Source abstract
Abstract
Abstract A mesoscale fatigue progressive damage model (FPDM) is proposed for fatigue life prediction and failure behavior assessment of 3D woven composites (3DWC). The Hashin's fatigue criteria and the maximum tensile/shear stress criteria are used as damage activation criteria for the yarn and resin-rich matrix, respectively. A fatigue damage evolution model is developed based on Fang's static-load damage evolution model, where the damage irreversibility and compressive crack closure effect are considered. The UserMat subroutine and APDL language in ANSYS are employed to implement the fatigue process of 3DWC. The results show that all predicted fatigue lives are within two-fold error band.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Textile materials and evaluations · Additive Manufacturing and 3D Printing Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (65)
Show source-provided references
1. Fatigue of textile composites
2. A review of numerical models for 3D woven composite reinforcements10.1016/j.compstruct.2018.10.085 ↗
3. Compression after multiple low velocity impacts of NCF, 2D and 3D woven composites10.1016/j.compositesa.2019.105576 ↗
4. Experimental Investigation on the Shear Properties and Failure Mechanism of 3D MWK Glass/Epoxy Composites under Compressive Loading10.1007/s12221-020-9312-2 ↗
5. Fabrication, properties and failure of 3D stitched carbon/epoxy composites with no stitching fibers damage10.1016/j.compstruct.2019.03.080 ↗
6. Tensile performance of basalt fiber composites with open circular holes and straight notches10.1016/j.ijmecsci.2020.105517 ↗
7. On the effects of temperature on tensile behavior of carbon fiber reinforced epoxy laminates10.1016/j.tws.2021.107769 ↗
8. Multi-scale damage modelling of 3D woven composites under uni-axial tension10.1016/j.compstruct.2016.01.103 ↗
9. Multi-scale progressive failure simulation of 3D woven composites under uniaxial tension10.1016/j.compstruct.2018.09.081 ↗
10. Progressive damage modelling and experimental investigation of three-dimensional orthogonal woven composites with tilted binder10.1177/1528083718821888 ↗
11. Finite Element Analysis of Mesh Size Effect of 3D Angle-Interlock Woven Composites Using Voxel-Based Method10.1007/s10443-018-9723-z ↗
12. Progressive damage investigation of 2.5D woven composites under quasi-static tension10.1007/s00707-017-2024-z ↗
13. Experimental and numerical investigation of mechanical behaviors of 2.5D woven composites at ambient and un-ambient temperatures10.1016/j.compstruct.2018.06.054 ↗
14. Finite Element Analysis of Warp-Reinforced 2.5D Woven Composites Based on a Meso-Scale Voxel Model under Compression Loading10.1007/s10443-016-9565-5 ↗
15. Experimental and numerical investigation on the thermal conduction properties of 2.5D angle-interlock woven composites10.1016/j.compstruct.2016.07.071 ↗
16. Multi-scale Analyses of 3D Woven Composite Based On Periodicity Boundary Conditions10.1177/0021998306069891 ↗
17. Meso-scale finite element analyses of three-dimensional five-directional braided composites subjected to uniaxial and biaxial loading10.1177/0731684415596629 ↗
18. Tensile Performance and Damage Evolution of a 2.5-D C/SiC Composite Characterized by Acoustic Emission10.1007/s10443-008-9066-2 ↗
19. Off-axis bending behaviors and failure characterization of 3D woven composites10.1016/j.compstruct.2018.10.009 ↗
20. Effects of off-axis angle on shear progressive damage of 3D woven composites with X-ray micro-computed tomography10.1016/j.compositesa.2018.10.007 ↗
21. Damage Evolution of 3D Woven Carbon/Epoxy Composites under Tension-Tension Fatigue Loading Based on Synchrotron Radiation Computed Tomography (SRCT)10.1016/j.ijfatigue.2020.105913 ↗
22. Experimental method and failure mechanisms investigation for out-of-plane shear fatigue behavior of 3D woven composites10.1016/j.ijfatigue.2020.105501 ↗
23. Damage analysis of 2.5D C/C-SiC composites subjected to fatigue loadings10.1016/j.jeurceramsoc.2019.01.014 ↗
24. Fatigue behavior of the 3D orthogonal carbon/glass fibers hybrid composite under three-point bending load10.1016/j.matdes.2019.108112 ↗
25. Fatigue life prediction of a woven fabric composite subjected to biaxial cyclic loads10.1016/S1359-835X(01)00091-4 ↗
26. Experimental Techniques for Evaluation of Fatigue Characteristics of Laminated Constructions from Composite Materials: Full-Scale Testing of the Helicopter Rotor Blades10.1520/JTE102768 ↗
