The role of nano-sized intergranular phases on nickel alloy 725 brittle failure

Maria Sofia Hazarabedian, Mariano Iannuzzi

npj Materials Degradation· Volume 5· Issue 1

Abstract

Abstract Although precipitation-hardened nickel alloys, such as Alloy 725, are extensively used in the most aggressive oil and gas production conditions given their a priori superior environmentally assisted cracking resistance, recent failures associated with hydrogen embrittlement (HE) cast doubts about their performance in H-bearing environments. These high-profile incidents have led to extensive research to elucidate the failure mechanism and develop methods to reduce risks. However, the microstructural features that made only specific heats of Alloy 725 susceptible to HE have yet to be agreed upon by the scientific community. Herein, our results showed that the abundant precipitation of F phase, i.e., a recently discovered nano-sized and embrittling phase, at grain boundaries increased cracking susceptibility. A continuous F phase network offered a low-energy path for crack opening by matrix-precipitate interfacial decohesion. Additionally, we correlated Alloy 725 microstructure with HE resistance, which is essential for thermomechanical processing optimization and the design of alternative qualification tests to obtain embrittlement-resistant nickel alloys.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Nuclear Materials and Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (62)

Show source-provided references
1. API 6ACRA. Age-hardened Nickel-based Alloys for Oil and Gas Drilling and Production Equipment (API, 2015).
2. Lu, X., Ma, Y. & Wang, D. On the hydrogen embrittlement behavior of nickel-based alloys: alloys 718 and 725. Mater. Sci. Eng. A 792, 139785 (2020).10.1016/j.msea.2020.139785 ↗
3. Mannan, S. K. Alloy 718 for oilfield applications. JOM 64, 265–270 (2012).10.1007/s11837-012-0238-z ↗
4. Bhavsar, R. B., Collins, A. & Silverman, S. Use of alloy 718 and 725 in oil and gas industry. in Superalloys 718, 625, 706 and Various Derivatives 47−55 (TMS, 2001).10.7449/2001/Superalloys_2001_47_55 ↗
5. Onyewuenyi, O. Alloy 718-alloy optimization for applications in oil and gas production. in Superalloy 718: Metallurgy and Applications 345−362 (TMS, 1989).10.7449/1989/Superalloys_1989_345_362 ↗
6. Iannuzzi, M., Barnoush, A. & Johnsen, R. Materials and corrosion trends in offshore and subsea oil and gas production. npj Mater. Degrad. 1, 2 (2017).10.1038/s41529-017-0003-4 ↗
7. Shademan, S. S., Martin, J. W. & Davis, A. P. UNS N07725 nickel alloy connection failure. In CORROSION 2012 Paper no. 1095 (NACE International, 2012).
8. Nice, P. et al. Hydrogen embrittlement failure of a precipitation hardened nickel alloy subsurface safety valve component installed in a North Sea seawater injection well. In CORROSION 2014 Paper no. 3892 (NACE International, 2014).
9. Cassagne, T., Bonis, M. & Duret, C. Understanding field failures of alloy 718 forging materials in HP/HT wells. In EUROCORR 2008 1−13 (European Federation of Corrosion, 2008).
10. McCoy, S. A., Mannan, S. K., Tassen, C. S., Maitra, D. & Crum, J. R. Investigation of the effects of hydrogen on high strength precipitation hardened nickel alloys for O&G service. In CORROSION 2015 (NACE International, 2015).
11. Duret-Thual, C. et al. Assessment of the hydrogen induced stress cracking resistance of precipitation hardened nickel-based alloys using the slow strain rate tensile test method—review of a three years test program. In CORROSION 2019, Paper no. 13284 (NACE International, 2019).
12. McCoy, S. A., Maitra, D., Mannan, S. K., Crum, J. R. & Tassen, C. S. The effect of hydrogen on plain and notched test specimens of precipitation hardenable nickel alloys. In CORROSION 2017 Paper no. 9655 (NACE International, NACE, 2017).
