Evaluation Method for Bond-Splitting Behavior of Reinforced Concrete with Corrosion Based on Confinement Stress of Concrete against Corrosion Expansion
Source abstract
Abstract
In this study, the bond behavior of corroded reinforced concrete (RC) was investigated by conducting pull-out tests on RC specimens with different corrosion crack widths. The confinement stress of concrete was evaluated by an expansion simulation using a non-explosive demolition agent, from which a confinement stress equation for RC with corrosion cracking was proposed. Bond strength linearly decreased with decreasing confinement stress in the concrete. The rate of decrease was independent of longitudinal corrosion crack width at the concrete surface, cover thickness, and reinforcement diameter. Furthermore, from the relationship between bond strength and confinement stress in concrete, equations for predicting bond stress and slip curve were proposed. Overall, the predicted values agreed well with the experimental results of other studies.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete Corrosion and Durability · Corrosion Behavior and Inhibition · Structural Behavior of Reinforced Concrete
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Nagaoka National College of Technology, Nagaoka, Japan.
References (19)
Show source-provided references
1. Cairns, J., Du, Y. and Law, D., (2006). “Residual bond strength of corroded plain round bars.” Magazine of Concrete Research, 58(4), 221-231.10.1680/macr.2006.58.4.221 ↗
2. Comité Euro-International du Béton, (1990). “CEB-FIP model code 1990 first draft” CEB.
3. Fédération Internationale du Béton, (2000). “State-of-art Report.” Bulletin 10. Bond of Reinforcement in Concrete, FIB.
4. Harada, T., Idemitsu, T. and Watanabe, A., (1985). “Demolition of concrete with expansive demolition agent.” Journal of Japan Society of Civil Engineers, 360, 61-70. (in Japanese)
5. Ikarimoto, D., Araki, K., Hattori, A. and Miyagawa, T., (2006). “Research for the relation about corroded reinforcement and bond strength with double-pulling test.” Proceedings of the Japan Concrete Institute, 28(2), 661-666. (in Japanese)
6. JCI, (1998.10). “Rehabilitation research council report of concrete structure.” (in Japanese)
7. JSCE., (2007). “JSCE guidelines for concrete No.15.” Japan Society of Civil Engineers. (in Japanese)
8. Kawamura, R., Nakamura, H., Kunieda, M. and Ueda, N., (2009). “Evaluation for behavior of propagating cracks due to corrosion of reinforcement.” Proceedings of the Japan Concrete Institute, 31(1), 1075-1080. (in Japanese)
9. Makino, S., Matsushima, M. and Yokota, Y., (2002). “Bond capacity of specimens with cracks occurred accelerated tests by electrolytic corrosion.” 57th Proceedings of Annual Conference of the Japan Society of Civil Engineers, 1119-1120. (in Japanese)
10. Morinaga, S., (1988). “Prediction of service lives of reinforced concrete buildings based on the rate of corrosion.” Institute of Technology, Shimizu Corporation, Special Report No. 23. (in Japanese)
11. Nagaoka, K., Sato, A. and Murakami, Y., (2011). “Influence of confinement of concrete on bond behavior of RC member with corrosion.” Proceedings of the Japan Concrete Institute, 33(1), 827-832. (in Japanese)
12. Nagaoka, K., Furukawa, Y. and Murakami, Y., (2012). “Influence of corrosion expansion of re-bars on confinement concrete.” Proceedings of the Japan Concrete Institute, 34(1), 1048-1053. (in Japanese)
13. Sasaki, A., Maruyama, K., Shimizu, K. and Yoneda, N., (1991). “Influence of corrosion of reinforcing bars on bond characteristics.” Proceedings of the Japan Concrete Institute, 13(2), 139-144. (in Japanese)
14. Tang, D. Molyneaux, T. K. C., Law, D. W. and Gravina, R., (2011). “Influence of surface crack width on bond strength of reinforced concrete” ACI Materials Journal, 108(1), 29-37.
15. Uda, K., Hussein, N. A., Louis, A., Darmawan. and Sato, R., (2004). “Bond characteristics of reinforced concrete prism with corrosion cracks.” Proceedings of the Japan Concrete Institute, 26(2), 841-846. (in Japanese)
16. Vos, E., (1983). “Influence of loading rate and radial pressure on bond in reinforced concrete.” Thesis (PhD). Delft University.
17. Williamson, S. J. and Clark, L. A., (2000). “Pressure required to cause cover cracking of concrete due to reinforcement corrosion.” Magazine of Concrete Research, 52(6), 455-467.10.1680/macr.2000.52.6.455 ↗
18. Yasojima, A. and Kanakubo, T., (2004). “Effect of lateral confinement in bond splitting behavior of RC members.” Proceedings of the Japan Concrete Institute, 26, (2), 853-858. (in Japanese)
19. Yoneda, N., Maruyama, K., Shimizu, K. and Yanagi, M., (1992). “Deterioration of bond characteristics due to corrosion of reinforcing bars.” Proceedings of the Japan Concrete Institute, 14, (2), 81-86. (in Japanese)