UV treatment of synthetic styrene-butadiene-styrene rubber

Abstract The effectiveness of the treatment with ultraviolet light (UV) on several polymeric surfaces has previously been established. In this study, a low pressure mercury vapour lamp was used as a source of UV radiation for the surface treatment of a difficult-to-bond block styrenebutadiene-styrene rubber (S6), the treatment time ranging from 10 s to 30 min. The UV-treated S6 rubber surfaces were characterized by contact angle measurements (ethylene glycol, 25°C), ATR-IR spectroscopy, XPS, Scanning Electron Microscopy (SEM), and Atomic Force Microscopy (AFM). T-peel tests on UV-treated S6 rubber/polyurethane (PU) adhesive/ leather joints (before and after ageing) were carried out to quantify adhesion strengths. The UV treatment of S6 rubber produced improved wettability, the formation of C—O, C=O and COO- moieties, and ablation (removal of a thin rubber layer from the surface). The extent of these modifications increased with increasing treatment time. The extended UV treatment produced greater surface modifications, as well as the incorporation of nitrogen moieties at the surface. Furthermore, noticeable ablation of S6 rubber surface occurred. Peel strength values increased with increased treatment time of UV treatment of S6 rubber. Also, with increasing treatment time, the adhesive joints showed different loci of failure: adhesional failure for the as-received and 2 min-UV treated S6 rubber/polyurethane adhesive/leather joints changed to mixed failure (cohesive in the treated S6 rubber + adhesional failure) for the 30 min-UV treated S6 rubber/polyurethane adhesive/leather joint. Keywords: SBS rubberUV treatmentcontact angle measurementsinfrared spectraXPSSEMpeel strength.