Incorporating alkali-catalyzed nano-silica sol to enhance the durability of sodium carbonate-activated slag mortar in aggressive environments
Source abstract
Abstract
Sodium carbonate-activated slag mortar (SCASM) exhibits the advantages of low shrinkage, high strength in late age, and low-cost and carbon emissions. However, its microstructure is relatively porous due to the formation of crystalline carbonate phases, which compromise its durability in marine and other aggressive environments. To address this, a highly reactive and dispersive alkali-catalyzed nano-silica sol (NSS) was incorporated to enhance the durability of SCASM. The mechanisms were explored using scanning electron microscopy, X-ray diffraction, and mercury intrusion porosimetry. The results showed that NSS significantly reduced the porosity and pore connectivity of SCASMs, decreasing their surface alkalinity, immersion porosity, capillary water absorption, and susceptibility to freeze-thaw damage. Under sodium sulfate and magnesium sulfate erosion, the strength loss of SCASM decreased markedly with increasing NSS content. Notably, after 180 days in sodium sulfate solution, the incorporation of 8% NSS reduced the compressive and flexural strength loss rates of SCASM by 46.9 and 41.9%, respectively, compared to the control without NSS. Furthermore, NSS significantly enhanced the SCASM’s resistance to chloride ion penetration, and chloride salt dry-wet cycles. The improvements are primarily due to the NSS-induced refinement of pore structure that hindered aggressive ion ingress, combined with the physical adsorption of the aggressive ions by alkali-catalyzed NSS. These collectively suppressed expansive product formation and thus mitigated SCASM degradation in corrosive environments. Additionally, NSS promoted the formation of a more polymerized and stable gel structure, enhancing its resistance to destabilization under aggressive conditions. This study offers an effective and low-cost solution to improve the durability of SCASMs, promoting their practical application in marine and other aggressive environments.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Microbial Applications in Construction Materials · Magnesium Oxide Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (74)
Show source-provided references
1. Xu, J. et al. An estimation of future county-level cement production and associated air pollutant emissions in China through artificial neural networks. Sci. Total Environ. 953, 176036 (2024).10.1016/j.scitotenv.2024.176036 ↗
2. Han, J., Sun, Q. & Jiang, Y. Studying the risk spillover effects of the carbon market and high-carbon-emission industries under economic uncertainty. Front. Environ. Sci. 12, 1407135 (2024).10.3389/fenvs.2024.1407135 ↗
3. Liu, X. et al. Carbon and air pollutant emissions forecast of China’s cement industry from 2021 to 2035. Resour. Conserv. Recy. 204, 107498 (2024).10.1016/j.resconrec.2024.107498 ↗
4. Zhen, X. et al. Cracking resistance and sustainability assessment of alkali-activated slag concrete incorporating lightweight aggregate. Cem. Concr. Compos. 131, 104556 (2022).10.1016/j.cemconcomp.2022.104556 ↗
5. Hojati, M. & Radlińska, A. Shrinkage and strength development of alkali-activated fly ash-slag binary cements. Constr. Build. Mater. 150, 808–816 (2017).10.1016/j.conbuildmat.2017.06.040 ↗
6. Jiang, H. et al. Effectiveness of alkali-activated slag as alternative binder on workability and early age compressive strength of cemented paste backfills. Constr. Build. Mater. 218, 689–700 (2019).10.1016/j.conbuildmat.2019.05.162 ↗
