Effect of contact pressure on fretting fatigue failure of oil-well pipe material
Source abstract
Abstract
Abstract As the result of a full-scale test of a thread joint connecting oil-well casing pipes, fretting fatigue failure at the middle of the thread engagement part was identified. The objective of this study is to understand the mechanism of the fretting fatigue failure at the middle of the contact part. A similar failure mode was reproduced by a bridge-pad type fretting fatigue test under gross slip conditions. It was found that the crack position moved from the contact edge toward the inside of the contact part with the progress of the fretting wear.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical stress and fatigue analysis · Engineering Structural Analysis Methods · Mechanical Failure Analysis and Simulation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (31)
Show source-provided references
1. Slipping behavior and fretting fatigue in the disk/blade dovetail region
2. Effect of contact materials on fretting fatigue strength of 3. 5Ni-Cr-Mo-V rotor steel and life-prediction method
3. Fretting fatigue in engineering alloys10.1016/S0142-1123(97)00039-X ↗
4. Fretting fatigue at elevated temperature in two steam turbine steels10.1111/j.1460-2695.1989.tb00549.x ↗
5. Effect of contact pressure on high temperature fretting fatigue10.2472/jsms.42.78 ↗
6. Fracture mechanics approach to the fretting fatigue strength of axle assemblies
7. The analysis of fretting fatigue failure in backup roll and its prevention
8. Effect of understress on fretting fatigue crack initiation of press-fitted axle10.1299/jsmea.46.297 ↗
9. Finite-element analysis of alternating axial loading of an elastic plate pressed between two elastic rectangular blocks with finite friction10.1016/0020-7225(71)90038-3 ↗
10. Fracture mechanisms of fretting fatigue10.2472/jsms.46.1233 ↗
11. Applications of fracture mechanics in fretting fatigue life assessment
12. Fracture mechanics approach to fretting fatigue and problem to be solved10.1016/S0301-679X(02)00136-6 ↗
13. Fretting fatigue strength estimation considering the fretting wear process10.1016/j.triboint.2006.02.049 ↗
14. Study on fretting fatigue crack initiation mechanism based on local stress at contact edge
15. A quantitative approach to evaluate fretting fatigue limit using a pre-cracked specimen10.1016/j.triboint.2016.10.017 ↗
16. Fundamental investigation of fretting fatigue – Part 3 Some Phenomena and mechanisms of surface cracks
17. Characterization of fretting damage in a press-fitted shaft below the fretting fatigue limit10.1016/j.proeng.2010.03.209 ↗
18. In-situ observation of fretting fatigue crack initiation behavior and wear process by using laser microscope
19. Effects of hybrid analysis on wear and contact stress in fretting fatigue
20. Simulation analysis of initial and steady-state wear in fretting process
21. Combined experimental - computational investigation of fretting in flexible marine risers
22. Fretting wear and fretting-fatigue: relation through a mapping concept
23. Fretting fatigue on threaded root of premium threaded connections10.1016/j.triboint.2016.10.021 ↗
24. Fundamental investigation of fretting fatigue – Part 6 effect of contact pressure and hardness
25. Analyses of contact pressure and stress amplitude effects on fretting fatigue life10.1115/1.1288211 ↗
26. Effect of contact pressure on fretting fatigue in type 316L stainless steel
27. Effect of contact pressure on fretting fatigue strength in friction-type joints
28. Study on fretting fatigue crack propagation condition at edge and center of contact part
29. The initiation of fatigue cracks in a 0.7% carbon steel by fretting10.1016/0043-1648(71)90024-X ↗
30. Effects of contact pressure and surface roughness on fretting fatigue characteristics of a high workable Ti–4.5%Al–3%V–2%Mo–2%Fe alloy10.2464/jilm.53.563 ↗
31. Effect of relative slip amplitude on fretting fatigue of high strength steel10.1111/j.1460-2695.1994.tb00806.x ↗