A natural frequency degradation model for very high cycle fatigue of woven fiber reinforced composite
Source abstract
Abstract
Abstract Based on the matrix crack density evolution, a theoretical model is proposed to study the natural frequency degradation of woven fabric composite subjected to very high cycle vibration loading. A very high cycle bending fatigue test of woven fabric composite is designed, and the existence of crack saturated state is verified. An on-line natural frequency measurement test is proposed, which proved the validity of the proposed natural frequency degradation model.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Textile materials and evaluations · Structural Analysis and Optimization
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. A model of the fatigue life distribution of composite laminates based on their static strength distribution10.1016/S1000-9361(08)60031-X ↗
2. Adams RDEA. Vibration testing as a nondestructive test tool for composite materials. In: Adams RD, et al. (Eds.) Conference on Composite Reliability, ASTM STP 580 (American Society for Testing and Materials, 1975) pp. 159–175, Vol. 7(3). 1976. p. 203.10.1520/STP32306S ↗
3. Effect of fatigue loading on the modal properties of composite structures and its utilization for prediction of residual life10.1016/S0263-8223(97)00028-7 ↗
4. Natural-frequency reduction model for matrix-dominated fatigue damage of composite laminates10.1016/S0263-8223(03)00080-1 ↗
5. A study on the change between tensile loading and natural frequency of carbon-carbon composite materials
6. Prediction of fatigue life of glass fiber reinforced polyester composites using modal testing10.1016/j.ijfatigue.2012.10.002 ↗
7. Fatigue testing of CFRP in the Very High Cycle Fatigue (VHCF) regime at ultrasonic frequencies10.1016/j.compscitech.2014.10.020 ↗
8. Ultrasonic fatigue and microstructural characterization of carbon fiber fabric reinforced polyphenylene sulfide in the very high cycle fatigue regime10.1016/j.compscitech.2016.02.020 ↗
9. Stiffness reduction of woven CFRP and CFRTP spring under ultra high cyclic fatigue for vibration conveyor10.4028/www.scientific.net/AMR.123-125.217 ↗
10. High-cycle fatigue characteristics of quasi-isotropic CFRP laminates over 10 cycles (Initiation and propagation of delamination considering interaction with transverse cracks)10.1016/j.ijfatigue.2009.02.028 ↗
11. Fatigue performance of wind turbine blade composite materials
12. Experimental investigation of the very high cycle fatigue of GFRP [90/0]s cross-ply specimens subjected to high-frequency four-point bending10.1016/j.compscitech.2014.06.023 ↗
13. Fatigue strength of carbon fibre composites up to the gigacycle regime (gigacycle-composites)10.1016/j.ijfatigue.2005.05.005 ↗
14. Fatigue testing of carbon fibre reinforced polymers under VHCF loading10.1016/j.mspro.2013.02.003 ↗
15. Transverse crack growth behavior considering free-edge effect in quasi-isotropic CFRP laminates under high-cycle fatigue loading10.1016/j.compscitech.2008.09.003 ↗
16. A VHCF life prediction method based on surface crack density for FRP
17. Talreja RR. Fatigue of Composite Materials. Taylor and Francis.
18. Transverse cracking and stiffness reduction in composite laminates
19. Transverse cracking and stiffness reduction in composite laminates10.1177/073168449301200905 ↗
20. Synergistic damage mechanic model for stiffness properties of early fatigue damage in composite laminates ☆
21. Multi-directional stiffness degradation induced by matrix cracking in composite laminates10.1016/S0142-1123(01)00066-4 ↗
22. Damaged mosaic laminate model of woven fabric composites with transverse yarn cracking and interface debonding10.1016/S0266-3538(02)00101-X ↗
23. Modeling of tensile fatigue damage in resin transfer molded woven carbon fabric composites10.1016/S1359-835X(02)00109-4 ↗