7. Xuan, Y., Wang, S., Lin, R., Kown, S. & Wang, X. Strength enhancement–carbon emission reduction–autogenous shrinkage mitigation of cement-slag-limestone ultra-high-performance concrete by using natural wollastonite. J. Build. Eng. 115, 114598 (2025).10.1016/j.jobe.2025.114598 ↗
8. Kucharczyková, B. et al. Comprehensive study of moist curing duration and activator type on mechanical properties, shrinkage, and cracking of alkali-activated slag. Constr. Build. Mater. 416, 135199 (2024).10.1016/j.conbuildmat.2024.135199 ↗
9. Luukkonen, T. et al. Influence of sodium silicate powder silica modulus for mechanical and chemical properties of dry-mix alkali-activated slag mortar. Constr. Build. Mater. 233, 117354 (2020).10.1016/j.conbuildmat.2019.117354 ↗
10. Jiao, Z., Wang, Y., Zheng, W. & Huang, W. Effect of the activator on the performance of alkali-activated slag mortars with pottery sand as fine aggregate. Constr. Build. Mater. 197, 83–90 (2019).10.1016/j.conbuildmat.2018.11.178 ↗
11. He, J. et al. Effect of reactive MgO on hydration and properties of alkali-activated slag pastes with different activators. Constr. Build. Mater. 271, 121608 (2020).10.1016/j.conbuildmat.2020.121608 ↗
12. Du, T. & Liu, Y. Effect of water glass on setting time and mechanical properties of fly ash slag geopolymer. Phys. Conf. Ser. 1676, 012024 (2020).10.1088/1742-6596/1676/1/012024 ↗
13. Yang, C. et al. Effects of different activators on autogenous shrinkage of alkali-activated slag cement. Constr. Build. Mater. 446, 138018 (2024).10.1016/j.conbuildmat.2024.138018 ↗
14. Cartwright, C., Rajabipour, F. & Aleksandra, R. Shrinkage characteristics of alkali-activated slag cements. J. Mater. Civ. Eng. 27, B4014007 (2014).10.1061/(ASCE)MT.1943-5533.0001058 ↗
15. Yang, J. et al. Effect of Na2CO3 on the tensile creep of slag-fly ash systems activated with Na2SiO3. Cem. Concr. Compos. 140, 105110 (2023).10.1016/j.cemconcomp.2023.105110 ↗
16. Wang, S., Lin, R. & Wang, Y. Insights on solid CO2 mixing method for hybrid alkaline cement (HAC): performance, sustainability, and experimental system improvement. Cem. Concr. Compos. 161, 106096 (2025).10.1016/j.cemconcomp.2025.106096 ↗
17. Mavroulidou, M., Sanam, I. & Mengasini, L. Mechanical and durability performance of alkali-activated slag cement concretes with carbonate and silicate activators. Sustain. Chem. Pharm. 31, 100896 (2023).10.1016/j.scp.2022.100896 ↗
18. Adeyemi, A. Performance and sustainability overview of sodium carbonate activated slag materials cured at ambient temperature. Resour. Environ. Sustain. 3, 100016 (2021).
19. Liu, C., Yao, X. & Zhang, W. Controlling the setting times of one-part alkali-activated slag by using honeycomb ceramics as carrier of sodium silicate activator. Constr. Build. Mater. 235, 117091 (2020).10.1016/j.conbuildmat.2019.117091 ↗
20. Adenisa, A. Influence of various additives on the early age compressive strength of sodium carbonate activated slag composites: an overview. J. Mech. Behav. Mater. 29, 106–113 (2020).10.1515/jmbm-2020-0011 ↗
21. Cui, H. et al. Effect of carbon nanotubes on properties of alkali activated slag—a mechanistic study. J. Clean. Prod. 245, 119021 (2020).10.1016/j.jclepro.2019.119021 ↗
22. Ren, J. et al. Constructing a novel nano-TiO2/Epoxy resin composite and its application in alkali-activated slag/fly ash pastes. Constr. Build. Mater. 232, 117218 (2020).10.1016/j.conbuildmat.2019.117218 ↗
23. Yan, H. et al. Research progress of nano-materials to optimize the performance of cement-based materials. Mater. China 36, 645–652 (2017).
