Quantitative Analysis of Phase Assemblage and Chemical Shrinkage of Alkali-Activated Slag
Source abstract
Abstract
This paper presents a quantitative analysis of hydrated phase assemblage and chemical shrinkage of alkali-activated slag (AAS) as a function of pH and modulus (n= SiO2/Na2O molar ratio) of activator. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and thermodynamic modeling, provide a com-prehensive characterization of the phase assemblages and distribution in AAS microstructure. The main hydration products in AAS are calcium-alumina-silicate-hydrate (C-A-S-H) and hydrotalcite-type phases, while the formation of other hydrates is activator-dependent. For NaOH-activated slag, hydration products are preferentially formed around slag particles showing a hydrated rim, while for sodium silicate-activated slag, hydration products are initialized at both slag surface and inter-particle spaces simultaneously. However, a dark hydrated rim whose composition is similar to that of alkali-aluminosilicate-hydrate was observed around unhydrated slag in aged AAS. It indicates that the composition and spatial distribution of hydrates in AAS microstructure is heterogeneous, which cannot be predicted by thermodynamic modeling. The chemical shrinkage of AAS was quantified using buoyancy method and backscattered image analysis. The average chemical shrinkage of AAS is about 0.1211 ml/gslag and increases with the increasing modulus and pH of activator. The chemical shrinkage of AAS is about twice larger than that of portland cement, which may be attributed to the limited formation of expansive crystalline phases, such as ettringite and portlandite.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Concrete Properties and Behavior · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Civil and Environmental Engineering, The Pennsylvania State University, PA, 16801, USA.
References (40)
Show source-provided references
1. 1) Ben, Haha, M., Le, Saout, G., Winnefeld, F. and Lothenbach, B., (2011a). “Influence of activator type on hydration kinetics, hydrate assemblage and microstructural development of alkali activated blast-furnace slags.” Cement and Concrete Research, 41, 301-310.10.1016/j.cemconres.2010.11.016 ↗
2. 2) Ben, Haha, M., Lothenbach, B., Le, Saout, G. and Winnefeld, F., (2011b). “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag—Part I: Effect of MgO.” Cement and Concrete Research, 41, 955-963.10.1016/j.cemconres.2011.05.002 ↗
3. 3) Bernal, S. A., Rose, V. and Provis, J. L., (2014). “The fate of iron in blast furnace slag particles during alkali-activation.” Materials Chemistry and Physics, 146, 1-5.10.1016/j.matchemphys.2014.03.017 ↗
4. 4) Bonk, F., Schneider, J., Cincotto, M. A. and Panepucci, H., (2003). “Characterization by Multinuclear High‐Resolution NMR of Hydration Products in Activated Blast‐Furnace Slag Pastes.” Journal of the American Ceramic Society, 86, 1712-1719.10.1111/j.1151-2916.2003.tb03545.x ↗
5. 5) Brough, A. and Atkinson, A., (2002). “Sodium silicate-based, alkali-activated slag mortars: Part I. Strength, hydration and microstructure.” Cement and Concrete Research, 32, 865-879.10.1016/S0008-8846(02)00717-2 ↗
6. 6) Cartwright, C., Rajabipour, F. and Radlińska, A., (2014). “Shrinkage characteristics of alkali-activated slag cements.” Journal of Materials in Civil Engineering, B4014007.
7. 7) Cartwright, C. P., Rajabipour, F. and Radlińska, A., (2013). “Measuring the chemical shrinkage of alkali-activated sslag cements using the buoyancy method.” In: F. J. Ulm, H. M. Jennings, R. Pellenq Eds., Mechanics and Physics of Creep, Shrinkage, and Durability of Concrete: A Tribute to Zdenek. P. Bazant, Proceedings of the Ninth International Conference on Creep, Shrinkage, and Durability Mechanics (CONCREEP-9), September 22-25, Cambridge, Massachusetts, 2013. ASCE Publications, 308p.
