Understanding hydrogen permeation in zinc flake coatings for hydrogen embrittlement mitigation
Source abstract
Abstract
Abstract Zinc flake coatings offer a viable alternative to conventional zinc applications like hot-dip galvanizing or electroplating, especially for high-strength steels prone to hydrogen embrittlement. Unlike electroplated coatings, they do not generate hydrogen during application, providing cathodic protection without compromising safety. However, under real-world conditions, hydrogen uptake can still occur due to corrosion processes, as for all zinc systems. This study examines the hydrogen permeation behavior of zinc flake-coated interstitial-free steel. Comparative analyses are conducted on two different zinc flake coatings containing either pure Zn flakes or alloyed ZnAlMg flakes, with a focus on their characteristics regarding corrosion-induced hydrogen permeation. Electrochemical techniques, including linear sweep voltammetry, and permeation tests using a Devanathan-Stachurski cell, are carried out to evaluate permeation behavior and calculate the diffusion coefficients of the coated and uncoated steel samples. Experimental data were compared and fit with a constant flux and a constant concentration boundary condition. The alloyed ZnAlMg flake system shows higher permeation than the Zn flakes at the same hydrogen generation current. Both have a lower overall diffusion coefficient during hydrogen generation than the bare steel, with the Zn flake system exhibiting the lowest. The findings contribute to a deeper understanding of the influencing factors of corrosion-induced hydrogen permeation mechanisms in zinc flake-coated steel. This knowledge facilitates the optimization and development of zinc flake systems tailored to minimize hydrogen permeation risks while maintaining superior corrosion resistance.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Hydrogen embrittlement and corrosion behaviors in metals · Corrosion Behavior and Inhibition · Electrodeposition and Electroless Coatings
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (42)
Show source-provided references
1. Fumagalli, G., Bolzoni, F., Fallahmohammadi, E., Re, G. & Lazzari, L. Electrochemical methods for determining diffusion coefficient of hydrogen in steels. Corros. Eng., Sci. Technol. 50, 203–210 (2015).10.1179/1743278215Y.0000000017 ↗
2. Dwivedi, S. K. & Vishwakarma, M. Hydrogen embrittlement in different materials: a review. Int. J. Hydrog. Energy 43, 21603–21616 (2018).10.1016/j.ijhydene.2018.09.201 ↗
3. Turnbull, A. Perspectives on hydrogen uptake, diffusion and trapping. Int. J. Hydrog. Energy 40, 16961–16970 (2015).10.1016/j.ijhydene.2015.06.147 ↗
4. DIN Deutsches Institut für Normung e.V. DIN EN ISO 10683: Fasteners - Nonelectrolytically applied zinc flake coating systems (ISO 10683:2018) (Beuth Verlag, 2018).
5. Chatterjee, B. Science and industry of processes for zinc-based coatings with improved properties. Jahrb. Oberfl. 72, 1–34 (2017).
6. Oleksiak, B., Kołtało, K. & Poloczek, R. Application methods and selected properties of zinc flake coatings. Metalurgija 60, 162–164 (2021).
7. Wynn, P. Fastener coating developments. Trans. IMF 81, B16–B18 (2003).10.1080/00202967.2003.11871475 ↗
8. Ren, H. et al. Highly economic and high quality zinc-flake manufacturing by high kinetic processing. In Proc. Korean Powder Metallurgy Institute Conference, 975–976 (The Korean Powder Metallurgy Institute, 2006).