13. Dodge, M., Sotoudeh, K., Gittos, M. & Griffiths, D. Hydrogen embrittlement of high strength precipitation hardenable nickel alloys. In CORROSION 2019 p. 15 (NACE International, NACE, 2019).
14. Rebak, R. B. Environmentally assisted cracking of commercial Ni-Cr-Mo alloys—a review. In CORROSION/2005 Conference paper no. 5457 (NACE International, 2004).
15. Klöwer, J., Gosheva, O., Klapper, H. S. & Tarzimoghadam, Z. Effect of microstructural particularities on the corrosion resistance of nickel alloy UNS N07718—what really makes the difference? In CORROSION 2017 (NACE International, 2017).
16. Morana, R., Smith, L. & Venkateswaran, S. P. On the susceptibility of precipitation hardened nickel alloys to hydrogen assisted cracking. In CORROSION 2019 (NACE International, 2019).
17. Zhang, Z., Moore, K. L., McMahon, G., Morana, R. & Preuss, M. On the role of precipitates in hydrogen trapping and hydrogen embrittlement of a nickel-based superalloy. Corros. Sci. 146, 58–69 (2019).10.1016/j.corsci.2018.10.019 ↗
18. Stenerud, G., Johnsen, R. & Olsen, J. S. Hydrogen stress cracking and crack initiation in precipitation hardened Ni-alloys. Eng. Fail. Anal. 89, 74–87 (2018).10.1016/j.engfailanal.2018.02.023 ↗
19. Hanson, J. P., Seita, M., Jones, E., Gradecak, S. & Demkowicz, M. J. Hydrogen embrittlement behavior in precipitation hardened Ni-base alloys. In CORROSION 2015 (NACE International, 2015).
20. Seita, M., Hanson, J. P., Gradečak, S. & Demkowicz, M. J. The dual role of coherent twin boundaries in hydrogen embrittlement. Nat. Commun. 6, 6164 (2014).10.1038/ncomms7164 ↗
21. Hanson, J. P. et al. Crystallographic character of grain boundaries resistant to hydrogen-assisted fracture in Ni-base alloy 725. Nat. Commun. 9, 3386 (2018).10.1038/s41467-018-05549-y ↗
22. Lu, X. & Wang, D. Effect of hydrogen on deformation behavior of Alloy 725 revealed by in-situ bi-crystalline micropillar compression test. J. Mater. Sci. Technol. 67, 243–253 (2020).10.1016/j.jmst.2020.08.006 ↗
23. Humphreys, J., Rohrer, G. S. & Rollett, A. Recrystallization and Related Annealing Phenomena (Elsevier, 2017).10.1016/B978-0-08-098235-9.00012-4 ↗
24. Rohrer, G. S., Randle, V., Kim, C. S. & Hu, Y. Changes in the five-parameter grain boundary character distribution in a-brass brought about by iterative thermomechanical processing. Acta Mater. 54, 4489–4502 (2006).10.1016/j.actamat.2006.05.035 ↗
25. Zhang, Z. et al. Strain localisation and failure at twin-boundary complexions in nickel-based superalloys. Nat. Commun. 11, 4890 (2020).10.1038/s41467-020-18641-z ↗
26. Chen, J. & Dongare, A. M. Role of grain boundary character on oxygen and hydrogen segregation-induced embrittlement in polycrystalline Ni. J. Mater. Sci. 52, 30–45 (2017).10.1007/s10853-016-0389-3 ↗
27. Zhang, Z., Obasi, G., Morana, R. & Preuss, M. Hydrogen assisted crack initiation and propagation in a nickel-based superalloy. Acta Mater. 113, 272–283 (2016).10.1016/j.actamat.2016.05.003 ↗
28. Aboura, Y., Martelo, D. F., Morana, R., Akid, R. & Moore, K. L. Characterising hydrogen induced cracking of alloy 625+ using correlative SEM-EDX and NanoSIMS. Corros. Sci. 181, 109228 (2021).10.1016/j.corsci.2020.109228 ↗
29. Bagri, A. et al. Measuring grain boundary character distributions in Ni-base alloy 725 using high-energy diffraction microscopy. Metall. Mater. Trans. A 48, 354–361 (2017).10.1007/s11661-016-3831-x ↗
30. Salvatori, I. et al. Assessment of the hydrogen induced stress cracking resistance of precipitation hardened nickel-based alloys using the slow strain rate tensile test method: influence of microstructure. In CORROSION 2019 Paper no. 13365 (NACE International, 2019).
