Assessing the fracture toughness of Zircaloy-4 fuel rod cladding tubes: impact of delayed hydride cracking
Source abstract
Abstract
Abstract Delayed Hydride Cracking (DHC) is a hydrogen embrittlement phenomenon that may potentially occur in Zircaloy-4 fuel claddings during dry storage conditions. An experimental procedure has been developed to measure the toughness of this material in the presence of DHC by allowing crack propagation through the thickness of a fuel cladding. Notched C-ring specimens, charged with 100 wppm of hydrogen, were used and pre-cracked by brittle fracture of a hydrided zone at the notch root at room temperature. The length of the pre-crack was measured on the fracture surface or cross-sections. Additionally, a finite element model was developed to determine the stress intensity factor as a function of the crack length for a given loading. Two types of tests were conducted independently to determine the fracture toughness with and without DHC, KIDHC and KIC, respectively: (i) constant load tests %after a thermal cycle at 150°C, 200°C, and 250°C; (ii) monotonic tests at 25°C, 200°C, and 250°C. The results indicate the following: (1) there is no temperature influence on the DHC toughness of Zircaloy-4 between 150 and 250°C (KIDHC ∈ [7.2;9.2] MPa.m1/2), (2) within this temperature range, the fracture toughness of Zircaloy-4 is halved by DHC (KIC ∈ [16.9;19.7] MPa.m1/2), (3) the crack propagation rate decreases with decreasing temperature and (4) the time before crack propagation increases as the temperature and loading decrease.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Nuclear reactor physics and engineering · Nuclear and radioactivity studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (44)
Show source-provided references
1. Allegre S, Sachot L, Rabouille O (2011) Method of analyzing an image of hydrides in a metal alloy, notably in a nuclear fuel cladding alloy. https://www.freepatentsonline.com/y2011/0116680.html
2. Alvarez Holston AM, Stjärnsäter J (2017) On the effect of temperature on the threshold stress intensity factor of delayed hydride cracking in light water reactor fuel cladding. Nucl Eng Technol 49(4):663–667. https://doi.org/10.1016/j.net.2017.04.00210.1016/j.net.2017.04.002 ↗
3. Arkoma A, Huhtanen R, Leppänen J, Peltola J, Pättikangas T (2018) Calculation chain for the analysis of spent nuclear fuel in long-term interim dry storage. Ann Nucl Energy 119:129–138. https://doi.org/10.1016/j.anucene.2018.04.03710.1016/j.anucene.2018.04.037 ↗
4. Auzoux Q, Bouffioux P, Machiels A, Yagnik S, Bourdiliau B, Mallet C, Mozzani N, Colas K (2022) Hydride reorientation and its impact on mechanical properties of high burn-up and unirradiated cold-worked stress-relieved Zircaloy-4 and ZirloTM fuel cladding. J Nucl Mater 568:153893. https://doi.org/10.1016/j.jnucmat.2022.15389310.1016/j.jnucmat.2022.153893 ↗
5. Chu H, Wu S, Kuo R (2008) Hydride reorientation in Zircaloy-4 cladding. J Nucl Mater 373(1–3):319–327. https://doi.org/10.1016/j.jnucmat.2007.06.01210.1016/j.jnucmat.2007.06.012 ↗
6. Coleman C, Grigoriev V, Inozemtsev V, Markelov V, Roth M, Makarevicius V, Kim YS, Liaqat Ali K, Chakravarrty JK, Mizrahi R, Lalgudi R, Barberis P, Dean SW (2010) The effect of microstructure on delayed hydride cracking behavior of Zircaloy-4 fuel cladding—an International Atomic Energy Agency Coordinated Research Program. J ASTM Int 7(5):103008. https://doi.org/10.1520/JAI10300810.1520/JAI103008 ↗
7. Coleman C, Grigoriev V, Inozemtsev V, Markelov V, Roth M, Makarevicius V, Kim YS, Liaqat Ali K, Chakravartty JK, Mizrahi R, Lalgudi R (2012) The effect of microstructure on delayed hydride cracking behavior of Zircaloy-4 fuel cladding—an International Atomic Energy Agency Coordinated Research Program. In: Limbäck M, Barbéris P (eds) Zirconium in the nuclear industry: 16th international symposium. ASTM International, West Conshohocken, pp 544–574
8. Colldeweih AW, Bertsch J (2022) Effect of temperature and hydrogen concentration on the threshold stress intensity factor of radial delayed hydride cracking in fuel cladding. J Nucl Mater 565:153737. https://doi.org/10.1016/j.jnucmat.2022.15373710.1016/j.jnucmat.2022.153737 ↗
