Micro-mechanism of rolling contact fatigue in Hadfield steel crossing

B. Lv, M. Zhang, F.C. Zhang, C.L. Zheng, X.Y. Feng, L.H. Qian, X.B. Qin

Publisher page

Abstract

The formation of the fatigue cracks was due to massive vacancy clusters in the subsurface layer of Hadfield steel crossing, which are induced by the accumulated plastic deformation under the conditions of impact and contact stresses from train wheels. The high concentration layers of vacancy clusters were formed parallel to the working surface of the crossing, which caused the initial rolling contact fatigue cracks to be parallel to the working surface with a laminar distribution in the depth direction. It can be predicted that metals containing elements with larger atomic diameter should have better rolling contact fatigue and wear performances. (C) 2012 Elsevier Ltd. All rights reserved.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Metal Alloys Wear and Properties · Railway Engineering and Dynamics · Surface Treatment and Coatings

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (27)

Show source-provided references
1. Fatigue crack propagation rate of austenitic high manganese steel
2. Development of high-manganese steels for heavy duty cast-to-shape applications10.1016/j.jmatprotec.2004.04.136 ↗
3. Microstructure in working surface of Hadfield steel crossing10.1142/S021797920906066X ↗
4. The effect of intermittent lubrication on the fatigue life of pearlitic rail steel in rolling–sliding contact10.1243/0954409001531360 ↗
5. Prediction of fatigue crack initiation for rolling contact fatigue10.1016/S0142-1123(99)00125-5 ↗
6. A new type of RCF, experimental investigations and theoretical modeling10.1016/S0043-1648(02)00084-4 ↗
7. Effects of imperfections on fatigue initiation in railway wheels10.1243/0954409001531234 ↗
8. Maillard-Salin C, Nhari A, Lebrun JL, et al. Analysis of ‘kidney-shape’ fatigue crack development in rail head using laboratory specimen. Eng Mater Advisory Services Ltd. 2 (1986) 255–268.
9. Johnson · 1985
10. Subsurface rolling contact fatigue damage of railway wheels – a probabilistic analysis10.1016/j.ijfatigue.2011.11.002 ↗
11. Numerical simulation of stress and deformation in a railway crossing10.1016/j.engfailanal.2011.08.006 ↗
12. Numerical stress analysis and rolling contact fatigue of white etching layer on rail steel10.1016/j.ijfatigue.2010.08.007 ↗
13. A computational model for determination of service life of gears10.1016/S0142-1123(02)00024-5 ↗
14. Numerical procedure for predicting the rolling contact fatigue crack initiation10.1016/S0142-1123(03)00019-7 ↗
15. Modelling of rolling contact fatigue of rails10.4028/www.scientific.net/KEM.324-325.987 ↗
16. Deformation and damage of a crossing nose due to wheel passages10.1016/j.wear.2008.01.033 ↗
17. Vacancy clusters close to a fatigue crack observed with the München scanning positron microscope10.1016/S0169-4332(02)00106-X ↗
18. Positron annihilation lifetime measurement of cyclically deformed Fe–0.5wt.% Si alloy single crystals10.1016/0956-716X(92)90283-K ↗
19. Non-destructive evaluation of plasticity and prediction of fatigue failure in industrial aluminum alloys with positrons10.1002/pssa.200925540 ↗
20. Nondestructive detection of fatigue damage in austenitic stainless steel by positron annihilation10.1007/s10853-005-3163-5 ↗
21. A study of fatigue failure in superalloys using positron annihilation10.1002/pssa.2211380113 ↗
22. Point defect model for fatigue crack initiation in Ni3Al+B single crystals10.1016/0956-7151(90)90192-J ↗
23. Direct observation of carbon-decorated defects in fatigued type 304 stainless steel using positron annihilation spectroscopy10.1016/S1359-6454(02)00027-7 ↗
24. Estimation of dislocation density and vacancy concentration in deformed high purity iron using PAT
25. On some recent trends in modeling of contact fatigue and wear in rail10.1016/S0043-1648(02)00104-7 ↗
26. Vacancy formation energies in bcc and fcc stainless steels by positron annihilation10.1139/p83-020 ↗
27. Nanoscale friction varied by isotopic shifting of surface vibrational frequencies10.1126/science.1147550 ↗