Kaolin-based geopolymers with various NaOH concentrations
Source abstract
Abstract
Kaolin geopolymers were produced by the alkali-activation of kaolin with an activator solution (a mixture of NaOH and sodium silicate solutions). The NaOH solution was prepared at a concentration of 6–14 mol/L and was mixed with the sodium silicate solution at a Na2SiO3/NaOH mass ratio of 0.24 to prepare an activator solution. The kaolin-to-activator solution mass ratio used was 0.80. This paper aimed to analyze the effect of NaOH concentration on the compressive strength of kaolin geopolymers at 80°C for 1, 2, and 3 d. Kaolin geopolymers were stable in water, and strength results showed that the kaolin binder had adequate compressive strength with 12 mol/L of NaOH concentration. When the NaOH concentration increased, the SiO2/Na2O decreased. The increased Na2O content enhanced the dissolution of kaolin as shown in X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analyses. However, excess in this content was not beneficial for the strength development of kaolin geopolymers. In addition, there was the formation of more geopolymeric gel in 12 mol/L samples. The XRD pattern of the samples showed a higher amorphous content and a more geopolymer bonding existed as proved by FTIR analysis.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Concrete and Cement Materials Research · Grouting, Rheology, and Soil Mechanics · Innovative concrete reinforcement materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. J. Davidovits, 30 years of successes and failures in geopolymer applications. Market trends and potential breakthroughs, [in] Geopolymer 2002 Conference, Melbourne, 2002.
2. J. Davidovits, Mineral Polymers and Methods of Making Them, United States Patent, Appl. 182571, 1982.
3. P. Duxson, A. Fernández-Jiménez, J.L. Provis, G.C. Lukey, and J.S.J. van Deventer, Geopolymer technology: the current state of the art, J. Mater. Sci., 42(2007), p. 2917.10.1007/s10853-006-0637-z ↗
4. A. Palomo, M.W. Grutzeck, and M.T. Blanco, Alkaliactivated fly ashes: a cement for the future, Cem. Concr. Res., 29(1999), p. 1323.10.1016/S0008-8846(98)00243-9 ↗
5. S. Songpiriyakij, T. Kubprasit, C. Jaturapitakkul, and P. Chindaprasirt, Compressive strength and degree of reaction of biomass- and fly ash-based geopolymer, Constr. Build. Mater., 24(2007), p. 236.10.1016/j.conbuildmat.2009.09.002 ↗
6. J. Davidovits, Geopolymer Chemistry and Application, 2nd ed., Institute Geopolymere, Saint-Quentin, 2008.
7. H. Xu and J.S.J. van Deventer, Microstructural characterisation of geopolymers synthesised from kaolinite/stilbite mixtures using XRD, MAS-NMR, SEM/EDX, TEM/EDX, and HREM, Cem. Concr. Res., 32(2002), p. 1705.10.1016/S0008-8846(02)00859-1 ↗
8. K. Komnitsas and D. Zaharaki, Geopolymerisation: a re view and prospects for the minerals industry, Miner. Eng., 20(2007), p. 1261.10.1016/j.mineng.2007.07.011 ↗
9. H. Xu and J.S.J. van Deventer, Geopolymerisation of alumino-silicate minerals, Int. J. Miner. Process., 59(2000), p. 247.10.1016/S0301-7516(99)00074-5 ↗
10. C.Y. Heah, H. Kamarudin, A.M. Mustafa Al Bakri, M. Luqman, I. Khairul Nizar, and Y.M. Liew, Potential application of kaolin without calcine as greener concrete: a review, Aust. J. Basic Appl. Sci., 5(2011), p. 1026.
11. J.G.S. van Jaarsveld, J.S.J. van Deventer, and G.C. Lukey, The effect of composition and temperature on the properties of fly ash- and kaolinite-based geopolymers, Chem. Eng. J., 89(2002), p. 63.10.1016/S1385-8947(02)00025-6 ↗
12. X.L. Guo, H.S. Shi, and W.A. Dick, Compressive strength and microstructural characteristics of class C fly ash geopolymer, Cem. Concr. Compos., 32(2010), p. 142.10.1016/j.cemconcomp.2009.11.003 ↗
13. M.L. Granizo, M.T.B. Varela, and S. Martínez-Ramírez, Alkali activation of metakaolins: parameters affecting mechanical, structural and microstructural properties, J. Mater. Sci., 42(2007), p. 2934.10.1007/s10853-006-0565-y ↗
14. Z. Zuhua, Y. Xiao, Z. Huajun, and C. Yue, Role of water in the synthesis of calcined kaolin-based geopolymer, Appl. Clay Sci., 43(2009), p. 218.10.1016/j.clay.2008.09.003 ↗
15. D. Khale and R. Chaudhary, Mechanism of geopolymerization and factors influencing its development: a review, J. Mater. Sci., 42(2007), p. 729.10.1007/s10853-006-0401-4 ↗
16. E. Álvarez-Ayuso, X. Querol, F. Plana, A. Alastuey, N. Moreno, M. Izquierdo, O. Font, T. Moreno, S. Diez, E. Vázquez, and M. Barra., Environmental, physical and structural characterisation of geopolymer matrixes synthesised from coal (co-)combustion fly ashes, J. Hazard. Mater., 154(2008), p. 175.10.1016/j.jhazmat.2007.10.008 ↗
17. D. Hardjito, S.E. Wallah, D.M.J. Sumajouw, and B.V. Rangan, Fly ash-based geopolymer concrete, Aust. J. Struct. Eng., 6(2005), p. 1.10.1080/13287982.2005.11464940 ↗
18. H.L. Wang, H.H. Li, and F.Y. Yan, Synthesis and mechanical properties of metakaolinite-based geopolymer, Colloids Surf. A, 268(2005), p. 1.10.1016/j.colsurfa.2005.01.016 ↗
19. ASTM C109/C109-05, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2- in. or [50mm] Cube Specimens), ASTM International, 2008.
