The fatigue crack growth rate and crack opening displacement in 18G2A-steel under tension
Source abstract
Abstract
Abstract In the paper, the results of crack tip opening displacement (CTOD) and crack opening displacement (COD) in place of crack initiation as well as the fatigue crack growth rate in higher strength steel are presented. The investigation were carried out on flat specimens with central notch under constant amplitude tensile fatigue loading at stress ratio R = 0.2 and different value of the stress σmax. The test results showed that with growth of crack length l grew values of the CTOD and COD. In the work, it was proposed calculation of the CTOD value on basis various dependence of plastic zone radius on crack tip.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Structural Load-Bearing Analysis · High Temperature Alloys and Creep
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (16)
Show source-provided references
1. Kocańda · 1978
2. Kocańda S, Szala J. Postawy obliczeń zmęczeniowych. PWN, Warszawa; 1997, p. 288.
3. Neimitz A. Mechanika pękania. Wydawnictwo Naukowe PWN S.A. Warszawa; 1998, p. 55–70.
4. Bochenek A. Elementy mechaniki pękania. Wydawnictwo Politechniki Częstochowskiej; 1998. p. 255.
5. Description of fatigue crack growth rate notched members under tension and bending using the ΔJ integral range
6. J-integral in the description of elastic–plastic crack growth kinetics curve
7. Wells AA. Critical tip opening displacement as fracture criterion. In: Proceedings of the crack propagation symposium, vol. 1. Cranfield; 1961. p. 210–21.
8. A survey of failure criteria and parameters in mixed-mode fatigue crack growth10.1007/s11003-009-9179-2 ↗
9. ASTM E1290-89. Standard test method for crack tip opening displacement (CTOD) fracture toughness measurement. Philadelphia; 1989.
10. BS 57862. Method for crack opening displacement (COD) testing. British Standard Institution; 1979.
11. ESIS, P1-92. Procedure for determining the fracture behaviour of materials. European Structural Integrety Society; 1992.
12. The crack opening displacement approach to fracture mechanics in yielding materials10.1243/03093247V012145 ↗
13. On the mechanism of fatigue crack propagation in ductile metallic materials10.1111/j.1460-2695.2010.01484.x ↗
14. In-situ scanning electron microscope observations of the deformation behavior of short cracks10.1016/S0921-5093(99)00209-9 ↗
15. Blochowitz · 2000
16. Werner K. The correlation of measurement results of development and opening of crack in steel specimens at fatigue loading. Prace Komisji Naukowych – PAN (the works of committee of scientific – Polish Academy of Sciences) O/Katowice; vol. 32; 2008. p. 126–9 [in Polish].