24. Yang, Z., He, R., Tan, Y., Chen, H. & Cao, D. Air pore structure, strength and frost resistance of air-entrained mortar with different content of nano-SiO2 hydrosol. Constr. Build. Mater. 308, 125096 (2021).10.1016/j.conbuildmat.2021.125096 ↗
25. Muhammad, H. K. et al. Evaluation of mechanical strength, gamma-ray shielding characteristics, and ITZ microstructural properties of heavyweight concrete using nano-silica (SiO2) and barite aggregates. Constr. Build. Mater. 419, 135483 (2024).10.1016/j.conbuildmat.2024.135483 ↗
26. Xu, Z. et al. Promoting utilization rate of ground granulated blast furnace slag (GGBS): incorporation of nanosilica to improve the properties of blended cement containing high volume GGBS. J. Clean. Prod. 332, 130096 (2022).10.1016/j.jclepro.2021.130096 ↗
27. Chen, P., Tian, F., Zhang, J., Li, Y. & We, Y. Effect of nano-silica on mechanical properties and shrinkage of alkali-activated slag cementitious material. Dev. Built Environ. 19, 100525 (2024).10.1016/j.dibe.2024.100525 ↗
28. Wang, W., Wang, B. & Zhang, S. Dispersion, properties, and mechanisms of nanotechnology-modified alkali-activated materials: a review. Renew. Sust. Energ. Rev. 192, 114215 (2024).10.1016/j.rser.2023.114215 ↗
29. Ramezanianpour, A. A. & Moeini, A. M. Mechanical and durability properties of alkali activated slag coating mortars containing nanosilica and silica fume. Constr. Build. Mater. 163, 611–621 (2018).10.1016/j.conbuildmat.2017.12.062 ↗
30. Yin, X. & Dai, Y. Characteristics, manufacture and application of silica sol. Chem. Propellants Polymeric Mater. 3, 27–32 (2005).
31. Chen, J., Huang, P., Xu, L. & Kwan, A. K. H. Use of nano-silica sol in concrete: Performance and influence mechanisms. Constr. Build. Mater. 411, 134582 (2024).10.1016/j.conbuildmat.2023.134582 ↗
32. Kong, D., Corr, D. J., Hou, P., Yang, Y. & Shah, S. P. Influence of colloidal silica sol on fresh properties of cement paste as compared to nano-silica powder with agglomerates in micron-scale. Cem. Concr. Compos. 63, 30–41 (2015).10.1016/j.cemconcomp.2015.08.002 ↗
33. Kong, D. et al. Effect and mechanism of colloidal silica sol on properties and microstructure of the hardened cement-based materials as compared to nano-silica powder with agglomerates in micron-scale. Cem. Concr. Compos. 98, 137–249 (2019).10.1016/j.cemconcomp.2019.02.015 ↗
34. Liu, H., Li, Q., Su, D., Yue, G. & Wang, L. Study on the influence of nanosilica sol on the hydration process of different kinds of cement and mortar properties. Mater 14, 3653 (2021).10.3390/ma14133653 ↗
35. Tanimola, O. J. & Efe, S. Recent advances in nano-modified concrete: enhancing durability, strength, and sustainability through nano silica (nS) and nano titanium (nT) incorporation. Appl. Eng. Sci. 19, 100189 (2024).
36. Long, W., Xiao, B., Gu, Y. & Xing, F. Micro- and macro-scale characterization of nano-SiO2 reinforced alkali activated slag composites. Mater. Charact. 136, 111–121 (2018).10.1016/j.matchar.2017.12.013 ↗
37. Gao, X., Yu, Q. & Brouwers, H. Characterization of alkali activated slag–fly ash blends containing nano-silica. Constr. Build. Mater. 98, 397–406 (2015).10.1016/j.conbuildmat.2015.08.086 ↗
38. Adak, D., Sarkar, M. & Mandal, S. Effect of nano-silica on strength and durability of fly ash based geopolymer mortar. Constr. Build. Mater. 70, 453–459 (2014).10.1016/j.conbuildmat.2014.07.093 ↗
39. Ibrahim, M., Salami, B. A., Khallaf, Z., Bahraq, A. & Adewumi, A. A. Evaluating long-term durability of nanosilica-enhanced alkali-activated concrete in sulfate environments towards sustainable concrete development. Constr. Build. Mater. 438, 137315 (2024).10.1016/j.conbuildmat.2024.137315 ↗
40. Liu, H. et al. Study on mechanical properties and mechanism of sodium mortar reinforced by nanosilica sol. Mater. Rep. 39, 24060009 (2025).
