Microstructures, Mechanical and High-Temperature Tribological Properties of Dual-Phase Fe50Mn30Co10Cr10 High-Entropy Alloy Fabricated by Laser Metal Deposition
Source abstract
Abstract
The dual-phase Fe50Mn30Co10Cr10 (atomic percent, at.%) high-entropy alloy (HEA) was fabricated successfully through a laser metal deposition process. Fe50Mn30Co10Cr10 HEA consisted of face-centered cubic (FCC) γ and hexagonal close-packed (HCP) ε phases, with an alternating distribution of equiaxed and columnar grains. The microhardness, tensile strength and elongation of the alloy were 270 ± 20 HV, 689 MPa and 38%, respectively. After tensile deformation, many HCP ε phases were generated inside and at the boundaries of FCC γ grains because of the transformation-induced plasticity effect. The content of the HCP ε phase increased because of tensile deformation, resulting in a 75% decrease in the average grain size of the samples. Under the effect of dispersion strengthening, the strength, microhardness and plasticity of the material were greatly enhanced, with the product of strength and elongation up to 26.2 GPa%. The average friction coefficient and wear rate of the alloy were 0.43 and 1.88 × 10−5 mm3/N/m at 400°C, respectively, which were 38.6% and 81.6% lower than those at room temperature, showing great high-temperature wear resistance. The main wear mechanism of the alloy at 400°C was oxidative wear, accompanied by abrasive wear and delamination.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Additive Manufacturing Materials and Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (66)
Show source-provided references
1. B. Cantor, I.T.H. Chang, P. Knight, and A.J.B. Vincent, Mater. Sci. Eng. A 375–377, 213 https://doi.org/10.1016/j.msea.2003.10.257 (2004).10.1016/j.msea.2003.10.257 ↗
2. J.-W. Yeh, S.-K. Chen, S.-J. Lin, J.-Y. Gan, T.-S. Chin, T.-T. Shun, C.-H. Tsau, and S.Y. Chang, Adv. Eng. Mater. 6, 299 https://doi.org/10.1002/adem.200300567 (2004).10.1002/adem.200300567 ↗
3. B. Gludovatz, A. Hohenwarter, D. Catoor, E.H. Chang, E.P. George, and R.O. Ritchie, Science 345, 1153 https://doi.org/10.1126/science.1254581 (2014).10.1126/science.1254581 ↗
4. Y. Zhang, T.T. Zuo, Z. Tang, M.C. Gao, K.A. Dahmen, P.K. Liaw, and Z.P. Lu, Prog. Mater. Sci. 61, 1 https://doi.org/10.1016/j.pmatsci.2013.10.001 (2014).10.1016/j.pmatsci.2013.10.001 ↗
5. D.B. Miracle, and O.N. Senkov, Acta Mater. 122, 448 https://doi.org/10.1016/j.actamat.2016.08.081 (2017).10.1016/j.actamat.2016.08.081 ↗