9. Zubielewicz, M. et al. Concepts of steel protection by coatings with a reduced content of zinc pigments. Prog. Org. Coat. 161, 106471 (2021).10.1016/j.porgcoat.2021.106471 ↗
10. Feldmann, F., Mears, L. L., Roth, M. & Valtiner, M. Characterisation of the galvanic protection of zinc flake coating by spectroelectrochemistry and industrial testing. Mater. Corros. 74, 1148–1158 (2023).10.1002/maco.202213719 ↗
11. Sato, R. & Takai, K. Quantitative hydrogen trap states on high-angle grain boundaries and at dislocations in iron. Scr. Mater. 228, 115339 (2023).10.1016/j.scriptamat.2023.115339 ↗
12. Hagi, H. Diffusion coefficient of hydrogen in iron without trapping by dislocations and impurities. Mater. Trans. JIM 35, 112–117 (1994).10.2320/matertrans1989.35.112 ↗
13. Devanathan, M. & Stachurski, Z. The adsorption and diffusion of electrolytic hydrogen in palladium. Proc. R. Soc. Lond. Ser. A. Math. Phys. Sci. 270, 90–102 (1962).
14. Tada, E. & Kaneko, H. Galvanic corrosion of a Zn/steel couple in aqueous Nacl. ISIJ Int. 51, 1882–1889 (2011).10.2355/isijinternational.51.1882 ↗
15. Zafra, A., Harris, Z., Sun, C. & Martínez-Pañeda, E. Comparison of hydrogen diffusivities measured by electrochemical permeation and temperature-programmed desorption in cold-rolled pure iron. J. Nat. Gas. Sci. Eng. 98, 104365 (2022).10.1016/j.jngse.2021.104365 ↗
16. Zafra, A., Harris, Z., Korec, E. & Martínez-Pañeda, E. On the relative efficacy of electropermeation and isothermal desorption approaches for measuring hydrogen diffusivity. Int. J. Hydrog. Energy 48, 1218–1233 (2023).10.1016/j.ijhydene.2022.10.025 ↗
17. Enomoto, M., Hirakami, D. & Tarui, T. Modeling thermal desorption analysis of hydrogen in steel. ISIJ Int. 46, 1381–1387 (2006).10.2355/isijinternational.46.1381 ↗
18. Turnbull, A. Hydrogen diffusion and trapping in metals. in Gaseous hydrogen embrittlement of materials in energy technologies, 89–128 (Elsevier, 2012).10.1533/9780857095374.1.89 ↗
19. Boellinghaus, T., Hoffmeister, H. & Dangeleit, A. A scatterband for hydrogen diffusion coefficients in microalloyed and low carbon structural steels. Weld. World/le. Soudage dans le. Monde 2, 149 (1995).
20. Kiuchi, K. & McLellan, R. The solubility and diffusivity of hydrogen in well-annealed and deformed iron. in Perspectives in hydrogen in metals, 29–52 (Elsevier, 1986).10.1016/B978-0-08-034813-1.50009-7 ↗
21. Jeklih, A. I. D. V. V. Absorption and diffusion of hydrogen in steels. Mater. Tehnol. 34, 331 (2000).
22. Bergmann, C. et al. Hydrogen embrittlement resistance evaluation of advanced high strength steel for automotive applications. In Proc. Steely Hydrogen, Ghent, Belgium 29–31 (OCAS NV, 2018).