41. Alexander, J. M., Dana, E. M. & Michel, W. B. High volume limestone alkali-activated cement developed by design of experiment. Cem. Concr. Compos. 34, 328–336 (2011).
42. You, S. et al. Tensile creep behavior and crack resistance of alkali-activated slag concrete with recycled concrete aggregate. Fujian Agriculture and Forestry University (2023).
43. Yang, J., Lin, T., Zhang, J., Chen, X. & Ji, T. Autogenous shrinkage mechanism of slag mortar activated by calcium oxide-sodium carbonate composite. J. Harbin Inst. Technol. 56, 86–94 (2024).
44. Yang, T. et al. Accelerated carbonation of one-part sodium carbonate-activated slag cements modified by calcined dolomite. Constr. Build. Mater. 375, 131073 (2023).10.1016/j.conbuildmat.2023.131013 ↗
45. General Administration of Quality Supervision, Inspection and Quarantine. GB/T 50081-2019 Standard for Test Method of Concrete Physical and Mechanical Properties (Building Industry Press, 2019).
46. Lu, L., Yang, Z., Lin, Y. & Dong, S. Partial replacement of manufactured sand with homologous granite powder in mortar: the effect on porosity and capillary water absorption. Constr. Build. Mater. 376, 131031 (2023).10.1016/j.conbuildmat.2023.131031 ↗
47. ASTM-C1585-13. Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes (ASTM, 2020).
48. General Administration of Quality Supervision, Inspection and Quarantine. GB/T 50082-2024 Standard for Test Methods of Long-Term Performance and Durability of Concrete (Building Industry Press, 2024).
49. Wang, S. et al. Alternative application of wollastonite in limestone calcined Hwangtoh clay cement (LC3) systems: engineering properties, microanalysis and resistance to sulfuric acid attack. Constr. Build. Mater. 475, 141214 (2025).10.1016/j.conbuildmat.2025.141214 ↗
50. Huang, X., Hu, S., Wang, F., Liu, Y. & Mu, Y. Properties of alkali-activated slag with addition of cation exchange material. Constr. Build. Mater. 146, 321–328 (2017).10.1016/j.conbuildmat.2017.03.127 ↗
51. Song, W. et al. Mechanical performance and micro-mechanism of alkali-activated binary/ternary composite industrial waste residues cementitious. Mater., Mater. Rep. 34, 22070–22077 (2020).
52. Liang, Y., Chen, L., Zhang, Y., Lin, X. & Ji, T. Study on the performance degradation and mechanism of CaO-Na2CO3 excitation slag mortar under sulfate immersion environment. Bull. Chin. Ceram. Soc. 41, 3556–3566 (2022).
53. Jebli, M., Jamin, F., Pelissou, C., Lhopital, E. & Youssoufi, M. S. E. l Characterization of the expansion due to the delayed ettringite formation at the cement paste-aggregate interface. Constr. Build. Mater. 289, 122979 (2021).10.1016/j.conbuildmat.2021.122979 ↗
54. Gu, Y., Martin, R., Metalssi, O., Fen-Chong, T. & Dangla, P. Pore size analyses of cement paste exposed to external sulfate attack and delayed ettringite formation. Cem. Concr. Res. 123, 105766 (2019).10.1016/j.cemconres.2019.05.011 ↗
55. Zhu, Y. et al. Solidification of chloride ions in alkali-activated slag. Constr. Build. Mater. 320, 126219 (2022).10.1016/j.conbuildmat.2021.126219 ↗
56. Gou, M., Huang, F. & Guan, X. The uring effect of slag on chloride ion. Mater. Rep. 28, 120–122 (2014). (in Chinese).