8. 8) Chen, W. and Brouwers, H., (2007). “The hydration of slag, part 1: reaction models for alkali-activated slag.” Journal of Materials Science, 42, 428-443.10.1007/s10853-006-0873-2 ↗
9. 9) Deir, E., Gebregziabiher, B. S. and Peethamparan, S., (2014). “Influence of starting material on the early age hydration kinetics, microstructure and composition of binding gel in alkali activated binder systems.” Cement and Concrete Composites, 48, 108-117.10.1016/j.cemconcomp.2013.11.010 ↗
10. 10) Douglas, E., Bilodeau, A. and Malhotra, V., (1992). “Properties and durability of alkali-activated slag concrete.” ACI Materials Journal, 89(5), 509-516.
11. 11) Duxson, P., Provis, J. L., Lukey, G. C., Mallicoat, S. W., Kriven, W. M. and Van Deventer, J. S., (2005). “Understanding the relationship between geopolymer composition, microstructure and mechanical properties.” Colloids and Surfaces A: Physicochemical and Engineering Aspects, 269, 47-58.10.1016/j.colsurfa.2005.06.060 ↗
12. 12) Gebregziabiher, B. S., Thomas, R. and Peethamparan., S., (2015). “Very early-age reaction kinetics and microstructural development in alkali-activated slag.” Cement and Concrete Composites, 55, 91-102.10.1016/j.cemconcomp.2014.09.001 ↗
13. 13) Jensen, O. M. and Hansen, P. F., (2001). “Water-entrained cement-based materials: I. Principles and theoretical background.” Cement and concrete research, 31, 647-654.10.1016/S0008-8846(01)00463-X ↗
14. 14) Jiang, M., Chen, X., Rajabipour, F. and Hendrickson, C. T., (2014). “Comparative life cycle assessment of conventional, glass powder, and alkali-activated slag concrete and mortar.” Journal of Infrastructure Systems, 20(4), 04014020.10.1061/(ASCE)IS.1943-555X.0000211 ↗
15. 15) Juenger, M., Winnefeld, F., Provis, J. and Ideker, J., (2011). “Advances in alternative cementitious binders.” Cement and Concrete Research, 41, 1232-1243.10.1016/j.cemconres.2010.11.012 ↗
16. 16) Kulik, D., Berner, U. and Curti, E., (2003). “Modelling chemical equilibrium partitioning with the GEMS-PSI code.” PSI Scientific Report, 4, 109-122.
17. 17) Lothenbach, B. and Gruskovnjak, A., (2007). “Hydration of alkali-activated slag: thermodynamic modelling.” Advances in cement research, 19, 81-92.10.1680/adcr.2007.19.2.81 ↗
18. 18) Lura, P., Jensen, O. M. and van Breugel, K., (2003). “Autogenous shrinkage in high-performance cement paste: An evaluation of basic mechanisms.” Cement and Concrete Research, 33, 223-232.10.1016/S0008-8846(02)00890-6 ↗
19. 19) Myers, R. J., Bernal, S. A. and Provis, J. L., (2014). “A thermodynamic model for C-(N-) ASH gel: CNASH_ss. Derivation and validation.” Cement and Concrete Research, 66, 27-47.10.1016/j.cemconres.2014.07.005 ↗
20. 20) Myers, R. J., Lothenbach, B., Bernal, S. A. and Provis, J. L., (2015). “Thermodynamic modelling of alkali-activated slag cements.” Applied Geochemistry, 61, 233-247.10.1016/j.apgeochem.2015.06.006 ↗
21. 21) Neto, A. A. M., Cincotto, M. A. and Repette, W., (2008). “Drying and autogenous shrinkage of pastes and mortars with activated slag cement.” Cement and Concrete Research, 38, 565-574.10.1016/j.cemconres.2007.11.002 ↗
22. 22) Oh, J. E., Monteiro, P. J., Jun, S. S., Choi, S. and Clark, S. M., (2010). “The evolution of strength and crystalline phases for alkali-activated ground blast furnace slag and fly ash-based geopolymers.” Cement and Concrete Research, 40, 189-196.10.1016/j.cemconres.2009.10.010 ↗
23. 23) Powers, T. C. and Brownyard, T. L., (1946). “Studies of the physical properties of hardened Portland cement paste.” ACI Journal Proceedings, 43(9), 249-336.
