Sub‐10 nm V₂O₅ Crystals on Carbon Nanosheets for Advanced All‐Solid‐State Lithium Metal Batteries

Abstract V₂O₅, as a lithium‐free cathode material, has inherent defects such as sluggish kinetics and volume change and, at the same time, requires a lithium metal anode that tends to form dendrites in liquid electrolytes. Both the lithium dendrite and the flammable electrolyte solvent bring longtime safety issues. This work introduces nonflammable inorganic–organic composite solid electrolyte to inhibit the growth of the lithium dendrite and suppress the instability caused by V₂O₅ nanometerization. However, the long‐term cycling and rate performances are still insufficient even when reducing V₂O₅ size to about 50 nm. As an improvement, sub‐10 nm V₂O₅/C nanosheets are designed and prepared using corn stalks as precursors through simple impregnation and calcination process. The V₂O₅/C offers a much better electrode/electrolyte contact and interface stability than bulk V₂O₅ and commercial V₂O₅ in the inorganic–organic composite solid electrolyte. The discharge capacity is 228 mAh g⁻¹ at 0.1 C after 50 cycles and ≈110 mAh g⁻¹ at 2.0 C.