6. Q.F. He, Z.Y. Ding, Y.F. Ye, and Y. Yang, JOM 69, 2092 https://doi.org/10.1007/s11837-017-2452-1 (2017).10.1007/s11837-017-2452-1 ↗
7. F. Wang, Y. Zhang, G. Chen, and H.A. Davies, Int. J. Mod. Phys. B 23, 1254 https://doi.org/10.1142/S0217979209060774 (2009).10.1142/S0217979209060774 ↗
8. J.Y. He, W.H. Liu, H. Wang, Y. Wu, X.J. Liu, T.G. Nieh, and Z.P. Lu, Acta Mater. 62, 105 https://doi.org/10.1016/j.actamat.2013.09.037 (2014).10.1016/j.actamat.2013.09.037 ↗
9. K.M. Youssef, A.J. Zaddach, C. Niu, D.L. Irving, and C.C. Koch, Mater. Res. Lett. 3, 95 https://doi.org/10.1080/21663831.2014.985855 (2014).10.1080/21663831.2014.985855 ↗
10. S.G. Ma, S.F. Zhang, J.W. Qiao, Z.H. Wang, M.C. Gao, Z.M. Jiao, H.J. Yang, and Y. Zhang, Intermetallics 54, 104 https://doi.org/10.1016/j.intermet.2014.05.018 (2014).10.1016/j.intermet.2014.05.018 ↗
11. F. Otto, A. Dlouhy, C. Somsen, H. Bei, G. Eggler, and E.P. George, Acta Mater. 61, 5743 https://doi.org/10.1016/j.actamat.2013.06.018 (2013).10.1016/j.actamat.2013.06.018 ↗
12. M.H. Chuang, M.H. Tsai, W.R. Wang, S.J. Lin, and J.W. Yeh, Acta Mater. 59, 6308 https://doi.org/10.1016/j.actamat.2011.06.041 (2011).10.1016/j.actamat.2011.06.041 ↗
13. J. Joseph, N. Haghdadi, K. Shamlaye, P. Hodgson, M. Barnett, and D. Fabijanic, Wear 428–429, 32 https://doi.org/10.1016/j.wear.2019.03.002 (2019).10.1016/j.wear.2019.03.002 ↗
14. Y. Shi, B. Yang, X. Xie, J. Brechtl, K.A. Dahmend, and P.K. Liaw, Corros. Sci. 119, 33 https://doi.org/10.1016/j.corsci.2017.02.019 (2017).10.1016/j.corsci.2017.02.019 ↗
15. Y. Lu, Y. Dong, S. Guo, L. Jiang, H. Kang, T. Wang, B. Wen, Z. Wang, J. Jie, Z. Cao, H. Ruan, and T. Li, Sci. Rep. 4, 6200 https://doi.org/10.1038/srep06200 (2014).10.1038/srep06200 ↗
16. W. Huo, H. Zhou, F. Fang, X. Zhou, Z. Xie, and J. Jiang, J. Alloys Compd. 735, 897 https://doi.org/10.1016/j.jallcom.2017.11.075 (2018).10.1016/j.jallcom.2017.11.075 ↗
17. Q. Wu, Z. Wang, T. Zheng, D. Chen, Z. Yang, J. Li, J.J. Kai, and J. Wang, Mater. Lett. 253, 268 https://doi.org/10.1016/j.matlet.2019.06.067 (2019).10.1016/j.matlet.2019.06.067 ↗
18. H. Jiang, D. Qiao, Y. Lu, Z. Ren, Z. Cao, T. Wang, and T. Li, Scripta Mater. 165, 145 https://doi.org/10.1016/j.scriptamat.2019.02.035 (2019).10.1016/j.scriptamat.2019.02.035 ↗
19. Z. Li, K.G. Pradeep, Y. Deng, D. Raabe, and C.C. Tasan, Nature 534, 227 https://doi.org/10.1038/nature17981 (2016).10.1038/nature17981 ↗
20. S. Basu, Z. Li, K.G. Pradeep, and D. Raabe, Front. Mater. 5, 30 https://doi.org/10.3389/fmats.2018.00030 (2018).10.3389/fmats.2018.00030 ↗