24. 24) Provis, J. L., Palomo, A. and Shi, C., (2015). “Advances in understanding alkali-activated materials.” Cement and Concrete Research, 78, 110-125.10.1016/j.cemconres.2015.04.013 ↗
25. 25) Regourd, M., (1980). “Structure and behaviour of slag Portland cement hydrates.” In: Proceedings of the 7th ICCC, 1980, 10-26.
26. 26) Richardson, I., (2004). “Tobermorite/jennite-and tobermorite/calcium hydroxide-based models for the structure of CSH: applicability to hardened pastes of tricalcium silicate, β-dicalcium silicate, Portland cement, and blends of Portland cement with blast-furnace slag, metakaolin, or silica fume.” Cement and Concrete Research, 34, 1733-1777.10.1016/j.cemconres.2004.05.034 ↗
27. 27) Roy, A., Schilling, P. J., Eaton, H. C., Malone, P. G., Brabston, W. N. and Wakeley, L. D., (1992). “Activation of ground blast‐furnace slag by alkali‐metal and alkaline‐Earth hydroxides.” Journal of the American Ceramic Society, 75,3 233-3240.10.1111/j.1151-2916.1992.tb04416.x ↗
28. 28) Sant, G., Lura, P. and Weiss, J., (2006). “Measurement of volume change in cementitious materials at early ages: review of testing protocols and interpretation of results.” Transportation Research Record: Journal of the Transportation Research Board, 21-29.10.1177/0361198106197900104 ↗
29. 29) Schilling, P. J., Roy, A., Eaton, H., Malone, P. G. and Brabston, N. W., (1994). “Microstructure, strength, and reaction products of ground granulated blast-furnace slag activated by highly concentrated NaOH solution.” Journal of materials research, 9, 188-197.10.1557/JMR.1994.0188 ↗
30. 30) Scrivener, K. L., (2004). “Backscattered electron imaging of cementitious microstructures: understanding and quantification.” Cement and Concrete Composites, 26, 935-945.10.1016/j.cemconcomp.2004.02.029 ↗
31. 31) Shi, C., Roy, D. and Krivenko, P., (2005). “Alkali-activated cements and concretes.” Taylor & Francis.
32. 32) Snellings, R., (2013). “Solution‐controlled dissolution of supplementary cementitious material glasses at pH 13: The Effect of Solution Composition on Glass Dissolution Rates.” Journal of the American Ceramic Society, 96, 2467-2475.10.1111/jace.12480 ↗
33. 33) Taylor, H. F., (1997). “Cement chemistry.” Thomas Telford.
34. 34) Thomas, J. J., Allen, A. J., Jennings, H. M., (2012). “Density and water content of nanoscale solid C–S–H formed in alkali-activated slag (AAS) paste and implications for chemical shrinkage.” Cement and Concrete Research, 42, 377-383.10.1016/j.cemconres.2011.11.003 ↗
35. 35) Thomas, R. J., Ye, H., Radlińska, A. and Peethamparan, S., (2016). “Alkali-activated slag concrete: A closer look at sustainable alternatives to portland cement.” Concrete International, 38, 33-38
36. 36) Wang, S.-D., Pu, X.-C., Scrivener, K. and Pratt, P., (1995). “Alkali-activated slag cement and concrete: a review of properties and problems.” Advances in cement research, 7, 93-102.10.1680/adcr.1995.7.27.93 ↗
37. 37) Wang, S.-D. and Scrivener, K. L., (1995). “Hydration products of alkali activated slag cement.” Cement and Concrete Research, 25, 561-571.10.1016/0008-8846(95)00045-E ↗
38. 38) Wardhono, A., Law, D. W. and Molyneaux, T. C., (2015). “Long term performance of alkali activated slag concrete.” Journal of Advanced Concrete Technology, 13, 187-192.10.3151/jact.13.187 ↗
39. 39) Ye, H., Cartwright, C., Rajabipour, F., Radlińska, A., (2014). “Effect of drying Rate on shrinkage of alkali-activated slag cements.” In: 4th International Conference on the Durability of Concrete Structure (ICDCS 2014), Purdue University, 2014. pp254-261.
40. 40) Ye, H. and Radlińska, A., (2016). “A review and comparative study of existing shrinkage prediction models for portland and non-portland cementitious materials.” Advances in Materials Science and Engineering, 2016.10.1155/2016/2418219 ↗