XPS/AFM study of the PET surface modified by oxygen and carbon dioxide plasmas: Al/PET adhesion

The formation of the interface between aluminium and O2 or CO2 plasma-modified poly(ethylene terephthalate) (PET) has been investigated by X-ray photoelectron spectroscopy (XPS). As demonstrated by the changes in the C 1s, O 1s, and A1 2p core level spectra upon A1 deposition, the metal was found to react preferentially with the original ester, with the plasma-induced carboxyl and carbonyl groups to form interfacial complexes. The phenyl ring at the modified PET surface was seen to be involved in the formation of the interface, but to a lesser extent. This confirms the high reactivity of the oxygen-containing groups towards the deposited A1 atoms. The adhesion between A1 and the plasma-modified PET films was evaluated by means of a 180° peel test. A considerable (up to ten times) improvement in adhesion was achieved by plasma treatment of the PET substrate, but for either plasma gas the adhesion strength was found to depend strongly on the plasma power and treatment time. The results are discussed in terms of the concentration of oxygen-containing groups at the polymer surface, the surface topography, and the possible presence of low-molecular-weight materials at the metal-polymer interface.