The cohesive zone model in a problem of delayed hydride cracking of zirconium alloys
Source abstract
Abstract
The crack tip model with the cohesive zone ahead of a finite crack tip has been presented. The estimation of the length of the cohesive zone and the crack tip opening displacement is based on the comparison of the local stress concentration, according to Westergaard's theory, with the cohesive stress. To calculate the cohesive stress, von Mises yield condition at the boundary of the cohesive zone is employed for plane strain and plane stress. The model of the stress distribution with the maximum stress within the cohesive zone is discussed. Local criterion of brittle fracture and modelling of the fracture process zone by cohesive zone were used to describe fracture initiation at the hydride platelet in the process zone ahead of the crack tip. It was shown that the theoretical K IH-estimation applied to the case of mixed plane condition within the process zone is qualitatively consistent with experimental data for unirradiated Zr-2.5Nb alloy. In the framework of the proposed model, the theoretical value of K H IC for a single hydride platelet at the crack tip has been also estimated.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Thermodynamic and Structural Properties of Metals and Alloys · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (15)
Show source-provided references
1. Anderson, T.L. (1995) Fracture Mechanics: Fundamentals and Applications, CRC Press, Boca Raton.
2. Eadie, R.L. and Ellyin, F. (1989). The Effect of Hydride Precipitation on the Stresses near the Crack Tip in a Delayed Hydride Crack in Zirconium-2.5% Niobium, Scripta Metall. 23, 585-592.10.1016/0036-9748(89)90456-0 ↗
3. Kim, Y.S., Matvienko, Yu.G., Cheong, Y.M., Kim, S.S. and Kwon, S.C. (2000). A Model of the Threshold Stress Intensity Factor, K IH, for Delayed Hydride Cracking of Zr-2.5Nb Alloy, J. Nucl. Mater. 278, 251-257.10.1016/S0022-3115(99)00249-4 ↗
4. Krasowsky, A.J. (1998). The Local Approach to Fracture of Structural Materials, Fracture: a Topical Encyclopedia of Current Knowledge (Edited by G.P. Cherepanov), Krieger Publ., Florida, 316-324.
5. Matvienko, Yu.G. (1999). On the Cohesive Zone Model for a Finite Crack, Int. J. Fract. 98, L53-L58.10.1023/A:1018761000139 ↗
6. Matvienko, Yu.G. (2000). A Theoretical Estimation of Fracture Toughness of Zirconium Hydride, J. Mater. Sci. Lett. 19, 1697-1699.10.1023/A:1006793911496 ↗
7. Puls, M.P. (1997). Assessment of Aging of Zr-2.5Nb Pressure Tubes in CANDU™ Reactors, Nucl.Eng.Des. 171, 137-148.10.1016/S0029-5493(96)01310-6 ↗
8. Sagat, S., Coleman, C.E., Griffiths, M. and Wilkins, B.J.S. (1994). The Effect of Fluence and Irradiation Temperature on Delayed Hydride Cracking in Zr-2.5Nb, Zirconium in the Nuclear Industry, ASTM STP 1245, in American Society for Testing Materials, (Edited by A.M. Garde and E.R Bradley), Philadelphia, 35-61.
9. Shek, G.K., Jovanovic, M.T., Seahra, H., Ma, Y., Li, D. and Eadie, R.L. (1996). Hydride Morphology and Striation Formation during Delayed Hydride Cracking in Zr-2.5% Nb, J. Nucl. Mater. 231, 221-230.10.1016/0022-3115(96)00370-4 ↗
10. Shi, S.-Q. and Puls, M.P. (1994). Criteria for Fracture Initiation at Hydrides in Zirconium Alloys I. Sharp Crack Tip, J. Nucl. Mater. 208, 232-242.10.1016/0022-3115(94)90332-8 ↗
11. Simpson, L.A. and Cann, C.D. (1979). Fracture Toughness of Zirconium Hydride and its Influence on the Crack Resistance of Zirconium Alloys, J. Nucl. Mater. 87, 303-316.10.1016/0022-3115(79)90567-1 ↗
12. Simpson, L.A. and Puls, M.P. (1979). The Effects of Stress, Temperature and Hydrogen Content on Hydride-Induced Crack Growth in Zr-2.5 Pct Nb, Metall. Trans. 10A, 1093-1105.
13. Smith, E. (1994). A Comparison of the Smeared-Dislocation and Super-Dislocation Description of a Hydrided Region in the Context of Modelling Delayed Hydride Cracking Initiation, J. Mater. Science 29, 1121-1126.10.1007/BF00351441 ↗
14. Wappling, D., Massih, A.R. and Stahle, P. (1997). A Model for Hydride-Induced Embrittlement in Zirconium-Based Alloys, J. Nucl. Mater. 249, 231-238.10.1016/S0022-3115(97)00183-9 ↗
15. Weatherly, G.C. (1981). The Precipitation of γ-Hydride Plates in Zirconium, Acta Metall. 29, 501-512.10.1016/0001-6160(81)90074-2 ↗