Enhancing the performance of solvent-borne poly(ethyl methacrylate) coatings for high-power laser applications via low-temperature drying

Organic polymers are a versatile class of materials employed in a broad range of optical coating applications. However, their use as coatings in high-power laser applications, particularly in the UV spectral region, has been limited in scope due to their relatively low laser-induced damage thresholds (LIDTs), which decrease further with exposure to multiple pulses. This study explores the effect of post-deposition drying temperature and residual solvent on the LIDT of solvent-borne polymer coatings. In this work, poly(ethyl methacrylate) (PEMA) coatings were deposited by first spin coating solutions of PEMA (dissolved in 2,2,2-trichloroethanol (TCE)) onto fused silica substrates, then baking at temperatures of either 130°C (soft-bake) or 180°C (hard-bake). Analysis of the two coatings revealed that the soft-bake coating retained a significant amount of TCE within the polymer matrix, which functioned to plasticize the coating and reduce internal stress. The laser-induced damage resistance of the two coatings was evaluated using 351-nm, 1-ns laser pulses. The testing protocols included single-pulse (1-on-1), 1-pulse ramp ( R -on-1), and a 1000-pulse ramp (1000 R -on-1) test. The results showed that the plasticized, soft-bake coating exhibits a significantly increased LIDT, especially for multipulse irradiation conditions.