Effect of low temperature on fatigue crack formation and microstructure-scale propagation in legacy and modern Al–Zn–Mg–Cu alloys
Source abstract
Abstract
Abstract Temperature dependence of fatigue crack formation and microstructure-scale growth from constituent particles in 7075-T651 and 7050-T7451 is quantified via load induced fracture surface marker-bands. Larger and more abundant particles in 7075-T651 lead to increased crack formation frequency and decreased life. Crack growth rates are similar between alloys and decreased with decreasing temperature, paralleling crack formation behavior. The temperature dependence is attributed to hydrogen environment embrittlement, but is not sufficiently understood to fully model the observed behavior.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Aluminum Alloy Microstructure Properties · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (66)
Show source-provided references
1. A structural integrity prognosis system10.1016/j.engfracmech.2008.09.007 ↗
2. Typical fatigue-initiating discontinuities in metallic aircraft structures10.1016/j.ijfatigue.2011.10.017 ↗
3. National Oceanic and Atmospheric Administration. US standard atmosphere. Washington (DC); 1976.
4. Scientific advances enabling next generation management of corrosion induced fatigue10.1016/j.proeng.2011.04.062 ↗
5. Wanhill · 2001
6. Environment sensitive fatigue crack tip processes and propagation in aerospace aluminum alloys
7. Environmentally assisted fatigue in the gaseous atmosphere
8. Wei · 2010
9. Effect of loading environment on fatigue crack formation and microstructurally small fatigue propagation in Al–Zn–Mg–Cu
10. Fatigue crack propagation in an aluminium alloy at 223K10.1016/j.scriptamat.2005.08.036 ↗
11. The effect of clamping compressive stresses on the fatigue life of Al 7075-T6 bolted plates at different temperatures10.1016/j.matdes.2011.07.073 ↗
12. Factors influencing stage I fatigue crack propagation in age-hardened alloys
13. Driving forces for localized corrosion-to-fatigue crack transition in Al–Zn–Mg–Cu10.1111/j.1460-2695.2011.01568.x ↗
14. Fatigue crack surface crystallography near crack initiating particle clusters in precipitation hardened legacy and modern Al–Zn–Mg–Cu alloys10.1016/j.ijfatigue.2011.01.018 ↗
15. Effect of initiation feature on microstructurally small fatigue crack propagation in Al–Zn–Mg–Cu10.1016/j.ijfatigue.2011.08.001 ↗
16. A geometric approach to modeling microstructurally small fatigue crack formation: I. Probabilistic simulation of constituent particle cracking in AA 7075-T65110.1088/0965-0393/16/6/065007 ↗
17. A geometric approach to modeling microstructurally small fatigue crack formation: II. Physically based modeling of microstructure-dependent slip localization and actuation of the crack nucleation mechanism in AA 7075-T65110.1088/0965-0393/18/4/045004 ↗
18. A geometric approach to modeling microstructurally small fatigue crack formation: III. Development of a semi-empirical model for nucleation10.1088/0965-0393/19/3/035008 ↗
19. Observations of fatigue crack initiation in 7075-T65110.1016/j.ijfatigue.2009.06.003 ↗
20. Papazian · 2009
21. ASTM, E466-07 · 2007 · vol. 3
22. Wiederhold · 1997
23. Hertzberg · 1996
24. Fatigue as a process of cyclic brittle microfracture10.1111/j.1460-2695.2005.00857.x ↗
25. The role of air in fatigue load interaction10.1046/j.1460-2695.2003.00582.x ↗
26. Equivalent initial flaw size testing and analysis of transport aircraft skin splices10.1046/j.1460-2695.2003.00637.x ↗
27. A simplified laboratory approach for the prediction of short crack behavior in engineering structures10.1111/j.1460-2695.1988.tb01183.x ↗
28. In situ SEM observations of the contrasting effects of an overload on small fatigue crack growth at two different load ratios in 2024-T351 aluminium alloy10.1016/S0142-1123(97)00010-8 ↗
29. Effect of corrosion severity on fatigue evolution in Al–Zn–Mg–Cu10.1016/j.corsci.2009.10.006 ↗
