Effects of residual stresses on fatigue crack growth behavior of structural materials: Analytical corrections
Source abstract
Abstract
Abstract Fatigue crack growth data developed to characterize a material can be significantly biased by the presence of bulk residual stresses introduced during material processing and subsequent fabrication of test samples. Residual stresses influence fatigue crack growth behavior and change the measured material response to dynamic loading. Correction to experimental data generated in the presence of residual stresses is necessary to produce accurate fatigue crack growth data for modeling and life prediction. This study proposes an analytical technique to correct fatigue crack growth data acquired in the presence of residual stresses. The technique was calibrated with multiple structural materials and multiple stress ratios, and found to produce good agreement between corrected data generated in residual stresses and data generated in minimal residual stresses.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Mechanical Behavior of Composites · Ultrasonics and Acoustic Wave Propagation
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Glinka G. Effect of residual stresses on fatigue crack growth in steel weldments under constant and variable amplitude loads. ASTM STP 677; 1979. p. 198–214.10.1520/STP34914S ↗
2. Stress intensity factors, crack profiles, and fatigue crack growth rates in residual stress fields10.1520/STP30095S ↗
3. Effects of residual stress on fatigue crack propagation10.1520/STP30104S ↗
4. The effect of residual stress and its redistribution on fatigue crack growth10.1016/0167-8442(89)90015-3 ↗
5. Fatigue crack propagation through residual stress fields with closure phenomena10.1016/0013-7944(90)90285-O ↗
6. An elastic–plastic analytical model for predicting fatigue crack growth in arbitrary edge-cracked two-dimensional geometries with residual stress10.1016/0142-1123(94)90102-3 ↗
7. Effect of residual stress on fatigue crack growth rate measurement10.1520/STP28789S ↗
8. The effect of residual stress on the fatigue crack growth behavior of Al–Si–Mg cast alloys – mechanisms and corrective mathematical models10.1007/s11661-006-0159-y ↗
9. Fatigue crack growth affected by metal fragments wedged between opening-closing crack surfaces
10. Fatigue crack closure under cyclic tension10.1016/0013-7944(70)90028-7 ↗
11. Fatigue-life prediction methodology using a crack-closure model10.1115/1.2804736 ↗
12. Near-threshold fatigue crack propagation: a perspective on the role of crack closure
13. Donald · 1948 · 674
14. Contribution of the cyclic loading portion below the opening load to fatigue crack growth10.1016/0921-5093(95)10079-2 ↗
15. Service load fatigue damage – a historical perspective10.1016/S0142-1123(99)00054-7 ↗
16. A method of mapping residual stress in a compact tension specimen10.1016/0036-9748(88)90004-X ↗
17. Determination of residual stress distributions from measured stress intensity factor10.1007/BF00036266 ↗
18. Measuring residual stress and the resulting stress intensity factor in compact tension specimens10.1046/j.1460-2695.1999.00155.x ↗
19. Fett · 1997
20. Fracture mechanics analysis for residual stress and crack closure corrections10.1016/j.ijfatigue.2006.07.002 ↗
21. The effect of residual stress on the fatigue crack growth behavior of Al–Si–Mg cast alloys – mechanisms and corrective mathematical models10.1007/s11661-006-0159-y ↗
22. American Society for Testing and Materials, Standard test method for measurement of fatigue crack growth rates designation E647-05; 2005.
23. Irwin GR. Plastic zone near a crack and fracture toughness. In: Proceedings 7th Sagamore conference, vol. 4; 1961. p. 63–76.
24. Yielding of steel sheets containing slits10.1016/0022-5096(60)90013-2 ↗
25. Limitations of elastic definitions in Al–Si–Mg cast alloys with enhanced plasticity: linear elastic fracture mechanics versus elastic–plastic fracture mechanics10.1016/j.engfracmech.2005.08.010 ↗
26. American Society for Testing and Materials, Standard test methods for tension testing of metallic materials designation E8-09; 2009.
27. Donald JK, Bray GH, Bush RW. An evaluation of the adjusted compliance ratio technique for determining the effective stress intensity factor, American Society for Testing and Materials, ASTM STP 1332; 1998. p. 674–95.10.1520/STP14977S ↗