Interface crack in sandwich specimen

Fracture of a sandwich specimen loaded with axial forces and bending moments is analyzed in the context of linear elastic fracture mechanics. A closed form expression for the energy release rate for interface cracking of a sandwich specimen with isotropic face sheets is found from analytical evaluation of the J-integral. An approach is applied, whereby the mode mixity for any combination of the loads can be calculated analytically when a load-independent phase angle has been determined. This load-independent phase angle is determined for a broad range of sandwich configurations of practical interest. The load-independent phase angle is determined using a novel finite element based method called the crack surface displacement extrapolation method. The expression for the energy release rate is based on the J-integral and certain stress distributions along the ends of the sandwich specimen. When the stresses from the crack tip interacts with the stresses at the ends, the present analytical calculation of the J-integral becomes inaccurate. The results show that for the analytically J-integral to be accurate the crack tip must be a certain distance away from the uncracked end of the specimen. For a sandwich specimen with face sheet/core stiffness ratio of 100, this distance is in the order 10 times the face sheet thickness. For sandwich structures with face sheet/core stiffness ratio of 1,000, the distance is 30 times the face sheet thickness.