Improved adhesion of EVAs with different vinyl acetate contents treated with sulphuric acid

Abstract Four ethylene vinyl acetate copolymers (EVAs) containing 9, 12, 18 and 20 wt% vinyl acetate (VA) were treated with concentrated sulphuric acid to improve their adhesion to polychloroprene (PCP) adhesive. The tensile strength and Young's modulus of EVAs decreased as the VA content increased, due to the reduction in crystallinity of the polyethylene blocks in the copolymer. The modifications produced in the EVAs by treatment with sulphuric acid were followed using contact angle measurements (water, 25 °C), ATR-IR spectroscopy and scanning electron microscopy (SEM). Adhesive-bond strength was obtained by T-peel tests on treated EVA/polychloroprene adhesive joints. The vinyl acetate content in the EVA affected the extent, but not the nature, of the surface modification produced by treatment with sulphuric acid. The treatment produced both sulfonation and oxidation on the EVA surfaces. The higher the vinyl acetate content in the EVA, the more significant the modifications produced. Increased T-peel strengths of EVA/polychloroprene adhesive + 5 wt% polyisocyanate joints were obtained and a mixed failure (adhesion failure + cohesive failure in the adhesive) was produced. It was found that, to be effective, the treatment of EVAs must be carried out with 96 wt% sulphuric acid. Keywords: EVASURFACE TREATMENTSULPHURIC ACIDPOLYCHLOROPRENE ADHESIVECONTACT ANGLEATR-IR SPECTROSCOPYSEMT-PEEL STRENGTH