9. Daum RS, Majumdar S, Liu Y, Billone MC (2006) Radial-hydride embrittlement of high-burnup Zircaloy-4 fuel cladding. J Nucl Sci Technol 43(9):1054–1067. https://doi.org/10.1080/18811248.2006.971119510.1080/18811248.2006.9711195 ↗
10. EPRI (2011) Delayed hydride cracking considerations relevant to spent nuclear fuel storage. Tech. Rep
11. Feria F, Herranz L (2011) Creep assessment of Zry-4 cladded high burnup fuel under dry storage. Prog Nucl Energy 53(4):395–400. https://doi.org/10.1016/j.pnucene.2011.01.01210.1016/j.pnucene.2011.01.012 ↗
12. Hong JD, Yang YS, Kook D (2020) Improvement of delayed hydride cracking assessment of PWR spent fuel during dry storage. Nucl Eng Technol 52(3):614–620. https://doi.org/10.1016/j.net.2019.07.03610.1016/j.net.2019.07.036 ↗
13. Hong JD, Park M, Holston AMA, Stjärnsäter J, Kook D (2021) Threshold stress intensity factor of delayed hydride cracking in irradiated and unirradiated Zircaloy-4 cladding. J Nucl Mater 543:152596. https://doi.org/10.1016/j.jnucmat.2020.15259610.1016/j.jnucmat.2020.152596 ↗
14. Huang FH, Mills WJ (1991) Delayed hydride cracking behavior for Zircaloy-2 tubing. Metall Trans A 22(9):2049–2060. https://doi.org/10.1007/BF0266987210.1007/BF02669872 ↗
15. IAEA (2010) Review of fuel failures in water cooled reactors. Tech. Rep. NF-T-2.1
16. IAEA (2016) Evaluation of conditions for hydrogen induced degradation of zirconium alloys during fuel operation and storage. Text TECDOC-1781. https://www-pub.iaea.org/MTCD/Publications/PDF/TE-1781_web.pdf
17. Kammenzind B, Franklin D, Peters H, Duffin W (1996) Hydrogen Pickup and Redistribution in Alpha-Annealed Zircaloy-4. In: Bradley E, Sabol G (eds) Zirconium in the nuclear industry: 11th international symposium. ASTM International, West Conshohocken, pp 338–338-3310.1520/STP16180S ↗
18. Kearns J (1967) Terminal solubility and partitioning of hydrogen in the alpha phase of zirconium, Zircaloy-2 and Zircaloy-4. J Nucl Mater 22(3):292–303. https://doi.org/10.1016/0022-3115(67)90047-510.1016/0022-3115(67)90047-5 ↗
19. Kearns J (1972) Diffusion coefficient of hydrogen in alpha zirconium, Zircaloy-2 and Zircaloy-4. J Nucl Mater 43(3):330–338. https://doi.org/10.1016/0022-3115(72)90065-710.1016/0022-3115(72)90065-7 ↗
20. Kim JS, Kim YJ, Kook DH, Kim YS (2015) A study on hydride reorientation of Zircaloy-4 cladding tube under stress. J Nucl Mater 456:246–252. https://doi.org/10.1016/j.jnucmat.2014.09.03210.1016/j.jnucmat.2014.09.032 ↗
21. Kim YS, Cheong YM (2008) Anisotropic delayed hydride cracking velocity of CANDU Zr–2.5 Nb pressure tubes. J Nucl Material 373(1–3):179–185. https://doi.org/10.1016/j.jnucmat.2007.05.04710.1016/j.jnucmat.2007.05.047 ↗
22. Kim YS, Park SS, Kwun SI (2008) Threshold stress intensity factor, KIH for delayed hydride cracking of a Zr–2.5% Nb tube with loading mode. J Alloys Compd 462(1–2):367–375. https://doi.org/10.1016/j.jallcom.2007.08.04510.1016/j.jallcom.2007.08.045 ↗
23. Konarski P, Cozzo C, Khvostov G, Ferroukhi H (2021) Spent nuclear fuel in dry storage conditions—current trends in fuel performance modeling. J Nucl Mater. https://doi.org/10.1016/j.jnucmat.2021.15313810.1016/j.jnucmat.2021.153138 ↗
24. Kreyns P, Bourgeois W, White C, Charpentier P, Kammenzind B, Franklin D (1994) Lifetime embrittlement of reactor core materials. Tech. Rep. WAPD-T–3046, USA
25. Kubo T, Kobayashi Y, Uchikoshi H (2012) Measurements of delayed hydride cracking propagation rate in the radial direction of Zircaloy-2 cladding tubes. J Nucl Mater 427(1–3):18–29. https://doi.org/10.1016/j.jnucmat.2012.04.01210.1016/j.jnucmat.2012.04.012 ↗
26. Lacroix E, Motta A, Almer J (2018) Experimental determination of zirconium hydride precipitation and dissolution in zirconium alloy. J Nucl Mater 509:162–167. https://doi.org/10.1016/j.jnucmat.2018.06.03810.1016/j.jnucmat.2018.06.038 ↗
27. Le Saux M, Besson J, Carassou S (2015) A model to describe the mechanical behavior and the ductile failure of hydrided Zircaloy-4 fuel claddings between 25$$\circ $$C and 480$$\circ $$C. J Nucl Mater 466:43–55. https://doi.org/10.1016/j.jnucmat.2015.07.02610.1016/j.jnucmat.2015.07.026 ↗