30. Dowling · 1999
31. Statistical analysis of constituent particles in 7075-T6 aluminum alloy10.1007/BF02586171 ↗
32. A probability model for the growth of corrosion pits in aluminum alloys induced by constituent particles10.1016/S0013-7944(97)00127-6 ↗
33. Characterizations of pore and constituent particle populations in 7050-T7451 aluminum plate alloys10.1007/s11661-998-0263-2 ↗
34. Microstructure-sensitive computational modeling of fatigue crack formation10.1016/j.ijfatigue.2010.01.003 ↗
35. High- and low-cycle fatigue crack initiation using polycrystal plasticity10.1098/rspa.2003.1258 ↗
36. The effect of constituent particles in aluminum alloys on fatigue damage evolution: statistical observations10.1016/j.ijfatigue.2009.02.036 ↗
37. Roles of microstructure in fatigue crack initiation10.1016/j.ijfatigue.2009.10.005 ↗
38. Modeling damage mechanisms in hydrogen embrittlement
39. The effect of hydrogen on dislocation dynamics10.1016/S0013-7944(01)00011-X ↗
40. Whitney award lecture 1987 – hydrogen – the versatile embrittler10.5006/1.3583875 ↗
41. Environmental fatigue-crack surface crystallography for Al–Zn–Cu–Mg–Mn/Zr10.1007/s11661-008-9522-5 ↗
42. Relevance of the small crack problem to lifetime prediction in gas-turbines10.1016/0142-1123(87)90049-1 ↗
43. A model of initial flaw sizes in aluminum alloys10.1016/S0142-1123(01)00122-0 ↗
44. Characterisation of equivalent initial flaw sizes in 7050 aluminium alloy10.1111/j.1460-2695.2006.01050.x ↗
45. Effects of hardness and crack geometries on DKTH of small crack emanating from small defects
46. Fatigue life prediction from inclusion initiated cracks10.1016/S0142-1123(97)00136-9 ↗
47. Predicting fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests10.1016/j.ijfatigue.2003.10.010 ↗
48. The EIFS distribution for anodized and pre-corroded 7010-T7651 under constant amplitude loading10.1111/j.1460-2695.2005.00912.x ↗
49. Microstructural aspects of crack nucleation during cyclic loading of AA7075-T65110.1016/j.engfracmech.2008.11.012 ↗
50. Three-dimensional finite element analysis using crystal plasticity for a parameter study of microstructurally small fatigue crack growth in a AA7075 aluminum alloy10.1016/j.ijfatigue.2008.03.027 ↗
51. The effect of porosity on the fatigue life of cast aluminium–silicon alloys10.1111/j.1460-2695.2004.00780.x ↗
52. Micromechanisms of multistage fatigue crack growth in a high-strength aluminum alloy10.1016/j.actamat.2006.11.009 ↗
53. Stress-intensity factor equations for cracks in three-dimensional finite bodies subjected to tension and bending loads
54. Small crack growth and fatigue life predictions for high-strength aluminium alloys. Part I: Experimental and fracture mechanics analysis10.1046/j.1460-2695.1998.00080.x ↗
55. Modeling microstructurally sensitive fatigue short crack growth10.1098/rspa.1994.0131 ↗
56. Fitting conic sections to scattered data
57. Environment-exposure-dependent fatigue crack growth kinetics for Al–Cu–Mg/Li10.1016/j.msea.2007.01.155 ↗
58. Fatigue crack formation and growth from localized corrosion in Al–Zn–Mg–Cu10.1016/j.engfracmech.2008.11.005 ↗
59. Boyer · 1986
60. Li D, Burns JT, Bush RW, Garratt M, Hinkle AJ, Mills T, et al. Characterization of corrosion-fatigue interaction for aluminum alloy substitution. In: Young RD, editor. 8th Joint NASA/FAA/DoD conference on aging aircraft; 2006.
61. Environmentally assisted fatigue-crack growth in 7075 and 7050 aluminum-alloys10.1016/0036-9748(85)90310-2 ↗
62. Corrosion fatigue crack propagation in metals
63. Chemical and metallurgical aspects of environmentally assisted fatigue crack-growth in 7075-T651 aluminum-alloy10.1007/BF02645142 ↗
64. Critical issues in hydrogen assisted cracking of structural alloys
65. Environmental considerations for fatigue cracking10.1046/j.1460-2695.2002.00551.x ↗
66. Hydrogen embrittlement and environmentally assisted crack growth