Microstructurally-dependent model for predicting the kinetics of physically small and long fatigue crack growth

Abstract Based on the proposed concept of the fatigue threshold stress intensity factor ranges, a model has been developed that describes the kinetics of physically small fatigue crack and long fatigue crack growth. The model allows the calculation of the crack growth rate under the regular fully-reversed uniaxial loading from the data on the static characteristics of mechanical properties and the microstructure of the initial material. The crack depth at which the cyclic plastic zone size ahead of the crack tip will exceed the grain size should be considered as a criterion of the small-to-long crack transition. Under high-cycle fatigue conditions physically small fatigue crack growth will be divided into two phases of growth: the first phase is when the crack propagates along the slip planes of individual grains, and the second one is when the crack changes the mechanism of growth and propagates in the plane perpendicular to the loading direction. The model validity has been tested using the experimental data on the growth of the long cracks in specimens of titanium alloy VT3-1 in seven microstructural states and the small cracks in specimens of titanium alloy Ti–6Al–4V and aluminum alloy 2024-T3. Good agreement between the calculated and experimental results is obtained.