Fatigue life evaluation of adhesively bonded scarf joints
Source abstract
Abstract
Abstract The fatigue life of adhesively bonded scarf joints with various scarf angles was analyzed experimentally in this study. Experimental results indicate that the fatigue strength increases significantly with the scarf angle of the studied specimen. The main failure modes for the specimens with small and large scarf angles are adhesive and cohesive, respectively. Additionally, the finite element method was employed to obtain the stress states within the studied scarf joint specimens, and the fatigue data of specimens with 0°/30° scarf angles and 45°/60° scarf angles were successfully correlated using the interfacial peeling stress parameter and the von Mises stress within the adhesive, respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Mechanical Behavior of Composites · Fatigue and fracture mechanics · Electronic Packaging and Soldering Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (35)
Show source-provided references
1. Plane stress analysis of a scarf joint10.1016/0020-7683(76)90032-9 ↗
2. The adhesive scarf joint in pure bending10.1016/0020-7403(76)90003-5 ↗
3. End effects in scarf joints10.1016/0266-3538(85)90034-X ↗
4. Strength of adhesively bonded scarf joints between glass fiber-reinforced plastics and metals10.1016/0143-7496(90)90104-6 ↗
5. Non-linear analysis of a metal-to-composite scarf joint10.1016/0020-7403(91)90052-5 ↗
6. An improved 2D model for bonded composite joints10.1016/j.ijadhadh.2001.06.001 ↗
7. Failure of aerospace composite scarf-joints subjected to uniaxial compression10.1016/j.msea.2005.08.033 ↗
8. Tensile failure of adhesively bonded CFRP composite scarf joints10.1016/j.mseb.2006.02.046 ↗
9. Parametric study of scarf joints in composite structures10.1016/j.compstruct.2006.04.053 ↗
10. Three-dimensional asymptotic stress field in the vicinity of an adhesively bonded scarf joint interface10.1016/j.compstruct.2008.10.002 ↗
11. Comparison between experimental and numerical study of the adhesively bonded scarf joint and double scarf joint: influence of internal singularity created by geometry of the double scarf joint on the damage evolution10.1016/j.ijadhadh.2009.01.006 ↗
12. Stress analysis and strength evaluation of scarf adhesive joints subjected to static tensile loadings10.1016/j.ijadhadh.2010.02.002 ↗
13. Design and analysis of test coupons for composite blade repair10.1016/S0263-8223(97)80011-6 ↗
14. Scarf repairs to highly strained graphite/epoxy structure10.1016/S0143-7496(98)00031-1 ↗
15. Improved design methods for scarf repairs to highly strained composite aircraft structure10.1016/j.compstruct.2006.04.091 ↗
16. On the design methodology of scarf repairs to composite laminates10.1016/j.compscitech.2007.05.045 ↗
17. Modelling the tensile fracture behaviour of CFRP scarf repairs10.1016/j.compositesb.2008.10.008 ↗
18. Micrographic studies on adhesively bonded scarf repairs to thick composite aircraft10.1016/j.compositesa.2008.12.011 ↗
19. Optimization of a composite scarf repair patch under tensile loading10.1016/j.compositesa.2009.04.033 ↗
20. Numerical evaluation of three-dimensional scarf repairs in carbon–epoxy structures10.1016/j.ijadhadh.2009.11.001 ↗
21. Traction-separation laws for progressive failure of bonded scarf repair of composite panel10.1016/j.compstruct.2010.10.015 ↗
22. Analysis of composite-to-metal joints with bondline flaws10.1016/0266-3538(85)90011-9 ↗
23. Fracture of interface cracks under combined loading10.1016/S0013-7944(96)00111-7 ↗
24. An experimental investigation of failure initiation in bonded joints10.1016/S1359-6454(98)00200-6 ↗
25. Interfacial mixed-mode fracture of adhesive bonds undergoing large deformation10.1016/S0020-7683(03)00398-6 ↗
26. An approach to the development of meaningful design rules for fatigue-loaded CFRP components10.1016/0010-4361(74)90546-1 ↗
27. On the behavior of bonded joints in composite material structures10.1016/0013-7944(75)90065-X ↗
28. Fatigue research on bonded carbon fibre composite/metal joints10.1016/0010-4361(77)90112-4 ↗
29. Stress distribution in carbon fibre-reinforced plastic joints10.1016/0010-4361(80)90021-X ↗
30. Optimal tubular adhesive-bonded lap joint of the carbon fiber epoxy composite shaft10.1016/0263-8223(92)90016-6 ↗
31. Fatigue failure criterion of adhesively bonded CFRP/metal joints under multiaxial stress conditions10.1016/S1359-835X(97)00096-1 ↗
32. Evaluation of the fatigue strength of adhesively bonded CFRP/metal single and single-step double-lap joints10.1016/S0266-3538(99)00028-7 ↗
33. Residual performance of scarf patch-repaired pultruded shapes initially impact damaged10.1016/S0263-8223(01)00016-2 ↗
34. Fatigue behavior of integrally fabricated joints between titanium matrix composite and titanium alloy10.1016/j.compstruct.2006.02.032 ↗
35. ANSYS use’s manual. Release 8.1. Swanson Analysis System Inc.; 2003.