21. I.S. Wani, T. Bhattacharjee, S. Sheikh, Y.P. Lu, S. Chatterjee, P.P. Bhattacharjee, S. Guo, and N. Tsuji, Mater. Res. Lett. 4, 174 https://doi.org/10.1080/21663831.2016.1160451 (2016).10.1080/21663831.2016.1160451 ↗
22. R. Li, Z. Ren, Y. Wu, Z. He, P.K. Liaw, J. Ren, and Y. Zhang, Mater. Sci. Eng. A 802, 140637 https://doi.org/10.1016/j.msea.2020.140637 (2021).10.1016/j.msea.2020.140637 ↗
23. Z. Qiu, C. Yao, K. Feng, Z. Li, and P.K. Chu, Int. J. Lightweight Mater. Manuf. 1, 33 https://doi.org/10.1016/j.ijlmm.2018.02.001 (2018).10.1016/j.ijlmm.2018.02.001 ↗
24. Z. Tong, X. Ren, J. Jiao, W. Zhou, Y. Ren, Y. Ye, E.A. Larson, and J. Gu, J. Alloys Compd. 785, 1144 https://doi.org/10.1016/j.jallcom.2019.01.213 (2019).10.1016/j.jallcom.2019.01.213 ↗
25. S. Xiang, H. Luan, J. Wu, K.F. Yao, J. Li, X. Liu, Y. Tian, W. Mao, H. Bai, G. Le, and Q. Li, J. Alloys Compd. 773, 387 https://doi.org/10.1016/j.jallcom.2018.09.235 (2019).10.1016/j.jallcom.2018.09.235 ↗
26. V.R. Molina, A. Weisheit, S. Gein, U. Hecht, and D. Vogiatzief, Front. Mater. 7, 275 https://doi.org/10.3389/fmats.2020.00275 (2020).10.3389/fmats.2020.00275 ↗
27. L. Huang, Y. Sun, A. Amar, C. Wu, X. Liu, G. Le, X. Wang, J. Wu, K. Li, C. Jiang, and J. Li, Vacuum 183, 109875 https://doi.org/10.1016/j.vacuum.2020.109875 (2021).10.1016/j.vacuum.2020.109875 ↗
28. P. Niu, R. Li, Z. Fan, T. Yuan, and Z. Zhang, Mater. Sci. Eng. A 814, 141264 https://doi.org/10.1016/j.msea.2021.141264 (2021).10.1016/j.msea.2021.141264 ↗
29. J.Y. Aguilar-Hurtado, A. Vargas-Uscategui, K. Paredes-Gil, R. Palma-Hillerns, M.J. Tobar, and J.M. Amado, Appl. Surf. Sci. 515, 146084 https://doi.org/10.1016/j.apsusc.2020.146084 (2020).10.1016/j.apsusc.2020.146084 ↗
30. X. Liu, L. Zhang, and Y. Xu, Appl. Phys. 123, 567 https://doi.org/10.1007/s00339-017-1151-7 (2017).10.1007/s00339-017-1151-7 ↗
31. Y. Han, H. Li, H. Feng, K. Li, Y. Tian, and Z. Jiang, J. Mater. Sci. Technol. 65, 210 https://doi.org/10.1016/j.jmst.2020.04.072 (2021).10.1016/j.jmst.2020.04.072 ↗
32. Y. Lv, X. Zhao, T. Shi, L. Bai, J. Chen, and X. Wang, J. Mater. Sci. 55, 2239 https://doi.org/10.1007/s10853-019-04064-9 (2020).10.1007/s10853-019-04064-9 ↗
33. Z. Li, C.C. Tasan, H. Springer, B. Gault, and D. Raabe, Sci. Rep. 7, 40704 https://doi.org/10.1038/srep40704 (2017).10.1038/srep40704 ↗
34. P. Zhang, S. Wang, Y. Lv, L. Chen, K. Liu, and D. Zhao, J. Mater. Sci. Technol. 15, 2145 https://doi.org/10.1016/j.jmrt.2021.09.018 (2021).10.1016/j.jmrt.2021.09.018 ↗
35. K. Kempen, L. Thijs, J. Van Humbeeck, and J.P. Kruth, Phys. Procedia 39, 439 https://doi.org/10.1016/j.phpro.2012.10.059 (2012).10.1016/j.phpro.2012.10.059 ↗
