Bonding ability of self-adhesive resin-cements after dentin biomodification with hyaluronic acid

Purpose: The present study evaluated the influence of the hyaluronic acid (HA) on the bonding ability of self-adhesive resin cements to dentin regarding the bond strength. Eighty bovine incisors were ground flat to obtain a 2-mm thick slices which received conical preparations. The specimens were randomly distributed into 4 groups (n = 15) according to the dentin pretreatment (1 – control: untreated dentin; 2 – application of HA) and the evaluation time (1 – control: immediate evaluation; 2 – hydrolytic degradation: 6 months of storage in water at 37 °C). Preparations received the application of a self-adhesive resin cement (RelyX U200 or MaxCem Elite). Push-out bond strength test was conducted (0.5 mm/min). The bond strength data was submitted to two-way ANOVA/Tukey’s test (α = 0.05). For U200, no significance was observed when comparing the immediate (24 h) and 6 months means for the control groups (unexposed specimens). Previous application of HA to dentin significantly reduced the bond strength of U200 to dentin in both evaluation times (p < 0.05). HA had no significant influence on the push-out bond strength means for the cement MAX in both evaluation times (p > 0.05). The type 1 failure mode (adhesive mode) occurred in 100% of the specimens, irrespective of the dentin treatment or evaluation times. Pretreatment of dentin with HA produces a material-dependent influence on the push-out bond strength. The bonding ability of RelyX U200 is negatively influenced by the pretreatment of dentin with HA, whereas the biomodification of dentin with this bioactive agent causes no impact for the cement MaxCem Elite.