20. BS EN 12390-7:2000, Testing Hardened Concrete. Density of Hardened Concrete, British Standards, London, 2000.
21. J. Davidovits, Geopolymers: inorganic polymeric new materials, J. Therm. Anal., 37(1991), p. 1633.10.1007/BF01912193 ↗
22. Y.M. Liew, H. Kamarudin, A.M. Mustafa Al Bakri, M. Luqman, I. Khairul Nizar, C.M. Ruzaidi, and C.Y. Heah, Processing and characterization of calcined kaolin cement powder, Cons. Build. Mater., 30(2012), p. 794.10.1016/j.conbuildmat.2011.12.079 ↗
23. D.L.Y. Kong, J.G. Sanjayan, and K. Sagoe-Crentsil, Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures, Cem. Concr. Res., 37(2007), p. 1583.10.1016/j.cemconres.2007.08.021 ↗
24. W. Sun, Y.S. Zhang, W. Lin, and Z.Y. Lin, In situ monitoring of the hydration process of K-PS geopolymer cement with ESEM, Cem. Concr. Res., 34(2004), p. 935.10.1016/j.cemconres.2003.10.026 ↗
25. Y.S. Zhang, W. Sun, and Z.J. Li, Composition design and microstructural characterization of calcined kaolin-based geopolymer cement, Appl. Clay Sci., 47(2010), p. 271.10.1016/j.clay.2009.10.014 ↗
26. A.G.S. Cristóbal, R. Castelló, M.A.M. Luengo, and C. Vizcayno, Zeolites prepared from calcined and mechanically modified kaolins: a comparative study, Appl. Clay Sci., 49(2010), p. 239.10.1016/j.clay.2010.05.012 ↗
27. G. Varga, The structure of kaolinite and metakaolinite, Epitoanyag, 59(2007), p. 6.10.14382/epitoanyag-jsbcm.2007.2 ↗
28. C. Villa, E.T. Pecina, R. Torres, and L. Gómez, Geopolymer synthesis using alkaline activation of natural zeolite, Constr. Build. Mater., 24(2010), p. 2084.10.1016/j.conbuildmat.2010.04.052 ↗
29. I. Lecomte, M. Liégeois, A. Rulmont, R. Cloots, and F. Maseri, Synthesis and characterization of new inorganic polymeric composites based on kaolin or white clay and on ground-granulated blast furnace slag, J. Mater. Res., 18(2003), p. 2571.10.1557/JMR.2003.0360 ↗
30. Q. Mohsen and N.Y. Mostafa, Investigating the possiblity of utilizing low kaolinitic clays in production of geopolymer bricks, Ceram. Silik., 54(2010), p. 160.
31. M.M.J. Treacy and J.B. Higgins, Collection of Simulated XRD Powder Patterns for Zeolites, Elsevier, 2001.
32. S. Chandrasekhar and P.N. Pramada, Investigation on the synthesis of zeolite NaX from Kerala Kaolin, J. Porous Mater., 6(1999), p. 283.10.1023/A:1009632606671 ↗
33. L. Heller-Kallai and I. Lapides, Reactions of kaolinites and metakaolinites with NaOH-comparison of different samples (Part 1), Appl. Clay Sci., 35(2007), p. 99.10.1016/j.clay.2006.06.006 ↗
34. J.L. Provis, P. Duxson, G.C. Lukey, and J.S.J. van Deventer, Modeling the formation of geopolymers, [in] Department of Chemical and Biomolecular Engineering, The University of Melbourne, Victoria, 2006.
35. T.W. Cheng and J.P. Chiu, Fire-resistant geopolymer produced by granulated blast furnace slag, Miner. Eng., 16(2003), p. 205.10.1016/S0892-6875(03)00008-6 ↗
36. J.G.S. van Jaarsveld, The physical and chemical characterisation of fly ash based geopolymers, [in] Department of Chemical Engineering, The University of Melbourne, Victoria, 2000.
37. S. Alonso and A. Palomo, Calorimetric study of alkaline activation of calcium hydroxide-metakaolin solid mixtures, Cem. Concr. Res., 31(2001), p. 25.10.1016/S0008-8846(00)00435-X ↗