Study on material property changes of mild steel S355 caused by block loads with varying mean stress
Source abstract
Abstract
Abstract The paper presents the results of research on material property and structure changes of S355 steel samples induced by fatigue of material subjected to block bending loads, with varying mean load value. In the tests, the mean load was increased and decreased in subsequent blocks, where the amplitude varies in accordance with the accepted maximum bending moment value. The changes of strains recorded during the tests show higher maximum mean strain for the case, where the mean load increases in block. Otherwise, the maximum mean strain is three times less, than before. Some hardening occurs, which affects the mechanical properties of the material. This is visible in the results of tensile tests, where ultimate strength increases for load path with increased mean load value. Metallographic examinations revealed no fatigue cracks at this level of fatigue life.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · High Temperature Alloys and Creep · Fire effects on concrete materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Kocańda · 1989
2. Kocańda · 1989
3. Kocańda · 1985
4. On the description of transient cyclic hardening behaviour of mild steel CK 1510.1016/0749-6419(92)90054-G ↗
5. Work-hardening behaviour of mild steel under stress reversal at large strains10.1016/0749-6419(92)90006-X ↗
6. On the description of anisotropic workhardening10.1016/0022-5096(67)90030-0 ↗
7. A three dimensional models of anisotropic hardening in metals and its application to the analysis of sheet metal formability10.1016/0022-5096(84)90008-5 ↗
8. Armstrong PJ, Frederic CO. A mathematical representation of the multiaxial Bauschinger effect. Report RD/B/N 731. Central Electricity Generating Board; 1966.
9. A review of some plasticity and viscoplasticity constitutive theories10.1016/j.ijplas.2008.03.009 ↗
10. Ramberg W, Osgood WR. Description of stress–strain curves by three parameters. Technical Note No. 902. Washington DC: National Advisory Committee for Aeronautics; 1943.
11. Mroziński S., Stabilization of cyclic properties in metals and its influence on fatigue life, Monograph No.128. Bydgoszcz: Publishing House of University of Technology and Life Sciences; 2008. p. 148 (in Polish).
12. Böhm M, Niesłony A, Pawliczek R. Review of mean stress compensation models used in thedetermination of fatigue life of construction elements. A new trends in engineering science, Creativetime, Cracov 2012. p. 119–26.
13. Fatigue life of metallic material estimated according to selected models and load conditions
14. New energy model for fatigue life determination under multiaxial loading with different mean values10.1016/j.ijfatigue.2014.04.008 ↗
15. Influence of irregularity coefficient of loading on calculated fatigue life
16. Low cycle fatigue under tensile mean stresses where cyclic life extension occurs10.1016/S0142-1123(00)00098-0 ↗
17. Effect of mean strain level on the cyclic stress/strain behaviour of AISI 316 stainless steel10.1016/S0921-5093(03)00016-9 ↗
18. Fatigue life prediction of 3-D problems by damage mechanics with two-block loading
19. Pawliczek R, Lachowicz CT, The mean stress effect on fatigue behaviour of constructional steels subjected to variable amplitude bending. In: Sonsino CM, McKeighan PC, editor. 2nd International conference on material and component performance under variable amplitude loading, DVM, Berlin; 2009. p. 1095–102.
20. Pawliczek R., Trwałość zmęczeniowa próbek ze stali 18G2A w warunkach blokowych obciążeń zginających z wartością średnią (Fatigue life of specimens made of 18G2A steel subjected to bending block loads with mean value.). Zeszyty Naukowe Politechniki Opolskiej Nr 305/2005, Mechanika Z. 83, Opole; 2005. p. 167–74 [in Polish].
21. Pawliczek R., Influence of the mean value of the block loading on the shape of hysteresis loop for specimens made from S355 steel subjected to bending load. Przegląd Mechaniczny. No. 2l; 2013. p. 32–6 [in Polish].
22. Influence of the mean load value in fatigue block loading on strains10.4028/www.scientific.net/KEM.598.195 ↗