Fatigue crack initiation in the presence of stratified surface layers on rail wheels
Source abstract
Abstract
This work presents a study on the fatigue crack initiation in the presence of stratified surface layers (SSL) – a combination of white and brown etching layer – on rail wheels. Reproducible SSLs comparable to field samples are created by a defined mechanical load and two consecutive laser surface treatments on discs made from two wheel materials (ER7, ER9). Fatigue testing is done by a twin disc tribometer, where the wheel discs with SSLs are driven against discs made from R260 rail material. The results show significant fatigue crack initiation and propagation in the presence of the SSLs, exclusively on the leading edge of the SSL, more pronounced for the wheel grade ER9. Based on topographical, light optical and scanning electron microscopy analysis an explanatory model is presented, describing fatigue crack morphologies and outpointing the relevance of SSLs on rail wheels to fatigue crack initiation.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Railway Engineering and Dynamics · Metal Alloys Wear and Properties · Gear and Bearing Dynamics Analysis
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (51)
Show source-provided references
1. Numerical investigation of crack initiation in rails and wheels affected by martensite spots10.1016/j.ijfatigue.2018.05.023 ↗
2. Wheel/rail rolling contact fatigue – Probe, predict, prevent10.1016/j.wear.2013.12.004 ↗
3. Fatigue of railway wheels and rails under rolling contact and thermal loading—an overview10.1016/j.wear.2004.03.039 ↗
4. Rail rolling contact fatigue formation and evolution with surface defects10.1016/j.ijfatigue.2022.106762 ↗
5. Fatigue crack initiation life prediction of railroad wheels10.1016/j.ijfatigue.2005.09.007 ↗
6. Fatigue crack growth of a railway wheel10.1016/j.engfailanal.2017.07.036 ↗
7. Studs and squats: The evolving story10.1016/j.wear.2016.03.021 ↗
8. Squat formation and rolling contact fatigue in curved rail track10.1016/j.engfracmech.2015.05.060 ↗
9. On the genesis of squat-type defects on rails – Toward a unified explanation
10. Squats and squat-type defects in rails: the understanding to date10.1177/0954409711422189 ↗
11. Studs: a squat-type defect in rails10.1177/0954409711421462 ↗
12. Formation Mechanism and Evolution of White Etching Layers on Different Rail Grades10.1016/j.ijfatigue.2022.107100 ↗
13. Characterisation of White Etching Layers formed on rails subjected to different traffic conditions
14. Comparative study on the influence of initial deformation and temperature of thermally induced white etching layers on rail wheels10.1016/j.triboint.2022.107990 ↗
15. Investigation into the evolution of tribological white etching layers10.1016/j.matchar.2022.112076 ↗
16. Rolling contact fatigue of white etching layer: Part 1 Crack morphology10.1016/j.wear.2007.01.003 ↗
17. Simulation and experiment based investigations of squat formation mechanisms
18. The microstructure analysis of white etching layer on treads of rails10.1016/j.engfailanal.2017.06.018 ↗
19. Modelling a squat form crack on a rail laid on an elastic foundation10.1016/j.engfracmech.2012.02.004 ↗
20. Crack propagation behavior in white etching layer on rail steel surface10.1016/j.engfailanal.2019.06.067 ↗
21. Early stages of rail squat formation and the role of a white etching layer10.1016/j.ijfatigue.2013.02.016 ↗
22. Numerical stress analysis and rolling contact fatigue of White Etching Layer on rail steel10.1016/j.ijfatigue.2010.08.007 ↗
23. Deuce R. Wheel Tread Damage - An Elementary Guide. Bombardier Transportation GmbH, Netphen, Germany, Technical Report; 2007.
24. Formation mechanism for the white etching microstructure in the subsurface of the failure pearlite wheel steel
25. Fatigue Investigation on Railway Wheel Steel with White Etching Layer10.1007/s13296-019-00271-x ↗
26. Investigation of influence of white layer geometry on spalling property in railway wheel steel10.1016/j.wear.2010.10.024 ↗
27. “Brown etching layer”: A possible new insight into the crack initiation of rolling contact fatigue in rail steels?10.1016/j.engfailanal.2016.03.019 ↗
28. Microstructural evolution of white and brown etching layers in pearlitic rail steels10.1016/j.actamat.2019.04.012 ↗
29. Formation mechanism of brown etching layers in pearlitic rail steel10.1016/j.mtla.2022.101625 ↗
30. Stratified surface layers on rails10.1016/j.wear.2018.07.019 ↗
31. Microstructural evaluation and interpretation of the mechanically and thermally affected zone under railway wheel flats
32. Influence of grain boundaries on the behaviour of carbon and nitrogen in α-iron10.1016/0001-6160(55)90058-4 ↗
33. ‘EN 13262:2004+A2:2011: Railway applications - Wheelsets and bogies - Wheels - Product requirements’.
34. Herian J, Aniołek K. Abrasive wear of railway sections of steel with a different pearlite morphology in railroad switches. J Achievements Mater Manuf Eng, 2010; 43.10.1088/1757-899X/22/1/012012 ↗
35. Fracture Toughness: A Quality Index for Railway Solid Wheels10.1520/MPC20130047 ↗
36. In situ study on fracture behaviour of white etching layers formed on rails10.1016/j.actamat.2019.08.060 ↗
37. In-situ micro-cantilever bending studies of a white etching layer thermally induced on rail wheels10.1016/j.msea.2023.144805 ↗
38. Micro fracture investigations of white etching layers10.1016/j.matdes.2019.107892 ↗
39. Severe Plastic Deformed Zones and White Etching Layers Formed During Service of Railway Wheels10.1007/s13632-023-00967-x ↗
40. Microstructural characterization of near-surface microstructures on rail wheels in service – an insight into “stratified surface layers”10.12688/openreseurope.15881.2 ↗
41. Comparison of rolling contact fatigue damage between railway wheels and twin-disc test specimens10.1016/j.triboint.2021.107037 ↗
42. Third-body and crack behavior in white etching layer induced by sliding–rolling friction10.1016/j.triboint.2019.105882 ↗
43. Investigation on the rolling wear and damage properties of laser discrete quenched rail material with different quenching shapes and patterns10.1016/j.surfcoat.2019.124991 ↗
44. Investigation on the microstructure and damage characteristics of wheel and rail materials subject to laser dispersed quenching10.1016/j.apsusc.2018.04.210 ↗
45. Squat formation and the occurrence of two distinct classes of white etching layer on the surface of rail steel10.1016/j.ijfatigue.2017.07.005 ↗
46. Analysis of subsurface layer formation on a pearlitic rail under heavy haul conditions: Spalling characterization10.1016/j.engfailanal.2021.105549 ↗
47. Investigation of white etching layers on rails by optical microscopy, electron microscopy, X-ray and synchrotron X-ray diffraction10.1016/S0921-5093(00)01842-6 ↗
48. Evolution of thermally induced white etching layer at rail surface during multiple wheel/train passages10.1016/j.ijfatigue.2022.106799 ↗
49. Influence of white etching layer on rolling contact behavior at wheel-rail interface10.1007/s40544-020-0388-x ↗
50. Modelling of cyclic plasticity and phase transformations during repeated local heating events in rail and wheel steels10.1016/j.ijfatigue.2021.106361 ↗
51. Freisinger M, Trausmuth A, Hahn R, Badisch E. Influence of the evolution of near-surface rail wheel microstructure on crack initiation by micro-bending investigations. Proc Inst Mech Eng, Part F: J Rail Rapid Transit, 2023; 09544097231191550, doi: 10.1177/09544097231191550.10.1177/09544097231191550 ↗