Three-dimensional polycaprolactone-bioactive glass composite scaffolds: Effect of particle size and volume fraction on mechanical properties and in vitro cellular behavior
Source abstract
Abstract
In this study, highly porous polycaprolactone-based composites (90% porosity) with hierarchical pore structure (400–500 µm) and nanotopographical features were prepared by 3D printing. 45S5 Bioglass particles with different sizes (<100 nm; 250 nm; 6 µm) and concentrations (2, 6, and 10 vol%) were utilized to attain improved mechanical strength and bioactivity. The micrometric particles embedded in the polymer matrix enhanced the elastic modules up to 235%. The ultrafine particles decorated the struts and affected nanotopography, hydrophilicity, and nanohardness by about 100%. The rate of pore filing lowers in the presence of nanoparticles as compared with microparticles.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · Additive Manufacturing and 3D Printing Technologies · 3D Printing in Biomedical Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Nanobiotechnology, Faculty of Biological Sciences, Tarbiat Modares University, Tehran, Iran
Funding
Deputy Office for Research and Technology
References (67)
Show source-provided references
1. 10.1016/S1369-7021(11)70058-X10.1016/S1369-7021(11)70058-X ↗
2. 10.1016/j.biomaterials.2006.01.03910.1016/j.biomaterials.2006.01.039 ↗
3. 10.1586/17434440.4.3.40510.1586/17434440.4.3.405 ↗
4. 10.1021/acsbiomaterials.7b0002910.1021/acsbiomaterials.7b00029 ↗
5. 10.1016/j.progpolymsci.2007.05.01710.1016/j.progpolymsci.2007.05.017 ↗
6. 10.22203/eCM.v005a0110.22203/eCM.v005a01 ↗
7. 10.1016/j.biomaterials.2003.08.00410.1016/j.biomaterials.2003.08.004 ↗
8. 10.1016/j.compscitech.2006.05.01810.1016/j.compscitech.2006.05.018 ↗
9. 10.1016/j.msec.2007.01.00410.1016/j.msec.2007.01.004 ↗
10. 10.1016/j.actbio.2007.01.00510.1016/j.actbio.2007.01.005 ↗
11. 10.1016/j.biomaterials.2005.09.01910.1016/j.biomaterials.2005.09.019 ↗
12. 10.1016/j.progpolymsci.2010.04.00210.1016/j.progpolymsci.2010.04.002 ↗
13. 10.1016/j.biomaterials.2005.11.02510.1016/j.biomaterials.2005.11.025 ↗
14. 10.1016/j.actbio.2008.07.01610.1016/j.actbio.2008.07.016 ↗
15. 10.1021/acsbiomaterials.6b0047010.1021/acsbiomaterials.6b00470 ↗
16. 10.1002/jbm.b.3065210.1002/jbm.b.30652 ↗
17. 10.1016/j.compstruct.2010.01.01710.1016/j.compstruct.2010.01.017 ↗
18. 10.1002/jbm.b.3139210.1002/jbm.b.31392 ↗
19. 10.1016/j.matlet.2017.05.11210.1016/j.matlet.2017.05.112 ↗
20. 10.1016/j.msec.2015.05.01110.1016/j.msec.2015.05.011 ↗
21. 10.1021/acsbiomaterials.6b0012110.1021/acsbiomaterials.6b00121 ↗
22. 10.1016/j.molmed.2016.01.00310.1016/j.molmed.2016.01.003 ↗
