Nano-Indentation Measurement of Fracture Toughness of Dental Enamel
Source abstract
Abstract
Effect of orthodontic bracket bonding-debonding on fracture toughness of human dental enamel was investigated by using nano-indentation test. For this purpose, some ceramic brackets were bonded by a dental adhesive on the buccal surface of sound human teeth enamel. All clinical requirements were considered for bracket bonding and sample preparation. After debonding of the brackets, the teeth were sectioned transverse to their longitudinal axes and from the middle of the bracket region to prepare the samples required for nano-indentation tests. The nanoindentation test was performed on both the enamel under bracket and the intact enamel. The values of fracture toughness of dental enamel in both regions were calculated from the analysis of nano-scale holes observed after the nano-indentation tests. A comparison between the results obtained from the two regions indicated that bracket bonding-debonding significantly decreased the fracture toughness of human dental enamel.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metal and Thin Film Mechanics · Diamond and Carbon-based Materials Research · Dental materials and restorations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. Ayatollahi M, Karimzadeh A (2012) Determination of Fracture Toughness of Bone Cement by Nano- Indentation Test. International Journal of Fracture 175 (2):193–198. doi: 10.1007/s10704-012-9711-510.1007/s10704-012-9711-5 ↗
2. Ge J, Cui FZ, Wang XM, H.L. Feng (2005) Property variations in the prism and the organic sheath within enamel by nanoindentation. Biomaterials 26: 3333–333910.1016/j.biomaterials.2004.07.059 ↗
3. Habelitz S, Marshall SJ, Marshall-Jr GW, Balooch M (2001) Mechanical properties of human dental enamel on the nanometre scale. Archives of Oral Biology 46: 173–18310.1016/S0003-9969(00)00089-3 ↗
4. Hassan R, Caputo AA, Bunshash RF (1981) Fracture toughness of human enamel. J Dent Res 60: 820–82710.1177/00220345810600040901 ↗
5. He LH, Swain MV (2008) Understanding the mechanical behaviour of human enamel from its structural and compositional characteristics. J Mech Behav Biomed Mater 1: 18–2910.1016/j.jmbbm.2007.05.001 ↗
6. Iijima M, Muguruma T, Brantley WA, Ito S, Yuasa T, Saito T, Mizoguchif I (2010) Effect of bracket bonding on nanomechanical properties of enamel. Am J Orthod Dentofac Orthop 138: 735–74010.1016/j.ajodo.2009.01.028 ↗
7. Kruzica J, Kimb D, Koesterc K, Ritchiec R (2009) Indentation techniques for evaluating the fracture toughness of biomaterials and hard tissues. J of mech behavior of biomed mater 2: 384–39510.1016/j.jmbbm.2008.10.008 ↗
8. Johnson CD, Hussey DL, Burden DJ (1996) The effect of etch duration on the microstricture of molar enamel: An in vitro study. Am J Orthod Dentofac Orthop 109: 531–53410.1016/S0889-5406(96)70138-5 ↗
9. Lawn BR, Evans AG, Marshall DB (1980) Elastic/plastic indentation damage in ceramics: The median/radial crack system. Journal of the American Ceramic Society 63(910): 574–58110.1111/j.1151-2916.1980.tb10768.x ↗
10. Oliver WC (2001) Alternative technique for analyzing instrumented indentation data. J Mater Res 16: 3202–320610.1557/JMR.2001.0441 ↗
11. Oliver WC, Pharr GM (2004) Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology. J Mater Res 19: 3–2010.1557/jmr.2004.19.1.3 ↗
12. Pharr GM (1998) Measurement of mechanical properties by ultra-low load indentation. Materials Science and Engineering A253:151–15910.1016/S0921-5093(98)00724-2 ↗
13. Pharr GM, Bolshakov A (2002) Understanding nanoindentation unloading curves. J Mater Res 17: 2660–267110.1557/JMR.2002.0386 ↗
14. Staines M, Robinson WH, Hood JAA (1981) Spherical indentation of tooth enamel. J Mater Sci Lett 16: 2551–255610.1007/BF01113595 ↗
15. White SN, Luo W, Paine ML, Fong H, Sarikaya M, Snead ML (2001) Biological organization of hydroxyapatite crystallites into a fibrous continuum toughens and controls anisotropy in human enamel. J Dent Res 80: 321–32610.1177/00220345010800010501 ↗
16. Xu HH, Smith DT, Jahanmir S, Romberg E, Kelly JR, Thompson VP (1998) Indentation damage and mechanical properties of human enamel and dentin. J Dent Res 77: 472–48010.1177/00220345980770030601 ↗