28. Narang P, Paul G, Taylor K (1977) Location of hydrogen in alpha-zirconium. J Less Common Met 56(1):125–128. https://doi.org/10.1016/0022-5088(77)90225-910.1016/0022-5088(77)90225-9 ↗
29. Pan Z, Ritchie I, Puls M (1996) The terminal solid solubility of hydrogen and deuterium in Zr–2.5 Nb alloys. J Nucl Mater 228(2):227–237. https://doi.org/10.1016/S0022-3115(95)00217-010.1016/S0022-3115(95)00217-0 ↗
30. Puls MP (2012) The effect of hydrogen and hydrides on the integrity of zirconium alloy components. Engineering materials. Springer, London. https://doi.org/10.1007/978-1-4471-4195-210.1007/978-1-4471-4195-2 ↗
31. Rais B, Garnier J, Pons E, Marini B, Besson J (2023) Determination of the fracture toughness of a 9Cr ODS steel fuel cladding using the pin loading tension test. Eng Fract Mech 290:109499. https://doi.org/10.1016/j.engfracmech.2023.10949910.1016/j.engfracmech.2023.109499 ↗
32. Raynaud PA, Einziger RE (2015) Cladding stress during extended storage of high burnup spent nuclear fuel. J Nucl Mater 464:304–312. https://doi.org/10.1016/j.jnucmat.2015.05.00810.1016/j.jnucmat.2015.05.008 ↗
33. Raynaud PA, Koss DA, Motta AT, Chan KS, Limback M, Kammenzind B, Dean SW (2008) Fracture toughness of hydrided Zircaloy-4 sheet under through-thickness crack growth conditions. J ASTM Int 5(1):101183. https://doi.org/10.1520/JAI10118310.1520/JAI101183 ↗
34. Raynaud PA, Koss DA, Motta AT (2012) Crack growth in the through-thickness direction of hydrided thin-wall Zircaloy sheet. J Nucl Mater 420(1–3):69–82. https://doi.org/10.1016/j.jnucmat.2011.09.00510.1016/j.jnucmat.2011.09.005 ↗
35. Rossiter G (2011) Development of the enigma fuel performance code for whole core analysis and dry storage assessments. Nucl Eng Technol 43(6):489–498. https://doi.org/10.5516/NET.2011.43.6.48910.5516/NET.2011.43.6.489 ↗
36. Sagat S, Coleman C, Griffiths M, Wilkins B (1994) The effect of fluence and irradiation temperature on delayed hydride cracking in Zr-2.5Nb. In: Garde A, Bradley E (eds) Zirconium in the nuclear industry: 10th international symposium. ASTM International, West Conshohocken, pp 35–35-2710.1520/STP15183S ↗
37. Sakamoto K, Nakatsuka M, Higuchi T (2008) Simulation of cracking during outside-in type failure of high burn-up fuel cladding tubes. Seoul, Korea. https://inis.iaea.org/search/search.aspx?orig_q=RN:44050178
38. Shek G (1998) The effect of material properties, thermal and loading history on delayed hydride cracking in Zr–2.5% Nb alloys. PhD thesis, University of Manchester. https://ethos.bl.uk/OrderDetails.do?uin=uk.bl.ethos.629567
39. Shi SQ, Puls M (1994) Criteria for fracture initiation at hydrides in zirconium alloys I. Sharp crack tip. J Nucl Mater 208(3):232–242. https://doi.org/10.1016/0022-3115(94)90332-810.1016/0022-3115(94)90332-8 ↗
40. Shi SQ, Puls MP (1995) Dependence of the threshold stress intensity factor on hydrogen concentration during delayed hydride cracking in zirconium alloys. J Nucl Mater 218(1):30–36. https://doi.org/10.1016/0022-3115(94)00368-810.1016/0022-3115(94)00368-8 ↗
41. Suo XZ, Combescure A (1992) On the application of G($$\theta $$) method and its comparison with De Lorenzi’s approach. Nucl Eng Des 135(2):207–224. https://doi.org/10.1016/0029-5493(92)90223-I10.1016/0029-5493(92)90223-I ↗
42. Tang R, Yang X (2009) Dissolution and precipitation behaviors of hydrides in N18, Zry-4 and M5 alloys. Int J Hydrogen Energy 34(17):7269–7274. https://doi.org/10.1016/j.ijhydene.2009.07.01810.1016/j.ijhydene.2009.07.018 ↗
43. Yan D, Eadie RL (2002) Calculation of the delayed hydride cracking velocity vs. KI curve for Zr-2.5%Nb by critical hydride cluster length. J Mater Sci 37(24):5299–5303. https://doi.org/10.1023/A:102102092343710.1023/A:1021020923437 ↗
44. Zanellato O, Preuss M, Buffiere JY, Ribeiro F, Steuwer A, Krebs B (2012) Synchrotron diffraction study of dissolution and precipitation kinetics of hydrides in Zircaloy-4. J Nucl Mater 420(1–3):537–547. https://doi.org/10.1016/j.jnucmat.2011.11.00910.1016/j.jnucmat.2011.11.009 ↗