AFM and SEM-FEG study on fundamental mechanisms leading to fatigue crack initiation
Source abstract
Abstract
Abstract Early stages of surface relief evolution of persistent slip markings (PSMs) in polycrystalline 316L austenitic stainless steel cycled with constant plastic strain amplitude at 93, 173 and 573 K were studied using atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM-FEG). Qualitative and quantitative data on the morphology of PSMs, occurrence of extrusions and intrusions and the kinetics of extrusion growth are reported for all temperatures. PSMs start in all cases as surface extrusions which are later accompanied by formation of intrusions. This finding is discussed with respect to the point defect formation within areas of localized cyclic slip and primarily to their mobility at different temperatures. Consequences of migration of respective point defects for surface relief formation and the conditions for creation of fatigue crack embryos, i.e. sharp intrusions are highlighted.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Microstructure and Mechanical Properties of Steels · High Temperature Alloys and Creep · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (53)
Show source-provided references
1. Fatigue crack initiation by cyclic slip irreversibilities in high-cycle fatigue
2. Fatigue
3. Dislocations in fatigue
4. Basinski · Prog Mater Sci · 1992 · 36 · 8910.1016/0079-6425(92)90006-S ↗
5. Fatigue
6. Fatigue crack initiation mechanisms
7. Cyclic deformation, crack initiation, and low-cycle fatigue
8. Extrusions and intrusions in fatigued metals. Part 1. State of the art and history10.1080/14786430902917616 ↗
9. Some comments about fatigue crack initiation in relation to cyclic slip irreversibility10.1016/j.engfracmech.2007.04.014 ↗
10. Cyclic slip irreversibilities and the evolution of fatigue damage10.1007/s11661-009-9839-8 ↗
11. Evolution of slip morphology and fatigue crack initiation in surface grains of Ni20010.1007/s11661-009-9980-4 ↗
12. Fatigue, an averlasting material problem – still an vogue10.1016/j.proeng.2010.03.003 ↗
13. The effect of grain size on the localization of plastic deformation in shear bands10.1016/j.scriptamat.2011.09.001 ↗
14. On the formation of vacancies by edge dislocation dipole annihilation in fatigued copper10.1016/j.ijfatigue.2011.05.004 ↗
15. A physically based fatigue model for prediction of crack initiation from persistent slip bands in polycrystals10.1016/j.actamat.2010.09.036 ↗
16. The physics of fatigue crack initiation10.1016/j.ijfatigue.2012.10.009 ↗
17. Cracks and extrusions by persistent slip band10.1080/14786435.2013.798048 ↗
18. A model of extrusions and intrusions in fatigued metals. I. Point-defect production and the growth of extrusions10.1080/01418618108239541 ↗
19. On the role of point defects in fatigue crack initiation10.1016/0025-5416(87)90157-1 ↗
20. Growth of extrusions in localized cyclic plastic straining10.1016/j.msea.2008.09.022 ↗
21. Mechanisms of extrusion and intrusion formation in fatigued crystalline materials10.1016/j.msea.2013.12.005 ↗
22. LCF mechanisms of the 25Cr7Ni0.25N duplex stainless steel investigated by atomic force microscopy10.3139/120.110045 ↗
23. Extrusions and intrusions in fatigued metals. Part 2. AFM and EBSD study of the early growth of extrusions and intrusions in 316L steel fatigued at room temperature10.1080/14786430902917624 ↗
24. Fatigue behavior of high-Mn TWIP steels10.1016/j.msea.2009.03.039 ↗
25. The shape of extrusions and intrusions and initiation of stage I fatigue cracks10.1016/j.msea.2009.03.070 ↗
26. Study of cyclic strain localization and fatigue crack initiation using FIB technique10.1016/j.ijfatigue.2011.05.002 ↗
27. Quantitative study of surface roughness evolution during low-cycle fatigue of 316L stainless steel using Scanning Whitelight Interferometric (SWLI) microscopy10.1016/j.ijfatigue.2012.11.009 ↗
28. The shape of early persistent slip markings in fatigued 316L steel10.1016/j.msea.2012.11.086 ↗
29. Influence of the crystalline orientations on microcrack initiation in low-cycle fatigue10.1016/j.msea.2013.02.046 ↗
30. Extrusion and intrusion by cyclic slip in copper10.1098/rspa.1957.0170 ↗
31. Surface structure of slip bands on copper fatigued at 293°, 90°, 20°, and 4.2°K
32. Fatigue damage in copper single crystals at room and cryogenic temperatures10.1016/0001-6160(89)90328-3 ↗
33. Microstructural studies on the initiation and growth of small fatigue cracks at 298, 77 and 4.2K in polycrystalline copper10.1016/0001-6160(89)90327-1 ↗
34. Copper single crystal PSB morphology between 4.2 and 350 K10.1016/0001-6160(89)90199-5 ↗
35. Direct measurement of the rate of extrusion growth in fatigued copper mono- and polycrystals
36. The formation of either tongue- or ribbon-like extrusions in fatigued copper polycrystals10.1016/0956-7151(91)90252-V ↗
37. Study of surface relief evolution in fatigued 316L austenitic stainless steel by AFM10.1016/S0921-5093(02)00846-8 ↗
38. AFM study of surface relief evolution in 316L steel fatigued at low and high temperatures10.1016/j.proeng.2010.03.175 ↗
39. Cyclic stress in 316L austenitic stainless steel at low temperatures10.4028/www.scientific.net/MSF.567-568.401 ↗
40. AFM evidence of surface relief formation and models of fatigue crack nucleation10.1016/S0142-1123(03)00114-2 ↗
41. Dislocation structures in fatigued Cu–Zn single crystals10.1002/pssb.19700370234 ↗
42. Cyclic deformation behavior of Cu–30wt% Zn single crystals oriented for single slip. I. Cyclic deformation response and slip band behavior10.1016/S1359-6454(98)00302-4 ↗
43. Persistent slipbands in fatigued face-centered and body-centered cubic metals
44. Low energy dislocation structures produced by cyclic deformation10.1016/0025-5416(86)90281-8 ↗
45. Imperfection density of fatigued and annealed copper via electrical resistivity measurements
46. Electrical resistivity of cyclically deformed copper10.1007/BF01712868 ↗
47. Study of fatigue in copper by resistometric method
48. Electrical resistivity of fatigued copper crystals10.1016/0001-6160(89)90200-9 ↗
49. Surface topography and crack initiation in emerging persistent slip bands in copper single crystals10.1016/0025-5416(85)90112-0 ↗
50. Defect recovery in irradiated high-purity austenitic Fe–Cr–Ni alloys: activation energies and dependence on initial defect concentration10.1016/0022-3115(82)90450-0 ↗
51. Dislocation structures in 316L stainless steel cycled with plastic strain amplitudes over a wide interval10.1016/0921-5093(94)90325-5 ↗
52. Overview of fatigue behavior in copper single crystals – I. Surface morphology and stage I crack initiation sites for tests at constant strain amplitude10.1016/0001-6160(89)90217-4 ↗
53. Fatigue crack initiation – the role of point defects10.1016/j.ijfatigue.2013.10.016 ↗