Formation of Sn@C Yolk–Shell Nanospheres and Core–Sheath Nanowires for Highly Reversible Lithium Storage

As one promising anode material with high theoretical capacity, metallic tin has attracted much research interest in the field of lithium‐ion batteries. Here, two types of tin/carbon (Sn@C) core–shell nanostructures with inner buffering voids are fabricated from SnO₂ hollow nanospheres via a facile chemical vapor deposition (CVD) method. The crystallinity and surface topography of SnO₂ hollow nanospheres are found to affect the morphology of resultant Sn@C materials. Sn@C yolk–shell nanospheres and core–sheath nanowires are obtained from the as‐prepared SnO₂ and high‐temperature annealed SnO₂ nanospheres, respectively. The unique Sn@C nanostructures can mitigate the agglomeration/pulverization of Sn nanoparticles and electrical disconnection from the current collector caused by the large volume change during the lithium alloying/dealloying process. Both Sn@C yolk–shell and core–sheath nanostructures show stable cycling performance up to 500 cycles with specific capacities of ca. 430 and 520 mA h g⁻¹, respectively.