36. D. Manfredi, F. Calignano, M. Krishnan, R. Canali, E.P. Ambrosio, and E. Atzeni, Materials 6, 856 https://doi.org/10.3390/ma6030856 (2013).10.3390/ma6030856 ↗
37. T.B. Sercombe, and X. Li, Mater. Tech. 31, 77 https://doi.org/10.1179/1753555715Y.0000000078 (2016).10.1179/1753555715Y.0000000078 ↗
38. K.G. Prashanth, S. Scudino, H.J. Klauss, K.B. Surreddi, L. Lober, Z. Wang, A.K. Chaubey, U. Kuhn, and J. Eckert, Mater. Sci. Eng. A 590, 153 https://doi.org/10.1016/j.msea.2013.10.023 (2014).10.1016/j.msea.2013.10.023 ↗
39. X.J. Wang, L.C. Zhang, M.H. Fang, and T.B. Sercombe, Mater. Sci. Eng. A 597, 370 https://doi.org/10.1016/j.msea.2014.01.012 (2014).10.1016/j.msea.2014.01.012 ↗
40. Z. Zeng, N. Stanford, C.H.J. Davies, J.F. Nie, and N. Birbilis, Int. Mater. Rev. 64, 27 https://doi.org/10.1080/09506608.2017.1421439 (2018).10.1080/09506608.2017.1421439 ↗
41. T. Nakata, T. Mezaki, R. Ajima, C. Xu, K. Oh-ishi, K. Shimizu, S. Hanaki, T.T. Sasaki, K. Hono, and S. Kamado, Scripta Mater. 101, 28 https://doi.org/10.1016/j.scriptamat.2015.01.010 (2015).10.1016/j.scriptamat.2015.01.010 ↗
42. J. Guo, Y. Zhou, C. Liu, Q. Wu, X. Chen, and J. Lu, Materials 9, 823 https://doi.org/10.3390/ma9100823 (2016).10.3390/ma9100823 ↗
43. G. Chahine, M. Koike, T. Okabe, P. Smith, and R. Kovacevic, JOM 60, 50 https://doi.org/10.1007/s11837-008-0148-2 (2008).10.1007/s11837-008-0148-2 ↗
44. B. Vrancken, L. Thijs, J.P. Kruth, and J.V. Humbeeck, J. Alloys Compd. 541, 177 https://doi.org/10.1016/j.jallcom.2012.07.022 (2012).10.1016/j.jallcom.2012.07.022 ↗
45. S.S. Al-Bermani, M.L. Blackmore, W. Zhang, and I. Todd, Metall. Mater. Trans. A 41, 3422 https://doi.org/10.1007/s11661-010-0397-x (2010).10.1007/s11661-010-0397-x ↗
46. T. Scharowsky, V. Juechter, R.F. Singer, and C. Korner, Adv. Eng. Mater. 17, 1573 https://doi.org/10.1002/adem.201400542 (2015).10.1002/adem.201400542 ↗
47. L.C. Zhang, D. Klemm, J. Eckert, Y.L. Hao, and T.B. Sercombe, Scripta Mater. 65, 21 https://doi.org/10.1016/j.scriptamat.2011.03.024 (2011).10.1016/j.scriptamat.2011.03.024 ↗
48. Y. Zhang, J. Li, X. Wang, Y. Lu, Y. Zhou, and X. Sun, J. Mater. Sci. Tech. 35, 902 https://doi.org/10.1016/j.jmst.2018.09.067 (2019).10.1016/j.jmst.2018.09.067 ↗
49. S. Luo, C. Zhao, Y. Su, Q. Liu, and Z. Wang, Addit. Manuf. 31, 100925 https://doi.org/10.1016/j.addma.2019.100925 (2020).10.1016/j.addma.2019.100925 ↗
50. R. Li, P. Niu, T. Yuan, P. Cao, C. Chen, and K. Zhou, J. Alloys Compd. 746, 125 https://doi.org/10.1016/j.jallcom.2018.02.298 (2018).10.1016/j.jallcom.2018.02.298 ↗
