Al2O3-modified 7YSZ thermal barrier coatings for protection against volcanic ash corrosion
Source abstract
Abstract
Abstract To prevent volcanic ash corrosion using thermal barrier coatings (TBCs), a novel method using Al2O3-modification was proposed to reduce molten CMAS wettability on TBCs surface through a lotus effect. Plasma spray-physical vapor deposition (PS-PVD), a third-generation method for TBCs fabrication, was adopted to deposit 7YSZ TBCs with a feather-like microstructure. Then, Al2O3 modification was introduced to fabricate a dense Al2O3 overlay with nano/micro-sized grains on the TBCs surface. The wetting ability of CMAS on APS/EB-PVD/PS-PVD 7YSZ TBCs was comparatively in situ observed at 1250 °C for 3600 s. The results indicated that the dense Al2O3 overlay inhibited penetration of molten CMAS. Additionally, the micro/nano dual-sized structure, which is similar to the papillary structure of a lotus leaf, reduced molten CMAS wettability on the TBCs surface. The results demonstrated that the Al2O3-modified TBCs had better CMAS corrosion resistance than the as-deposited APS/EB-PVD/PS-PVD TBCs.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Advanced materials and composites · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Naraparaju, R., Schulz, U., Ramana, C. V. & Gomez, J. Interaction and infiltration behavior of Eyjafjallajökull, Sakurajima volcanic ashes and a synthetic CMAS containing FeO with/in EB-PVD ZrO2-65 wt%Y2O3 coating at high temperature. Acta Mater. 136, 164–180 (2017).10.1016/j.actamat.2017.06.055 ↗
2. Fang, H. et al. Investigation of CMAS resistance of sacrificial plasma-sprayed mullite-YSZ protective layer on 8YSZ thermal barrier coating. Corros. Sci. 173, 1–9 (2020).10.1016/j.corsci.2020.108764 ↗
3. Wu, J. et al. Microstructure and thermo-physical properties of yttria stabilized zirconia coatings with CMAS deposits. J. Eur. Ceram. Soc. 31, 1881–1888 (2011).10.1016/j.jeurceramsoc.2011.04.006 ↗
4. Wellman, R. et al. CMAS corrosion of EB PVD TBCs: identifying the minimum level to initiate damage. Int. J. Refract. Met. Hard Mater. 28, 124–132 (2010).10.1016/j.ijrmhm.2009.07.005 ↗
5. Zhang, X. et al. In situ synthesis of α-alumina layer on thermal barrier coating for protection against CMAS (CaO–MgO–Al2O3–SiO2) corrosion. Surf. Coat. Int. 261, 54–59 (2015).10.1016/j.surfcoat.2014.11.064 ↗
6. Zhang, X. et al. Adsorbability and spreadability of calcium-magnesium-alumino-silicate (CMAS) on Al-modified 7YSZ thermal barrier coating. Ceram. Int. 42, 19349–19356 (2016).10.1016/j.ceramint.2016.09.106 ↗
7. Morelli, S. et al. CMAS corrosion of YSZ thermal barrier coatings obtained by different thermal spray processes. J. Eur. Ceram. Soc. 40, 4084–4100 (2020).10.1016/j.jeurceramsoc.2020.04.058 ↗
8. Zhang, X. et al. Tracking the calcium-magnesium-alumino-silicate (CMAS) infiltration into an air-plasma spray thermal barrier coating using X-ray imaging. Scr. Mater. 176, 94–98 (2020).10.1016/j.scriptamat.2019.09.016 ↗
9. Schulz, U. et al. Effect of processing and interface on the durability of single and bilayer 7YSZ/gadolinium zirconate EB-PVD thermal barrier coatings. Surf. Coat. Technol. 381, 1–10 (2020).10.1016/j.surfcoat.2019.125107 ↗
10. Zhang, X. et al. Gas-deposition mechanisms of 7YSZ coating based on plasma spray-physical vapor deposition. J. Eur. Ceram. Soc. 36, 697–703 (2016).10.1016/j.jeurceramsoc.2015.10.041 ↗
11. Mack, D. et al. Lifetime and failure modes of plasma sprayed thermal barrier coatings in thermal gradient rig tests with simultaneous CMAS injection. Surf. Coat. Technol. 324, 36–47 (2017).10.1016/j.surfcoat.2017.04.071 ↗
12. Shan, X. et al. Influence of pore characteristics of air plasma sprayed thermal barrier coatings on calcia-magnesia-alumino-silicate (CMAS) attack behavior. Corros. Sci. 190, 1–9 (2021).10.1016/j.corsci.2021.109636 ↗
13. Li, W. et al. Air plasma-sprayed yttria and yttria-stabilized zirconia thermal barrier coatings subjected to calcium-magnesium-alumino-silicate (CMAS). J. Therm. Spray. Technol. 23, 975–983 (2014).10.1007/s11666-014-0107-0 ↗
14. Li, M. et al. Preparation of nanostructured Gd2Zr2O7-LaPO4 thermal barrier coatings and their calcium-magnesium-alumina-silicate (CMAS) resistance. J. Eur. Ceram. Soc. 37, 3425–3434 (2017).10.1016/j.jeurceramsoc.2017.03.069 ↗
15. Ozgurluk, Y. et al. Investigation of calcium–magnesium-alumino-silicate (CMAS) resistance and hot corrosion behavior of YSZ and La2Zr2O7/YSZ thermal barrier coatings (TBCs) produced with CGDS method. Surf. Coat. Technol. 411, 1–12 (2021).10.1016/j.surfcoat.2021.126969 ↗
16. Yan, Z. et al. Versatility of potential protective layer material Ti2AlC on resisting CMAS corrosion to thermal barrier coatings. Corros. Sci. 167, 1–14 (2020).10.1016/j.corsci.2020.108532 ↗
17. Tan, Z. et al. Mechanical properties and calcium-magnesium-alumino-silicate (CMAS) corrosion behavior of a promising Hf6Ta2O17 ceramic for thermal barrier coatings. Ceram. Int. 46, 25242–25248 (2020).10.1016/j.ceramint.2020.06.316 ↗
18. Bilge, S. et al. CMAS-resistant plasma sprayed thermal barrier coatings based on Y2O3-stabilized ZrO2 with Al3+ and Ti4+ solute additions. J. Therm. Spray. Technol. 23, 708–715 (2014).10.1007/s11666-014-0077-2 ↗
19. Yan, Z. et al. Effects of laser glazing on CMAS corrosion behavior of Y2O3 stabilized ZrO2 thermal barrier coatings. Corros. Sci. 157, 450–461 (2019).10.1016/j.corsci.2019.06.025 ↗
20. Meng, B. et al. Influence of fuel combustion the corrosion behavior of pipeline steels in fire flooding technology. npj Mater. Degrad. 21, 1–9 (2022).
