Blackening of copper pigments in wall paintings: impact of the fresco technique and the chemical composition of the pigments
Source abstract
Abstract
This study addresses the blackening of copper-based pigments in fresco paintings. Historical evidence shows that copper carbonates, silicates and acetates were widely used despite often blackening, usually due to copper oxide formation in humid, highly alkaline conditions. To clarify the causes, eight fresco-applied copper pigments were studied after blackening. Physical, mineralogical and chemical analysis suggested that moisture, high alkalinity and carbonation promoted oxide formation. However, crystalline oxides alone did not explain the observed blackening. Instead, XPS analysis indicated poorly crystalline or amorphous reduced copper species as additional contributors. Pigment composition was found to be critical: carbonate- and acetate-based pigments showed instability, whereas silicate ones remained comparatively stable. Pigment origin and impurities further influenced alteration pathways, with copper-acetate verdigris exhibiting the most complex behaviour. These results highlight the multifactorial nature of copper pigment degradation and underline the importance of pigment identification for conservation strategies in fresco paintings.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Cultural Heritage Materials Analysis · Building materials and conservation · Conservation Techniques and Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (61)
Show source-provided references
1. Jiménez-Desmond, D., Pozo-Antonio, J. S. & Arizzi, A. The fresco wall painting techniques in the Mediterranean area from Antiquity to the present: a review. J. Cult. Herit. 66, 166–186 (2024).10.1016/j.culher.2023.11.018 ↗
2. Švarcová S., Hradil D., Hradilová J. & Čermáková Z. Pigments—copper-based greens and blues. Archaeol. Anthropol. Sci. 13, https://doi.org/10.1007/s12520-021-01406-0 (2021).10.1007/s12520-021-01406-0 ↗
3. Fiedler, I. & Bayard, M. Emerald green and Scheele’s green. in A Handbook of their History and Characteristics Vol. 3 (ed FitzHugh, E. W.) 219–272 (Archetype Publications, 1997).
4. Gettens, R. J. & FitzHugh, E. W. Azurite and blue verditer. in Artists Pigments. A Handbook Of Their History And Characteristics Vol. 2 (ed Roy, A.) 23–36 (Archetype Publications, 1993).
5. Gettens, R. J. & FitzHugh, E. W. Malachite and green verditer. in Artists pigments. A Handbook of Their History and characteristics Vol. 2 (ed Roy, A.) 183–202 (Archetype Publications, 1993).
6. Riederer, J. Egyptian blue. in Artists Pigments. A Handbook of Their History and Characteristics Vol. 3, (ed West Fitzhugh, E.) 23–46 (Archetype Publications, 1997).
7. Scott, D. A review of ancient Egyptian pigments and cosmetics. Stud. Conserv. 61, 185–202 (2016).10.1179/2047058414Y.0000000162 ↗
8. Mugnaini, S. et al. Thirteenth century wall paintings under the Siena Cathedral (Italy). Mineralogical and petrographic study of materials, painting techniques and state of conservation. J. Cult. Herit. 7, 171–185 (2006).10.1016/j.culher.2006.04.002 ↗
9. Abd Elrehim, S. A., Awad, M. A. A. & Sleem, H. R. A. Analytical studies of plaster painting and state of conservation in Red Monastery-The Church of Saints Bishai and Bigol, Sohag, Egypt. Int. J. Basic Appl. Sci. 4, 160–168 (2015).
10. Jorge-Villar, S. E. & Edwards, H. G. M. Green and blue pigments in Roman wall paintings: a challenge for Raman spectroscopy. J. Raman Spectrosc. 52, 2190–2203 (2021).10.1002/jrs.6118 ↗
11. Kühn, H. Verdigris and copper resinate. in Artists Pigments. A Handbook of Their History and Characteristics vol. 2 (ed Roy, A.) p. 131–156 (Archetype Publications, 1993).