31. Li, X., Viswanathan, G. B. & Thodla, R. Hydrogen embrittlement study of two heats of UNS N07725 in sea water under cathodic polarization conditions. In CORROSION 2020 Paper no. 15008 (NACE International, 2020).
32. Martelo, D. F., Morana, R. & Akid, R. Understanding the mechanical behaviour of 718 and 625+ nickel based super-alloys under cathodic polarization. Theor. Appl. Fract. Mech. 112, 102871 (2021).10.1016/j.tafmec.2020.102871 ↗
33. Mannan, S. & Veltry, F. Time-temperature-transformation diagram of alloy 725. in Superalloys 718, 625, 706 and Various Derivatives 345−356 (TMS, 2001).10.7449/2001/Superalloys_2001_345_356 ↗
34. Hazarabedian, M. S., Quadir, M. Z. & Iannuzzi, M. Characterization of intergranular phases in precipitation hardening Ni alloy UNS N07725. Mater. Charact. 171, 110770 (2021).10.1016/j.matchar.2020.110770 ↗
35. Sabol, G. P. & Stickler, R. Microstructure of nickel‐based superalloys. Phys. Stat. Sol. 35, 11–52 (1969).10.1002/pssb.19690350102 ↗
36. Wilson, A. S. Formation and effect of topologically close-packed phases in nickel-base superalloys. Mater. Sci. Technol. 33, 1108–1118 (2017).10.1080/02670836.2016.1187335 ↗
37. Hazarabedian, M. S., Quadir, M. Z. & Iannuzzi, M. Detecting intergranular phases in UNS N07725. Part II: Double-loop electrochemical potentiokinetic reactivation test validation. J. Electrochem. Soc. 168, 031516 (2021).10.1149/1945-7111/abf065 ↗
38. Hazarabedian, M. S., Lison-Pick, M., Quadir, M. Z. & Iannuzzi, M. Detecting intergranular phases in UNS N07725. Part I: Adapting the double-loop electrochemical potentiokinetic reactivation test. J. Electrochem. Sci., 168, 031506 (2021).10.1149/1945-7111/abe9d0 ↗
39. Hazarabedian, M. S. et al. Hydrogen-induced stress cracking of swaged super duplex stainless steel subsea components. CORROSION 75, 824–838 (2019).10.5006/3192 ↗
40. Ou, K. C. & Wu, J. K. Effect of calcareous deposits formation on the hydrogen absorption of steel. Mater. Chem. Phys. 48, 52–55 (1997).10.1016/S0254-0584(97)80076-4 ↗
41. Lin, Y. P. & Steeds, J. W. Identification of a hitherto unreported Frank−Kasper phase. Acta Cryst. B42, 159–162 (1986).10.1107/S0108768186098427 ↗
42. Li, D. X. & Kuo, K. H. Some new σ-related structures determined by high-resolution electron microscopy. Acta Cryst. B42, 152–159 (1986).10.1107/S0108768186098439 ↗
43. Ramgopal, T., Viswanathan, G. B., Amaya, H., Fahimi, B. & Taylor, C. D. Crack growth behavior of 725 in seawater under cathodic polarization. Mater. Sci. Eng. A 814, 141112 (2021).10.1016/j.msea.2021.141112 ↗
44. Shi, Q. et al. Fracture mode of a Ni-based single crystal superalloy containing topologically close-packed phases at ambient temperature. Metall. Mater. Trans. A 45A, 1665–1669 (2014).10.1007/s11661-014-2190-8 ↗
45. Nowell, M. M., Witt, R. A. & True, B. W. EBSD sample preparation: techniques, tips, and tricks. Microsc. Microanal. 11, 504–505 (2005).