51. Y. Chew, G.J. Bi, Z.G. Zhu, F.L. Ng, F. Weng, S.B. Liu, S.M.L. Nai, and B.Y. Lee, Mater. Sci. Eng. A 744, 137 https://doi.org/10.1016/j.msea.2018.12.005 (2019).10.1016/j.msea.2018.12.005 ↗
52. T. Dursun, and C. Soutis, Mater. Des. 56, 862 https://doi.org/10.1016/j.matdes.2013.12.002 (2014).10.1016/j.matdes.2013.12.002 ↗
53. M.K. Kulekci, Int. J. Adv. Manuf. Technol. 38, 851 https://doi.org/10.1007/s00170-007-1279-2 (2008).10.1007/s00170-007-1279-2 ↗
54. L.C. Zhang, and L.Y. Chen, Adv. Eng. Mater. 21, 1801215 https://doi.org/10.1002/adem.201801215 (2019).10.1002/adem.201801215 ↗
55. Z. Li, C.C. Tasan, K.G. Pradeep, and D. Raabe, Acta Mater. 131, 323 https://doi.org/10.1016/j.actamat.2017.03.069 (2017).10.1016/j.actamat.2017.03.069 ↗
56. J. Su, D. Raabe, and Z. Li, Acta Mater. 163, 40–54 https://doi.org/10.1016/j.actamat.2018.10.017 (2019).10.1016/j.actamat.2018.10.017 ↗
57. J.A. Spittle, Int. Mater. Rev. 51, 247 https://doi.org/10.1179/174328006X102493 (2006).10.1179/174328006X102493 ↗
58. M.M. Kirka, P. Nandwana, Y. Lee, and R.R. Dehoff, Scripta Mater. 135, 130 https://doi.org/10.1016/j.scriptamat.2017.01.005 (2017).10.1016/j.scriptamat.2017.01.005 ↗
59. S. Bontha, N.W. Klingbeil, P.A. Kobryn, and H.L. Fraser, J. Mater. Process. Technol. 178, 135 https://doi.org/10.1016/j.jmatprotec.2006.03.155 (2006).10.1016/j.jmatprotec.2006.03.155 ↗
60. S. Allain, J.P. Chateau, O. Bouaziz, S. Migot, and N. Guelton, Mater. Sci. Eng. A 387–389, 158 https://doi.org/10.1016/j.msea.2004.01.059 (2004).10.1016/j.msea.2004.01.059 ↗
61. J.R.C. Guimaraes, and P.R. Rios, J. Mater. Sci. 45, 1074 https://doi.org/10.1007/s10853-009-4044-0 (2010).10.1007/s10853-009-4044-0 ↗
62. X. Zhao, Z. Xue, W. Chen, Y. Wang, and T. Mu, Chemsuschem 13, 2038 https://doi.org/10.1002/cssc.202000173 (2020).10.1002/cssc.202000173 ↗
63. Y.Q. Gao, X.Y. Liu, and G.W. Yang, Nanoscale 8, 5015 https://doi.org/10.1039/c5nr08989a (2016).10.1039/c5nr08989a ↗
64. S. Ma, L. Sun, L. Cong, X. Gao, C. Yao, X. Guo, L. Tai, P. Mei, Y. Zeng, H. Xie, and R. Wang, J. Phys. Chem. C 117, 25890 https://doi.org/10.1021/jp407576q (2013).10.1021/jp407576q ↗
65. Q. Jiang, R. Lu, J. Gu, L. Zhang, K. Liu, M. Huang, P. Liu, S. Zuo, Y. Wang, Y. Zhao, P. Ma, and Z. Fu, Chem. Eng. J. 453, 139510 https://doi.org/10.1016/j.cej.2022.139510 (2023).10.1016/j.cej.2022.139510 ↗
66. Y. Yang, L. Dang, M.J. Shearer, H. Sheng, W. Li, J. Chen, P. Xiao, Y. Zhang, R.J. Hamers, and S. Jin, Adv. Energy Mater. 8, 1703189 https://doi.org/10.1002/aenm.201703189 (2018).10.1002/aenm.201703189 ↗