12. Scott, D., Taniguchi, Y. & Koseto, E. The verisimilitude of verdigris: a review of the copper carboxylates. Stud. Conserv. 46, 73–91 (2001).10.1179/sic.2001.46.Supplement-1.73 ↗
13. Mora, L., Mora, P. & Philippot, P. La Conservazione Delle Pitture Murali (Editrice Compositori, 1999).
14. Piovesan, R., Mazzoli, C., Maritan, L. & Cornale, P. Fresco and lime-paint: an experimental study and objective criteria for distinguishing between these painting techniques. Archaeometry 54, 723–736 (2012).10.1111/j.1475-4754.2011.00647.x ↗
15. Botticelli, G. Metodologia di restauro delle pitture murali. Firenze: Centro Di (1992).
16. Murat, Z. Wall paintings through the ages: the medieval period (Italy, twelfth to fifteenth century). Archaeol. Anthropol. Sci. 13. https://doi.org/10.1007/s12520-021-01410-4 (2021).10.1007/s12520-021-01410-4 ↗
17. Švarcová, S., Hradil, D., Hradilová, J., Kočí, E. & Bezdička, P. Micro-analytical evidence of origin and degradation of copper pigments found in Bohemian Gothic murals. Anal. Bioanal. Chem. 395, 2037–2050 (2009).10.1007/s00216-009-3144-7 ↗
18. Lluveras, A., Boularand, S., Andreotti, A. & Vendrell-Saz, M. Degradation of azurite in mural paintings: distribution of copper carbonate, chlorides and oxalates by SRFTIR. Appl. Phys. A 99, 363–375 (2010).10.1007/s00339-010-5673-5 ↗
19. Avranovich Clerici, E. et al. Multi-scale X-ray imaging of the pigment discoloration processes triggered by chlorine compounds in the upper basilica of Saint Francis of Assisi. Molecules 28, 6106 (2023).10.3390/molecules28166106 ↗
20. Bidaud, E., Halwax, E., Pantos, E. & Sipek, B. Analyses of a green copper pigment used in a thirteenth-century wall painting. Stud. Conserv. 53, 81–92 (2008).10.1179/sic.2008.53.2.81 ↗
21. Liberti, S. Sulla alterazione dei dipinti murali. Boll. Dell Istituto Cent. Del. Restauro 3–4, 31–44 (1950).
22. Gutscher, D., Mühlethaler, B., Portmann, A. & Reller, A. Conversion of azurite into tenorite. Stud. Conserv. 34, 117–122 (1989).10.1179/sic.1989.34.3.117 ↗
23. Mattei, E. et al. Raman spectroscopic analysis of azurite blackening. J. Raman Spectrosc. 39, 302–306 https://doi.org/10.1002/jrs.1845 (2008).10.1002/jrs.1845 ↗
24. Kotulanová, E. et al. Wall painting damage by salts: causes and mechanisms. Acta Res. Rep. 18, 27–31 (2009).
25. Coccato, A., Moens, L. & Vandenabeele, P. On the stability of mediaeval inorganic pigments: a literature review of the effect of climate, material selection, biological activity, analysis and conservation treatments. Herit. Sci. 5. https://doi.org/10.1186/s40494-017-0125-6 (2017).10.1186/s40494-017-0125-6 ↗
26. Asraf Ali, A. & Rajdeo Singh, M. From blue to green: a review of the use and alteration of azurite pigment in cultural heritage. Arts Commun. 0, 025220048 (2025).10.36922/AC025220048 ↗
27. Špec, T., Retko, K., Ropret, P., Meden, A. & Bernard, J. The influence of UV-Vis radiation, and oscillations of temperature and relative humidity, on malachite alteration in the presence of different organic binders and varnishes. J. Raman Spectrosc. 45, 1068–1075 (2014).10.1002/jrs.4518 ↗