46. Winiarski, B. et al. Broad ion beam serial section tomography. Ultramicroscopy 172, 52–64 (2017).10.1016/j.ultramic.2016.10.014 ↗
47. Kirby, G. N., Sponseller, D. L. & Van Vlack, L. H. The relative effects of chromium, molybdenum, and tungsten on the occurrence of σ-phase in Ni−Co−Cr alloys. Metall. Trans. 5, 1477–1494 (1974).10.1007/BF02646635 ↗
48. Kernion, S. J., Magee, J. H., Werley, T. N. & Maxwell, P. Offshore Technology Conference (Offshore Technology Conference, 2014).
49. Porter, D. A. & Easterling, K. E. Phase Transformations in Metals and Alloys (Springer, 1992).10.1007/978-1-4899-3051-4 ↗
50. Zhang, Z., Obasi, G., Morana, R. & Preuss, M. In-situ observation of hydrogen induced crack initiation in a nickel-based superalloy. Scr. Mater. 140, 40–44 (2017).10.1016/j.scriptamat.2017.07.006 ↗
51. Mannan, S. & Puckett, B. Physical metallurgy of alloys 718, 925, 725, and 725HS for service in aggressive corrosion environments. In CORROSION 2003 Paper no. 03126 (NACE International, 2003).
52. International Organization for Standardization. Petroleum, petrochemical, and natural gas industries—test methods for quality control of microstructure of ferritic/austenitic (duplex) stainless steels (ISO 17781:2017). (2017).
53. Majidi, A. P. & Streicher, M. A. The double loop reactivation method for detecting sensitization in AISI 304 stainless steels. CORROSION 40, 584–593 (1984).10.5006/1.3581921 ↗
54. Pound, B. G. Hydrogen trapping in precipitation-hardened alloys. Acta Metall. Mater. 38, 2373–2381 (1990).10.1016/0956-7151(90)90250-K ↗
55. Bechtle, S., Kumar, M., Somerday, B. P., Launey, M. E. & Ritchie, R. O. Grain-boundary engineering markedly reduces susceptibility to intergranular hydrogen embrittlement in metallic materials. Acta Mater. 57, 4148–4157 (2009).10.1016/j.actamat.2009.05.012 ↗
56. Palumbo, G. & Aust, K. T. Solute effects in grain boundary engineering. Can. Metall. Q. 34, 165–173 (1995).10.1179/cmq.1995.34.3.165 ↗
57. Trillo, E. et al. Assessment of the hydrogen induced stress cracking resistance of precipitation hardened nickel-based alloys using the slow strain rate tensile test method—experimental parameters and related issues. In CORROSION 2019 Paper no. 13455 (NACE International, 2019).
58. Li, X., Viswanathan, G. B. & Thodla, R. Hydrogen embrittlement study of three heats of UNS N07718 in subsea applications. In CORROSION 2019 (NACE International, 2019).
59. ASTM G 1–03. Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens (ASTM International, 2017).
60. Burgess, S., Sagar, J., Holland, J., Li, X. & Bauer, F. Ultra-low kV EDS—a new approach to improved spatial resolution, surface sensitivity, and light element compositional imaging and analysis in the SEM. Microscopy Today 25, 20−29 (2017).10.1017/S1551929517000013 ↗
61. Tomus, D. & Ng, H. P. In situ lift-out dedicated techniques using FIB–SEM system for TEM specimen preparation. Micron 44, 115–119 (2013).10.1016/j.micron.2012.05.006 ↗
62. Grabulov, A., Petrov, R. & Zandbergen, H. W. EBSD investigation of the crack initiation and TEM/FIB analyses of the microstructural changes around the cracks formed under rolling contact fatigue (RCF). Int. J. Fatigue 32, 576–583 (2010).10.1016/j.ijfatigue.2009.07.002 ↗