Aluminum Alloy Microstructure Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Guangdong Industry Analysis and Testing Center

School of Materials Science and Engineering, Central South University

Guangdong Fenglv Alumina Company Ltd.

References (21)

Show source-provided references
1. 10.1016/j.actamat.2012.01.00210.1016/j.actamat.2012.01.002 ↗
2. 10.1016/j.jallcom.2018.03.18810.1016/j.jallcom.2018.03.188 ↗
3. 10.1016/j.jallcom.2003.11.17510.1016/j.jallcom.2003.11.175 ↗
4. 10.1557/jmr.2019.26810.1557/jmr.2019.268 ↗
5. 10.4028/www.scientific.net/MSF.519-521.127110.4028/www.scientific.net/MSF.519-521.1271 ↗
6. B. Liu, C.Q. Peng and R.C. Wang, Recent development and prospects for giant plane aluminum alloys Chin. J. Nonferrous Met. 20 (2010), pp. 1705–1715.
7. 10.1016/j.actamat.2010.05.01710.1016/j.actamat.2010.05.017 ↗
8. 10.1016/j.jallcom.2017.03.24010.1016/j.jallcom.2017.03.240 ↗
9. 10.1016/j.actamat.2004.06.02310.1016/j.actamat.2004.06.023 ↗
10. 10.1016/j.matchar.2019.10995310.1016/j.matchar.2019.109953 ↗
11. Z. Zhang, K.H. Chen and H.C. Fang, Effects of trace Cr and Nb additions on mechanical properties and stress corroded cracking of Al-Zn-Mg-Cu-Zr aluminum alloy. Chin. J. Nonferrous Met. 18 (2008), pp. 985–989.
12. 10.1016/j.msea.2019.04.00910.1016/j.msea.2019.04.009 ↗
13. 10.1016/j.jallcom.2012.10.11410.1016/j.jallcom.2012.10.114 ↗
14. 10.1016/j.jallcom.2016.06.25410.1016/j.jallcom.2016.06.254 ↗
15. 10.1016/j.msea.2009.03.06810.1016/j.msea.2009.03.068 ↗
16. 10.1007/s10853-018-2388-z10.1007/s10853-018-2388-z ↗
17. 10.1016/j.jmatprotec.2004.03.02910.1016/j.jmatprotec.2004.03.029 ↗
18. 10.1007/s10853-010-5203-z10.1007/s10853-010-5203-z ↗
19. 10.1016/j.jallcom.2017.11.07010.1016/j.jallcom.2017.11.070 ↗
20. 10.1016/j.actamat.2015.03.05710.1016/j.actamat.2015.03.057 ↗
21. 10.1016/j.actamat.2007.09.00410.1016/j.actamat.2007.09.004 ↗