Generation and analysis of FCG data using a single specimen and Kmax–ΔK testing matrix

Abstract A custom method to generate fatigue crack growth (FCG) data requires testing of multiple specimens at different load ratios, R, and the application of a load shedding procedure from pre-cracking level to threshold. In this paper, a novel method of testing has been investigated which utilizing a single specimen and a testing matrix in terms of Kmax and ΔK values corresponding to predetermined R-ratios for which FCG data are recorded. Automatic K-controlled tests on 2324-T39 Al alloy were conducted using both increasing and decreasing ΔK procedures while Kmax was kept constant. Results show that the increasing ΔK procedure gives less scatter than decreasing ΔK procedure. Also, fatigue crack growth curves near the threshold region obtained from increasing ΔK are above the curves obtained from decreasing ΔK procedure. These differences are explained by means of interaction between cyclic plastic zones and their effect on fatigue damage. The procedure with increasing ΔK demonstrated minimal interaction effects and hence it is recommended for efficient FCG data generation. The proposed procedure reduces testing time, the overall scatter associated with multiple samples and eliminates possible uncertainty linked to the load shedding procedure and its effects on threshold.