Formation of polyimide- Cu complexes: improvement of direct Cu-on-PI and PI-on-Cu adhesion
Source abstract
Abstract
Polyimides containing triazole or imidazole functionalities have been synthesized. Poly(3,3',4,4'-benzophenone tetracarboxylic dianhydride-3,5-diamino-1,2,4-triazole) (BTDA-TADA) contains triazole groups as repeat units and poly(4,4'-oxydiphthalic anhydride-1,3-aminophenoxybenzene-8-azaadenine) (ODPA-APB-8-azaadenine) consists of triazole (8-azaadenine) groups as the end caps. While the BTDA-TADA polyimide starts to decompose at 350°C, the ODPA-APB-8-azaadenine polyimide is thermally stable at 400°C. The peel strength of copper to BTDA-TADA polyimide without surface modification is 200-400 J/m2. For the adhesion of polyimide to copper, ODPA-APB-8-azaadenine polyisoimide (1.0 μm) and poly(pyromellitic dianhydride-oxydianiline) (20 μm) were coated onto the copper substrate and then the two layers were cured together to polyimides at 400°C. Peel strengths of 500-800 J/m2 were obtained. The failure of the copper/polyimide interface by peeling either the copper or the polymer layer occurred in the near-interface region of the polymer. Both PI/Cu and Cu/PI adhesion was enhanced due to the formation of Cu-polyimide complexes. In the case of PI/Cu adhesion, the polymer chain flexibility of ODPA-APB-8-azaadenine polyimide also plays a significant role in improving adhesion.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Synthesis and properties of polymers · Epoxy Resin Curing Processes · Tribology and Wear Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. Feger, C. and Feger, C. 1993.Multichip Module Technologies and Alternatives, Edited by: Doane, D. A. and Franzon, P. D. 311–348. New York: Van Nostrand Reinhold.10.1007/978-1-4615-3100-5_8 ↗
2. Mittal K. L. · 1984 · 110.1007/978-1-4615-7637-2 ↗
3. Wilson D. · 199010.1007/978-94-010-9661-4 ↗
4. Tummala R. R. · 1989
5. 10.1163/156856188X0010110.1163/156856188X00101 ↗
6. Viehbeck A. · 1990
7. Saraf R. F. · Macromolecules · 1993 · 26 · 362310.1021/ma00066a022 ↗
8. Sugama T. · J. Mater. Sci. · 1984 · 19 · 404510.1007/BF00980770 ↗
9. Burrell M. C. · J. Vac. Sci. Technol. A · 1989 · 7 · 5510.1116/1.575731 ↗
10. Kowalczyk S. P. · J. Kim, Appl. Phys. Lett. · 1988 · 52 · 37510.1063/1.99470 ↗
11. Shih D. Y. · J. Vac. Sci. Technol. · 1989 · 7 · 140210.1116/1.576293 ↗
12. Dugdale I. · Corros. Sci. · 1963 · 3 · 6910.1016/S0010-938X(63)80001-3 ↗
13. Ishida H. · Corros. Sci. · 1986 · 26 · 65710.1016/0010-938X(86)90031-4 ↗
14. Xue G. · J. Am. Chem. Soc. · 1988 · 110 · 239310.1021/ja00216a009 ↗
15. Xue G. · Macromolecules · 1991 · 24 · 419510.1021/ma00014a037 ↗
16. Carron K. T. · Langmuir · 1991 · 7 · 210.1021/la00049a001 ↗
17. Carron K. T. · J. Mater. Sci. · 1993 · 28 · 409910.1007/BF00351239 ↗
18. Eng F. P. · J. Mater. Sci. · 1986 · 21 · 156110.1007/BF01114709 ↗
19. Ishida H. · J. Adhesion · 1991 · 36 · 17710.1080/00218469108027071 ↗
20. Jang J. · J. Appl. Polym. Sci. · 1993 · 49 · 195710.1002/app.1993.070491111 ↗
21. Kim K. S. · J. Eng. Mater. Technol. ASME Trans. · 1988 · 110 · 26610.1115/1.3226047 ↗