21. Guo, L. et al. Microstructure modification of Y2O3 stabilized ZrO2 thermal barrier coatings by laser glazing and the effects on the hot corrosion resistance. J. Adv. Ceram. 9, 232–242 (2020).10.1007/s40145-020-0363-z ↗
22. Gildersleeve, E. et al. Molten silicate interactions with plasma sprayed thermal barrier coatings: Role of materials and microstructure. J. Eur. Ceram. Soc. 39, 2122–2131 (2019).10.1016/j.jeurceramsoc.2019.01.023 ↗
23. Liu, Z. et al. Modeling stress evolution in porous ceramics subjected to molten silicate infiltration and corrosion. Corros. Sci. 191, 109698–109698 (2021).10.1016/j.corsci.2021.109698 ↗
24. Zhou, X. et al. Failure of plasma sprayed nano-zirconia-based thermal barrier coatings exposed to molten CaO–MgO–Al2O3–SiO2 deposits. J. Am. Ceram. Soc. 102, 6357–6371 (2019).10.1111/jace.16498 ↗
25. Jackson, R. et al. Interaction of molten silicates with thermal barrier coatings under temperature gradients. Acta Mater. 89, 396–407 (2015).10.1016/j.actamat.2015.01.038 ↗
26. Zhang, X. et al. Al2O3-modified PS-PVD 7YSZ thermal barrier coatings for advanced gas-turbine engines. npj Mater. Degrad. 4, 1–6 (2020).10.1038/s41529-020-00134-5 ↗
27. Song, J. et al. Research of in situ modified PS-PVD thermal barrier coating against CMAS (CaO–MgO–Al2O3–SiO2) corrosion. Ceram. Int. 42, 3163–3169 (2016).10.1016/j.ceramint.2015.10.106 ↗
28. Wu, X. et al. Microstructure evolution of Al-modified 7YSZ PS-PVD TBCs in thermal cycle. Ceram. Int 47, 12170–12180 (2021).10.1016/j.ceramint.2021.01.064 ↗
29. Zhang, P. et al. Hot corrosion behavior of YSZ thermal barrier coatings modified by laser remelting and Al deposition. J. Therm. Spray. Technol. 28, 1225–1238 (2019).10.1007/s11666-019-00880-2 ↗
30. Kang, Y. et al. High temperature wettability between CMAS and YSZ coating with tailored surface microstructures. Mater. Lett. 229, 40–43 (2018).10.1016/j.matlet.2018.06.066 ↗
31. Lokachari, S. et al. Novel thermal barrier coatings with hexagonal boron nitride additives resistant to molten volcanic ash wetting. Corros. Sci. 168, 1–7 (2020).10.1016/j.corsci.2020.108587 ↗
32. Qu, W. et al. Hot corrosion behavior and wettability of calcium–magnesium–alumina–silicate (CMAS) on LaTi2Al9O19 ceramic. Corros. Sci. 162, 1–11 (2020).10.1016/j.corsci.2019.108199 ↗
33. Naraparaju, R. et al. Estimation of CMAS infiltration depth in EB-PVD TBCs: A new constraint model supported with experimental approach. J. Eur. Ceram. Soc. 39, 2936–2945 (2019).10.1016/j.jeurceramsoc.2019.02.040 ↗
34. Zhang, B. et al. Wetting, infiltration and interaction behavior of CMAS towards columnar YSZ coatings deposited by plasma spray physical vapor. J. Eur. Ceram. Soc. 38, 3564–3572 (2018).10.1016/j.jeurceramsoc.2018.04.013 ↗
35. Meng, B. et al. On the rumpling mechanism in nanocrystalline coatings: Improved by reactive magnetron sputtering with oxygen. J. Mater. Sci. Technol. 132, 69–80 (2023).10.1016/j.jmst.2022.04.054 ↗