23. 10.1097/00000658-199807000-0000210.1097/00000658-199807000-00002 ↗
24. 10.1016/j.biomaterials.2006.02.03910.1016/j.biomaterials.2006.02.039 ↗
25. 10.1016/S0142-9612(01)00232-010.1016/S0142-9612(01)00232-0 ↗
26. 10.1016/S0142-9612(02)00276-410.1016/S0142-9612(02)00276-4 ↗
27. 10.1016/S0142-9612(03)00030-910.1016/S0142-9612(03)00030-9 ↗
28. 10.1016/j.msec.2006.05.05010.1016/j.msec.2006.05.050 ↗
29. 10.1002/mabi.20040002610.1002/mabi.200400026 ↗
30. 10.1016/j.biomaterials.2004.10.04010.1016/j.biomaterials.2004.10.040 ↗
31. 10.1016/j.matdes.2015.08.13310.1016/j.matdes.2015.08.133 ↗
32. 10.1002/jbm.a.3458410.1002/jbm.a.34584 ↗
33. 10.1088/1758-5082/6/2/02500310.1088/1758-5082/6/2/025003 ↗
34. 10.1088/1758-5090/7/4/04500310.1088/1758-5090/7/4/045003 ↗
35. 10.1002/jbm.a.3572110.1002/jbm.a.35721 ↗
36. 10.1016/j.actbio.2015.08.03610.1016/j.actbio.2015.08.036 ↗
37. 10.1089/ten.tec.2011.062110.1089/ten.tec.2011.0621 ↗
38. 10.1186/s13036-015-0001-410.1186/s13036-015-0001-4 ↗
39. 10.1002/adhm.20150016810.1002/adhm.201500168 ↗
40. 10.1016/j.nano.2010.10.00510.1016/j.nano.2010.10.005 ↗
41. 10.1016/j.compscitech.2010.06.00210.1016/j.compscitech.2010.06.002 ↗
42. 10.1023/A:101992010520710.1023/A:1019920105207 ↗
43. 10.1016/S0142-9612(01)00345-310.1016/S0142-9612(01)00345-3 ↗
44. 10.1016/S0142-9612(03)00558-110.1016/S0142-9612(03)00558-1 ↗
45. 10.1016/j.biomaterials.2007.12.04010.1016/j.biomaterials.2007.12.040 ↗
46. Mohn D. · J. Eur. Cell. Mater. · 2008 · 16 · 8
47. 10.3390/ma307386710.3390/ma3073867 ↗
48. 10.1016/j.actbio.2011.03.01610.1016/j.actbio.2011.03.016 ↗
49. 10.1007/s10973-005-7165-y10.1007/s10973-005-7165-y ↗
50. 10.1007/s10973-005-7166-x10.1007/s10973-005-7166-x ↗
51. 10.1016/j.msec.2011.06.01310.1016/j.msec.2011.06.013 ↗
52. Soleymani Eil Bakhtiyari S. · Sci. Iran. F · 2015 · 22 · 1337
53. Maji K. · Int. J. Biomater. · 2016 · 1 · 9825659
54. 10.1615/CritRevBiomedEng.v40.i5.1010.1615/CritRevBiomedEng.v40.i5.10 ↗
55. 10.1016/j.actbio.2012.10.02010.1016/j.actbio.2012.10.020 ↗
56. 10.1002/jbm.102810.1002/jbm.1028 ↗
57. 10.1016/j.actbio.2016.01.04110.1016/j.actbio.2016.01.041 ↗
58. 10.1021/ja00082a01510.1021/ja00082a015 ↗
59. de Vries, D. V. W. M. Characterization of Polymeric Foams. MSc thesis, Eindhoven University of Technology, 2009.
60. Guarino V. · J. Appl. Biomater. Biomech. · 2007 · 5 · 149
61. 10.1021/bm101305210.1021/bm1013052 ↗
62. 10.1016/j.compscitech.2005.12.02810.1016/j.compscitech.2005.12.028 ↗
63. 10.1016/j.compositesb.2008.01.00210.1016/j.compositesb.2008.01.002 ↗
64. 10.1093/labmed/20.3.17210.1093/labmed/20.3.172 ↗
65. Chen Q. Z. · 2008 · 1
66. 10.1021/nl070678d10.1021/nl070678d ↗
67. 10.1016/j.actamat.2007.01.02910.1016/j.actamat.2007.01.029 ↗