28. Frost, R. L., Ding, Z., Kloprogge, J. T. & Martens, W. N. Thermal stability of azurite and malachite in relation to the formation of mediaeval glass and glazes. Thermochim. Acta 390, 133–144 (2002).10.1016/S0040-6031(02)00127-2 ↗
29. Chappé, M., Hildenhagen, J., Dickmann, K. & Bredol, M. Laser irradiation of medieval pigments at IR, VIS and UV wavelengths. J. Cult. Herit. 4, 264–270 (2003).10.1016/S1296-2074(02)01206-2 ↗
30. Andrés-Herguedas, L. et al. Influence of pulse duration on the effects induced by three Nd:YAG lasers operating at 1064 nm to tempera paintings mock-ups. J. Cult. Herit. 76, 373–386 (2025).10.1016/j.culher.2025.10.023 ↗
31. Malagodi, M. et al. Alteration processes of pigments exposed to acetic and formic acid vapours. In Proc. IEEE International Conference on Environment and Electrical Engineering and 2017 1st IEEE Industrial and Commercial Power Systems Europe (EEEIC/I&CPS), 1–6 (IEEE, 2017).10.1109/EEEIC.2017.7977770 ↗
32. Smith, G. D. & Clark, R. J. H. The role of H2S in pigment blackening. J. Cult. Herit. 3, 101–105 (2002).10.1016/S1296-2074(02)01173-1 ↗
33. Jiménez-Desmond, D., Pozo-Antonio, J. S. & Arizzi, A. The dark fate of copper-based pigments in fresco painting: preliminary results. In Proc. 7th Historic Mortars Conference (HMC 2025) (eds Bonetto, J., Dilaria, S. & Previato, C.) 417–418 (Edizioni Quasar di S. Tognon S.r.l., 2025).
34. Jiménez-Desmond, D., Pozo-Antonio, J. S., Arizzi, A. & López-Martínez, T. Physico-chemical compatibility of an aqueous colloidal dispersion of silica nano-particles as binder for chromatic reintegration in wall paintings. Appl. Sci. 15, 3690 (2025).10.3390/app15073690 ↗
35. Carrasco, E., Oujja, M., Sanz, M., Marco, J. F. & Castillejo, M. X-ray and ion irradiation effects on azurite, malachite and alizarin pictorial models. Microchem. J. 137, 381–391 (2018).10.1016/j.microc.2017.11.014 ↗
36. Rodriguez-Navarro, C., Elert, K. & Ševčík, R. Amorphous and crystalline calcium carbonate phases during carbonation of nanolimes: implications in heritage conservation. CrystEngComm 18, 6594–6607 (2016).10.1039/C6CE01202G ↗
37. Ethiraj, A. S. & Kang, D. J. Synthesis and characterization of CuO nanowires by a simple wet chemical method. Nanoscale Res. Lett. 7, 1–5 (2012).10.1186/1556-276X-7-70 ↗
38. Ma, M., Djanashvili, K. & Smith, W. A. Controllable hydrocarbon formation from the electrochemical reduction of CO2 over Cu nanowire arrays. Angew. Chem. Int. Ed. 55, 6680–6684 (2016).10.1002/anie.201601282 ↗
39. Fernández-Carrasco, L., Torrens-Martín, D., Morales, L. M. & Martínez-Ramírez, S. Infrared spectroscopy in the analysis of building and construction materials. in Infrared Spectroscopy: Materials Science, Engineering and Technology (ed Theophanides, T.) 369–381 (InTech, 2012).10.5772/36186 ↗
40. Derrick, M. R., Stulik, D. & Landry, J. M. Scientific tools for conservation. In Infrared Spectroscopy in Conservation Science (The Getty Conservation Institute, 1999).
41. Socrates, G. Infrared and Raman Characteristic Group Frequencies: Tables and Charts. 3rd ed (John Wiley & Sons LTD,2004).
