Mechanism for fatigue striations as formed under variable negative R-ratio in Al-based structural alloys
Source abstract
Abstract
Abstract Effect of varying negative R-ratio on the fatigue striation patterns was examined for Al-based V95-T4 (analogue of 7057T6) and D16T (analogue of 2024T3) alloys. Three different sequences of cyclic loads and of the varying maximum and minimum stress levels were applied in air atmosphere to the test alloy panels 10 × 160 × 460 mm in size. The tests were conducted at room temperature with the loading frequencies in the range of 0.5–1.5 Hz. Fractographically, the magnitudes of striation spacing were found increasing for increasingly negative R-ratios. To estimate the effects of negative R-ratio on the crack growth rate correction-function surfaces were constructed for the stress-intensity factor KI. The fractographic analysis suggests that the unloading portions of cycling trajectory are only responsible for the fatigue striation effects. Such a mechanism appears dominating in the positive as in the negative ranges of R-ratio.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Probabilistic and Robust Engineering Design · Material Properties and Failure Mechanisms
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. Elber W. The significance of fatigue crack closure. ASTM STP 486, ASTM Philadelphia; 1971. p. 230–42.10.1520/STP26680S ↗
2. Shanyavskiy AA. Tolerance fatigue cracking of aircraft components. synergetics in engineering application. Ufa: Monograph (Russia); 2003.
3. Shanyavskiy AA. Fractographic analysis of in-service fatigued structures. In: Science works of institute of railway transports “cyclical resistance of metals cracking of structures and transportation devices”, vol. 669. Moscow: Transportation (Russia); 1984. p. 57–69.
4. Measurements of fatigue crack closure through electron microscopy10.1016/0142-1123(82)90065-2 ↗
5. Shanyavskiy AA. Modeling of metals fatigue cracking. Synergetics in aviation. Ufa: Monograph (Russia); 2007.
6. Bifurcation diagram for in-service fatigued metals10.1016/j.proeng.2010.03.026 ↗
7. Batias · 2005
8. Fatigue crack growth in ductile materials under cyclic compressive loading10.1111/j.1460-2695.1994.tb00775.x ↗
9. Current aspects of fatigue10.1179/msc.1977.11.8-9.274 ↗
10. Influence of microstructure on near-threshold fatigue-crack propagation in ultra-high strength steel10.1179/msc.1977.11.8-9.368 ↗
11. Elevated-temperature fatigue interactions in engineering materials10.1179/msc.1977.11.8-9.414 ↗
12. Analysis of fatigue crack propagation under biaxial loading using an inclined strip yield zone model of crack tip plasticity
13. Quantitative analysis of microstructural effects on fatigue crack growth in widmanstatten Ti–6Al–4V and Ti–8Al–1Mo–1V10.1016/0013-7944(79)90138-3 ↗
14. A geometrical model for fatigue crack closure induced by fracture surface roughness10.1007/BF02644803 ↗
15. Shanyavskiy AA. Influence of material state at a crack tip on the process of fatigue striations formation for Al-based alloys. In: Jaroslav Pokluda, editor. Materials structure and micromechanics of fracture IV, MSMF-4, Switzerland: Trans. Tech. Publication LTD 482; 2005. p. 235–8.10.4028/0-87849-964-4.235 ↗
16. A model of fatigue crack growth after an overload in D16T Al-alloy subjected to biaxial cyclic loads at various R-ratios10.1111/j.1460-2695.1997.tb00275.x ↗
17. Fatigue cracking simulation based on crack closure effects in Al-based sheet materials subjected to biaxial cyclic loads10.1016/j.engfracmech.2011.01.019 ↗
18. Acoustic emission monitoring of fatigue crack growth10.1016/0025-5416(78)90206-9 ↗
19. Dependence of acoustic emission for low strength steels upon the embrittlement and the plastic zone reduction at the crack tip during corrosion fatigue crack propagation10.1111/j.1460-2695.1993.tb00099.x ↗
20. Shanyavsky AA. Theoretical analysis and practice of stress equivalent determination for fatigue fracture by the quantitative fractography. In: Romaniv ON, editor. Standardization of fractographic method for fatigue crack growth estimation in metals by the fractographic analysis, vol. 5. Moscow:Standardization; 1984. p. 54–61 [in Russian].
21. Shanyavskiy AA. Mechanisms associated with the formation of fatigue striations in low-cycle-fatigue regime. In: Portella PD, Beck T, Okazaki M, editors. Proceedings of the sixth international conference on low cycle fatigue, LCF6, September 8–12, DVM, Berlin, Germany; 2008. p. 599–07.
22. Ivanova · 1988
23. The mechanism of stage II fatigue crack growth10.1111/j.1460-2695.1996.tb00166.x ↗
24. Bichler CH, Pippan R. Direct observation of the formation of striations. In: Beynon JH, Brown MW, Smith RA, Lindley TC, Tomkins B, editors. Engineering against fatigue; 1999. p. 211–8.
25. Ishii H, Choi SJ, Tohgo K. AFM fractography of fatigued aluminum alloy. In: Ellins F, Provan James W, editors. Proceedings of ICM8 progress in mechanical behavior of metals, vol. 1, May 16–21, Victoria: Canada; 1999. p. 73–8.
26. Fatigue crack growth in metals and alloys: mechanisms and micromechanisms10.1179/imr.1992.37.1.45 ↗
27. On the formation of fatigue striations10.1007/BF00185199 ↗
28. Fractography of fatigue crack propagation in 2024-T3 and 7075-T6 aluminum alloys in air and vacuum
29. Lynch SP. Mechanisms of fatigue and environmentally assisted fatigue. Fatigue mechanisms. ASTM STP 675, ASTM; 1979. p. 174–213.10.1520/STP35890S ↗
30. Hertzberg RW. Fatigue fracture surface appearance. ASTM STP 415, ASTM; 1967. p. 205–25.10.1520/STP47232S ↗
31. Laird C. The influence of metallurgical structure on the mechanisms of fatigue crack propagation. ASTM STP 415, ASTM; 1967. p. 131–68.10.1520/STP47230S ↗
32. Mechanisms of formation of ductile material striations
33. A quantitative stereoscopic fractographic study of the mechanism of fatigue crack propagation in nickel10.1007/BF00033220 ↗
34. Fatigue damage and crack growth in aluminum alloys10.1016/0001-6160(63)90008-7 ↗
35. Shear lips on fatigue fractures in aluminium alloy sheet material10.1016/0013-7944(81)90091-6 ↗
36. Linch SP. Mechanisms of fatigue and environmentally assisted fatigue. ASTM STP 675, ASTM; 1978. p. 174–213.10.1520/STP35890S ↗
37. Fatigue crack propagation under program and random loads
38. Nix KJ, Flower HM. The metallography of fatigue in the high strength aluminium alloy 7010. In: Proceedings of the conference on “advanced fracture research”, Cannes; 1981. p. 915–22.
39. Schick E, Ude J, Michtl F, Blumenauer H. Estimation of the R-curve by in situ measurements. In: Petit J. editor, and Fouquet J, Henaff G, Villechaise, Dragon A, co-editors. Proceedings of the ECF11 on “mechanisms and mechanics of damage and failure”, vol. I, September 3–6, Poitier-Futuroscope, France; 1996. p. 157–62.
40. Panin VE, editor. Physical mesomechanics of heterogeneous media and computer-aided design of materials. Cambridge, UK; 1988.
41. Fractographic analysis of crack growth and shear lip development under simple variable-amplitude loading10.1111/j.1460-2695.1990.tb00616.x ↗