Three-dimensional strain imaging of irradiated chromium using multi-reflection Bragg coherent diffraction

Abstract Radiation-induced materials degradation is a key concern in limiting the performance of nuclear materials. The formation of nanoscale void and gas bubble superlattices in metals and alloys under radiation environments can effectively mitigate radiation-induced damage, such as swelling and aid the development of next generation radiation tolerant materials. To effectively manage radiation-induced damage via superlattice formation, it is critical to understand the microstructural changes and strain induced by such superlattices. We utilize multi-reflection Bragg coherent diffraction imaging to quantify the full strain tensor induced by void superlattices in iron irradiated chromium substrate. Our approach provides a quantitative estimation of radiation-induced three-dimensional (3D) strain generated at the microscopic level and predicts the number density of defects with a high degree of sensitivity. Such quantitative evaluation of 3D strain in nuclear materials can have a major impact on predicting materials behavior in radiation environments and can revolutionize design of radiation tolerant materials.