Influence of work-hardening on fatigue crack growth, effective threshold and crack opening behavior in the nickel-based superalloy Inconel 718
Source abstract
Abstract
Abstract In this study, the influence of rotary swaging induced cold work on long fatigue crack growth, threshold and opening behavior in the nickel-based superalloy Inconel 718 was investigated. Ambient temperature experiments were carried out using arc-shaped tension specimens according to ASTM standard E399. The direct current potential drop (DCPD) method was used for crack length measurements and crack opening force evaluation. Fatigue crack growth rates (FCGR) measured at load ratios of R = 0.2 , R = 0.5 and R = 0.7 were found to increase due to work-hardening in continuous (increasing Δ K ) and load shedding (decreasing Δ K ) tests. Effective fatigue crack growth thresholds ( Δ K th , eff ) were determined according to the K max = const . procedure and found to decrease monotonically with increasing degree of work-hardening. Compared to the non-deformed material, crack opening stress intensities K op were reduced in work-hardened states at three different crack lengths. To quantify the detrimental effects of cold work, the effective stress intensity factor range ( Δ K eff ) model was applied. SEM and TEM micrographs were taken to complement the study.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · High Temperature Alloys and Creep · Aluminum Alloy Microstructure Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (42)
Show source-provided references
1. Schulze · 2006
2. Surface modification by machine hammer peening and burnishing10.1016/j.cirp.2016.05.005 ↗
3. A literature survey on the stability and significance of residual stresses during fatigue10.1111/j.1460-2695.2007.01102.x ↗
4. Stress intensity factors, crack profiles, and fatigue crack growth rates in residual stress fields
5. Fatigue crack closure: observations and technical significance
6. The significance of fatigue crack closure
7. Near-threshold fatigue crack growth behavior in copper10.1007/BF02644801 ↗
8. The role of dislocation substructures in fatigue crack propagation in copper and alpha brass10.1007/BF02811733 ↗
9. The effect of pre-stress cycles on fatigue crack growth–an analysis of crack growth mechanism10.1016/0013-7944(74)90062-9 ↗
10. The effect of pre-strain on fatigue crack growth and crack closure10.1016/0013-7944(76)90031-X ↗
11. Influence of monotonic and cyclic predeformation on fatigue crack propagation of high-strength aluminum alloys10.1016/0013-7944(80)90031-4 ↗
12. Fatigue crack growth analysis of pre-strained 7475–T7351 aluminum alloy10.1016/j.ijfatigue.2005.09.008 ↗
13. Effect of grain size and cold work on the near threshold fatigue crack propagation rate and crack closure in iron10.1016/0036-9748(82)90477-X ↗
14. An investigation of the effect of pre-straining on fatigue crack growth10.1016/0025-5416(75)90237-2 ↗
15. Effect of prestrain on fatigue crack propagation in mild steel containing non-metallic inclusions10.1016/0013-7944(88)90007-0 ↗
16. Effect of monotonic and cyclic prestrain on the fatigue threshold in medium-carbon steels10.1016/0142-1123(92)90152-3 ↗
17. Influence of prestrain and ageing on near-threshold fatigue crack growth in fine-grained dual-phase steels10.1016/0142-1123(89)90178-3 ↗
18. The influence of microstructural morphology and prestrain on fatigue crack propagation of dual-phase steels in the near-threshold region10.2355/isijinternational.39.486 ↗
19. Influence of microstructural morphology and prestraining on short fatigue crack propagation in dual-phase steels10.2355/isijinternational.41.298 ↗
20. Fatigue-crack growth in 20% cold-worked type 316 stainless steel at elevated temperatures10.13182/NT72-A31197 ↗
21. Crack propagation in cold-worked austenitic stainless steel at elevated temperatures10.13182/NT78-A32039 ↗
22. Effect of single plastic prestraining on crack resistance. 2. An approach to predicting the fatigue crack growth rate10.1007/BF01528957 ↗
23. Role of microstructures on the growth of long fatigue cracks10.1016/S0142-1123(97)00027-3 ↗
24. The influence of metallurgical structure on the mechanisms of fatigue crack propagation
25. The effect of prestraining on fatigue crack growth in nickel-base alloys
26. Influence of prestraining on high temperature, low frequency fatigue crack growth in superalloys10.1016/0921-5093(93)90470-Y ↗
27. Effect of frequency on fatigue crack growth rate of Inconel 718 at high temperature
28. Plastic zone near a crack and fracture toughness
29. Experimental and numerical investigation of crack closure measurements with electrical potential drop technique10.1016/j.ijfatigue.2005.11.005 ↗
30. Analysis of fatigue crack closure and thresholds
31. A critical analysis of crack propagation laws10.1115/1.3656900 ↗
32. Frequency and wave-form effects on the fatigue crack growth behavior of alloy 718 at 298 K and 823 K10.1007/BF02646402 ↗
33. Effects of compressive residual stress on short fatigue crack growth in a nickel-based superalloy10.1016/j.ijfatigue.2017.11.010 ↗
34. Microstructural effects on fatigue crack growth in a low carbon steel10.1007/BF02697075 ↗
35. Crack closure under high load-ratio conditions for Inconel-718 near threshold behavior10.1016/j.engfracmech.2008.09.009 ↗
36. Some considerations on fatigue crack closure at near-threshold stress intensities due to fracture surface morphology10.1007/BF02642409 ↗
37. Effect of heat-treatment and heat-to-heat variations in the fatigue-crack growth response of Alloy 71810.1016/0013-7944(85)90109-2 ↗
38. Effects of Kmax on fatigue crack growth threshold in aluminum alloys
39. Investigation of an abnormality in fatigue crack growth curves-the Marci effect10.1016/S1359-6462(98)00120-1 ↗
40. Low cycle fatigue behavior of Inconel 718 at 298 K and 823 K10.1007/BF02667395 ↗
41. Shearing of γ precipitates and formation of planar slip bands in Inconel 718 during cyclic deformation10.1016/j.scriptamat.2004.11.023 ↗
42. Effect of precipitation condition, prestrain and temperature on the fatigue behaviour of wrought nickel-based superalloys in the VHCF range10.1016/j.actamat.2011.05.005 ↗