23. Prosek, T., Nazarov, A., Bexell, U., Thierry, D. & Serak, J. Corrosion mechanism of model zinc–magnesium alloys in atmospheric conditions. Corros. Sci. 50, 2216–2231 (2008).10.1016/j.corsci.2008.06.008 ↗
24. Volovitch, P., Allely, C. & Ogle, K. Understanding corrosion via corrosion product characterization: I. case study of the role of Mg alloying in Zn–Mg coating on steel. Corros. Sci. 51, 1251–1262 (2009).10.1016/j.corsci.2009.03.005 ↗
25. Hosking, N., Ström, M., Shipway, P. & Rudd, C. Corrosion resistance of zinc–magnesium coated steel. Corros. Sci. 49, 3669–3695 (2007).10.1016/j.corsci.2007.03.032 ↗
26. Diler, E. et al. Characterization of corrosion products of Zn and Zn–Mg–al coated steel in a marine atmosphere. Corros. Sci. 87, 111–117 (2014).10.1016/j.corsci.2014.06.017 ↗
27. Zhao, D. et al. Recent progress of ion-modified Tio2 for enhanced photocatalytic hydrogen production. Molecules 29, 2347 (2024).10.3390/molecules29102347 ↗
28. Bavykin, D. V., Friedrich, J. M. & Walsh, F. C. Protonated titanates and Tio2 nanostructured materials: synthesis, properties, and applications. Adv. Mater. 18, 2807–2824 (2006).10.1002/adma.200502696 ↗
29. Yoon, Y.-G. & Pyun, S.-I. Hydrogen transport through plasma enhanced chemical vapour-deposited Tio2 film-palladium bilayer by ac-impedance spectroscopy. Electrochim. Acta 40, 999–1004 (1995).10.1016/0013-4686(94)00366-9 ↗
30. Boiadjieva-Scherzer, T., Kronberger, H., Fafilek, G. & Monev, M. Hydrogen evolution reaction on electrodeposited Zn-Cr alloy coatings. J. Electroanal. Chem. 783, 68–75 (2016).10.1016/j.jelechem.2016.10.059 ↗
31. Kim, S. J., Park, J. S. & Jung, S.-P. Corrosion-induced hydrogen evolution, absorption, and cracking behaviors of ultra-high-strength galvanized and galvannealed steel sheets. npj Mater. Degrad. 6, 31 (2022).10.1038/s41529-022-00245-1 ↗
32. Kitahara, G. et al. Assessment of hydrogen absorption into steel during sacrificial dissolution of zinc and zinc coatings in various pH solutions. Mater. Trans. 60, 306–315 (2019).10.2320/matertrans.M2018343 ↗
33. Kawanami, H., Takahashi, T. & Omura, T. Effect of halide ions on hydrogen entry efficiency into steel sheet. Corros. Sci. Technol. 23, 410–415 (2024).
34. Li, Y., Pan, X. & Horri, B. A. The role of monovalent cations in activating cathodic reactions for enhanced hydrogen evolution using Mn/MnSo4 redox pair. Electrochim. Acta 536, 146719 (2025).10.1016/j.electacta.2025.146719 ↗
35. Yao, C., Tay, S. L., Zhu, T., Shang, H. & Gao, W. Effects of mg content on microstructure and electrochemical properties of zn–al–mg alloys. J. Alloy. Compd. 645, 131–136 (2015).10.1016/j.jallcom.2015.05.010 ↗
36. Manolatos, P. & Jerome, M. A thin palladium coating on iron for hydrogen permeation studies. Electrochim. Acta 41, 359–365 (1996).10.1016/0013-4686(95)00379-7 ↗
37. Ott, T. S. et al. Hydrogen generation during repassivation on ultra-high-strength steel. npj Mater. Degrad. https://doi.org/10.1038/s41529-026-00790-z (2026).10.1038/s41529-026-00790-z ↗
38. DIN Deutsches Institut für Normung e.V. DIN EN ISO 17081: Elektrochemisches Verfahren zur Messung der Wasserstoffpermeation und zur Bestimmung von Wasserstoffaufnahme und -transport in Metallen (ISO 17081:2014) (Beuth Verlag, 2014).
39. Zakroczymski, T. Electrochemical determination of hydrogen in metals. J. Electroanal. Chem. 475, 82–88 (1999).10.1016/S0022-0728(99)00355-1 ↗
40. Zakroczymski, T. Adaptation of the electrochemical permeation technique for studying entry, transport and trapping of hydrogen in metals. Electrochim. Acta 51, 2261–2266 (2006).10.1016/j.electacta.2005.02.151 ↗
41. Crank, J. The mathematics of diffusion (Oxford University Press, 1979).
42. Luu, W. & Wu, J. The influence of microstructure on hydrogen transport in carbon steels. Corros. Sci. 38, 239–245 (1996).10.1016/0010-938X(96)00109-6 ↗