57. Wang, T. et al. Effects of Al in C–A–S–H gel on the chloride binding capacity of blended cement paste. Cem. Concr. Res. 190, 107805 (2025).10.1016/j.cemconres.2025.107805 ↗
58. Long, W., Xiao, B., Gu, Y. & Xing, F. Micro-and macro-scale characterization of nano-SiO2 reinforced alkali activated. Mater. Charact. 136, 111–121 (2018).10.1016/j.matchar.2017.12.013 ↗
59. Qing, G., Liu, L. & Yin, X. The pore structure changes of alkali-activated slag paste under freeze-thaw cycles. Henan Sci. 38, 755–762 (2020).
60. Grzegorczyk-Frańczak, M., Barnat-Hunek, D., Materak, K. & Łagód, G. Influence of water with oxygen and ozone micro-nano bubbles on concrete physical properties. Mater 15, 7938 (2022).10.3390/ma15227938 ↗
61. Cui, X. Experiment on the influence of nano-admixture on the performance of dam concrete under freeze-thaw cycle. Hunan Hydro Power 0, 85–88 (2024).
62. Liu, L. et al. Degradation of alkali-activated slag pastes exposed to high-concentration chloride, sulfate and magnesium multi-salt solutions. Constr. Build. Mater. 464, 140182 (2025).10.1016/j.conbuildmat.2025.140182 ↗
63. Ye, H., Chen, Z. & Huang, L. Mechanism of sulfate attack on alkali-activated slag: the role of activator composition. Cem. Concr. Res. 125, 105868 (2019).10.1016/j.cemconres.2019.105868 ↗
64. Said, A. M., Islam, M. S., Zeidan, M. S. & Mahgoub, M. Effect of nano-silica on the properties of concrete and Its interaction with slag. Transp. Res. Rec. 2675, 47–55 (2021).10.1177/0361198120943196 ↗
65. Wei, M. et al. Alkali-activated materials modified with micro-nano additives: a review. Mater. Rep. 37, 254–263 (2023).
66. Zhang, X. et al. Effects of particle size of colloidal nanosilica on hydration of Portland cement at early age. Adv. Mech. Eng. 11, 1687814019828948 (2019).10.1177/1687814019828948 ↗
67. Yang, J. Molecular dynamics simulation of microstructure and properties of hydrated calcium aluminosilicate. (Wuhan University of Technology, 2019).
68. Li, S. et al. Interfacial and nanoconfinement effects on electric field-driven chloride migration in C-(A)-S-H nanopores. Case Stud. Constr. Mater. 23, e05344 (2025).
69. Wang, B., Yang, H., Fan, C., Liu, F. & Lu, W. Adsorption behavior and immobilization mechanism of typical heavy metals in synthetic C − A − S − H gels. Microporous Mesoporous Mater. 403, 114030 (2026).10.1016/j.micromeso.2026.114030 ↗
70. Yan, Y. & Dai, Y. Properties, preparation and application of silica sol. Chem. Propellants Polymeric Mater. 03, 35–40 (2005).
71. Ruiz, A. I., Reyes, E., Argiz, C., de la Rubia, M. A. & Moragues, A. Nano-scale aluminium interaction in synthetic hydrated calcium silicate gel studied by 29Si MAS-NMR. Bol. Soc. Esp. Ceram. Vidr. 62, 388–401 (2023).10.1016/j.bsecv.2022.06.004 ↗
72. Qin, L., Qu, B. & Shi, C. The effect of calcium-silicon ratio on the formation and properties of aluminosilicate gels. Mater. Rep. 34, 12057–12063 (2020).
73. Ba, H. et al. Effect of calcium to silicon ratio on the microstructure of hydrated calcium silicate gels prepared under medium alkalinity. Constr. Build. Mater. 379, 131240 (2023).10.1016/j.conbuildmat.2023.131240 ↗
74. Ewa, K., Lukasz, K. & Agnieszka, R. Golek, Lukasz, Incorporation of Al in C − A − S − H gels with various Ca/Si and Al/Si ratio: microstructural and structural characteristics with DTA/TG, XRD, FTIR and TEM analysis. Constr. Build. Mater. 155, 643–653 (2017).10.1016/j.conbuildmat.2017.08.091 ↗