42. Labate, M. et al. Multi-analytical and non-invasive approach for characterising blackened areas of originally blue paints. Molecules 29. https://doi.org/10.3390/molecules29246043 (2029).10.3390/molecules29246043 ↗
43. Cudennec, Y. & Lecerf, A. The transformation of Cu(OH)2 into CuO, revisited. Solid State Sci. 5, 1471–1474 (2003).10.1016/j.solidstatesciences.2003.09.009 ↗
44. Illas, F., Rubio, J., Centellas, F. & Virgili, J. Molecular structure of copper(I) hydroxide and copper hydroxide(1-) (Cu(OH)2-). An ab initio study. J. Phys. Chem. 88, 5225–5228 (2002).10.1021/j150666a022 ↗
45. Mambwe, P., Shengo, M., Kidyanyama, T., Muchez, P. & Chabu, M. Geometallurgy of cobalt black ores in the Katanga copperbelt (Ruashi Cu-Co deposit): a new proposal for enhancing cobalt recovery. Minerals 12, 295 (2022). 2022;12:295.10.3390/min12030295 ↗
46. Ye, M. & Shen, A. H. Gemmological and mineralogical characteristics of Chrysocolla chalcedony from Taiwan, Indonesia and the USA, and their separation. J. Gemmol. 37, 262–280 (2020).10.15506/JoG.2020.37.3.262 ↗
47. Berke, H. The invention of blue and purple pigments in ancient times. Chem. Soc. Rev. 36, 15–30 (2007).10.1039/B606268G ↗
48. Salvadó, N., Butí, S., Cotte, M., Cinque, G. & Pradell, T. Shades of green in 15th century paintings: combined microanalysis of the materials using synchrotron radiation XRD, FTIR and XRF. Appl Phys. A Mater. Sci. Process 111, 47–57 (2013).10.1007/s00339-012-7483-4 ↗
49. Musumeci, A. W., Frost, R. L. & Waclawik, E. R. A spectroscopic study of the mineral paceite (calcium acetate). Spectrochim. Acta A Mol. Biomol. Spectrosc. 67, 649–661 (2007).10.1016/j.saa.2006.07.045 ↗
50. Preis, W. & Gamsjäger, H. Solid–solute phase equilibria in aqueous solution. XVI. Thermodynamic properties of malachite and azurite—predominance diagrams for the system Cu 2 + – H2 O– CO 2. J. Chem. Thermodyn. 34, 631–650 (2002).10.1006/jcht.2002.0928 ↗
51. Kumashiro, R., Kuroda, Y. & Nagao, M. New analysis of oxidation state and coordination environment of copper ion-exchanged in ZSM-5 zeolite. J. Phys. Chem. B 103, 89–96 (1999).10.1021/jp981935t ↗
52. Murakami, R., Niiyama, S. & Kitada, M. Characterization of the black surface layer on a copper alloy coloured by traditional Japanese surface treatment. Stud. Conserv. 33, 133–136 (1988).10.1179/SIC.1988.33.S1.031 ↗
53. Scott D. A. Copper and bronze in art. in Corrosion, Colorants, Conservation (Getty Publications, 2002).
54. Scott, D. A. Copper compounds in metals and colorants: oxides and hydroxides. Stud. Conserv. 42, 93–100 (1997).10.1179/sic.1997.42.2.93 ↗
55. Zivković, A. et al. Structural and electronic properties of Cu4O3 (paramelaconite): The role of native impurities. Pure Appl. Chem. 93, 1229–1244 (2021).10.1515/pac-2021-0114 ↗
56. Zhao, L. et al. Facile solvothermal synthesis of phase-pure Cu4O3 microspheres and their lithium storage properties. Chem. Mater. 24, 1136–1142 (2012).10.1021/cm203589h ↗
57. Salthammer, T. Carbon monoxide as an indicator of indoor air quality. Environ. Sci. Atmos 4, 291–305 (2024).10.1039/D4EA00006D ↗
58. Abu Tahari, M. N. et al. Influence of hydrogen and carbon monoxide on reduction behavior of iron oxide at high temperature: Effect on reduction gas concentrations. Int J. Hydrog. Energy 46, 24791–24805 (2021).10.1016/j.ijhydene.2020.06.250 ↗
59. American Lung Association. (Indoor Air Pollution: An Introduction for Health Professionals) (Diane Books Publishing Company, 1996).
60. Wolff, G. T. Characteristics and consequences of soot in the atmosphere. Environ. Int. 11, 259–69 (1985).10.1016/0160-4120(85)90018-2 ↗
61. Barr, T. L. & Seal, S. Nature of the use of adventitious carbon as a binding energy standard. J. Vac. Sci. Technol. 13, 1239–1246 (1995).10.1116/1.579868 ↗