27. An Experimental Methodology for Evaluating Survivability of an Aeronautical Constructions from Composite Materials: An Overview10.1533/ijcr.2006.0135 ↗
28. Numerical Modeling of Nomex Honeycomb Core Composite Plates at Meso Scale Level10.5937/fme2004874D ↗
29. Chapter 2: Use of Modern Numerical Methods for Fatigue Life Predictions
30. Review of impact damages modelling in laminated composite aircraft structures
31. Beaumont · 2015
32. Zweben · 2018
33. Fatigue damage modeling of fibre-reinforced composite materials: Review10.1115/1.1381395 ↗
34. Fatigue Damage Mechanism Characterization and Modeling of a Woven Graphite/Epoxy Composite10.1106/YNR6-XVQP-QU7C-XNG3 ↗
35. On modelling the mechanical degradation of fatigue loaded glass-fibre non-crimp fabric reinforced epoxy laminates10.1016/j.compscitech.2005.07.037 ↗
36. Damage evolution of novel 3D textile-reinforced composites under fatigue loading conditions10.1016/j.compscitech.2009.10.010 ↗
37. Fatigue behaviors of four-step three-dimensional braided composite material: a meso-scale approach computation10.1177/0040517514540767 ↗
38. Computational schemes on the bending fatigue deformation and damage of three-dimensional orthogonal woven composite materials10.1016/j.commatsci.2014.04.052 ↗
39. Nonlinear numerical predictions of three-dimensional orthogonal woven composite under low-cycle tension using multiscale repeating unit cells10.1177/1056789514532667 ↗
40. Computational analysis of fatigue behavior of 3D 4-directional braided composites based on unit cell approach10.1016/j.advengsoft.2014.12.007 ↗
41. A progressive damage model of textile composites on meso-scale using finite element method: Fatigue damage analysis10.1016/j.compstruc.2015.02.005 ↗
42. Fatigue life prediction method of 2.5 dimensional woven composites
43. Fatigue behaviors of 2.5D woven composites at ambient and un-ambient temperatures10.1016/j.compstruct.2017.01.055 ↗
44. Fatigue life prediction model of 2.5D woven composites at various temperatures10.1016/j.cja.2017.12.006 ↗
45. Warp direction fatigue behavior and damage mechanisms of centrally notched 2.5D woven composites at room and elevated temperatures10.1016/j.compscitech.2019.107769 ↗
46. Weft direction tension-tension fatigue responses of layer-to-layer 3D angle-interlock woven composites at room and elevated temperatures10.1016/j.ijfatigue.2020.105770 ↗
47. Meso-scale progressive damage modeling and life prediction of 3D braided composites under fatigue tension loading10.1016/j.compstruct.2018.06.021 ↗
48. Multi-scale damage mechanics method for predicting fatigue life of plain-braided C/SiC composites10.1016/j.compstruct.2020.112860 ↗
49. A continuum damage model for composite laminates: Part III - Fatigue10.1016/j.mechmat.2020.103659 ↗
50. Investigation on the compressive properties of the three dimensional four-directional braided composites10.1016/j.compstruct.2010.09.002 ↗
51. Multi-scale finite element analysis of 2.5D woven fabric composites under on-axis and off-axis tension10.1016/j.commatsci.2013.07.003 ↗
52. Review on the fatigue properties of 3D woven fiber/epoxy composites: testing and modelling strategies
53. Effect of apertures on tensile property of warp-reinforced 2.5D woven composites notched plates10.1016/j.compstruct.2020.112693 ↗
54. Effect of bias yarn on tensile fracture mechanism of multiaxial 3D angle-interlock woven composites10.1016/j.tws.2020.107269 ↗
55. Failure criteria of unidirectional carbon fiber reinforced polymer composites informed by a computational micromechanics model10.1016/j.compscitech.2019.01.012 ↗
56. Failure Criteria for Unidirectional Fiber Composites10.1115/1.3153664 ↗
57. Fatigue Failure Criteria for Unidirectional Fiber Composites10.1115/1.3157744 ↗
58. Crack band theory for fracture of concrete10.1007/BF02486267 ↗
59. Prediction of Remaining Fatigue Cycles in Composite Materials Under Uncertainty
60. Strain-based theoretical fatigue damage model of woven glass-epoxy fabric composite material
61. Mechanical modeling of material damage10.1115/1.3173673 ↗
62. G D, L LJ. Les inequations en me canique et en physique. Paris: Dunod; 1972.
63. Investigation of mechanical properties for 2.5D woven composites with different weft-layer-numbers by a triple-cell model system
64. Effect of Stress Ratio on Fatigue Behaviour of Non-Crimp Fabric Composites at Room and Elevated Temperatures10.1007/s10443-020-09817-3 ↗
65. A microscale energy-based fatigue damage model for unidirectional composites under multiaxial loading at different stress ratios10.1016/j.engfracmech.2018.11.024 ↗