Influence of hot corrosion on low cycle fatigue behavior of nickel base superalloy SU 263

Abstract The influence of hot corrosion on low cycle fatigue behavior is studied by conducting fatigue tests at 800 °C in air on bare and salt-coated (90%Na 2 SO 4 + 10%NaCl) specimens. This was followed by extensive scanning electron microscopic (SEM) examinations. Significant reduction in fatigue life is observed across all values of Δ e t /2 for the salt-coated specimens in comparison with bare specimens. SEM examination reveals that the fused salt mixture sporadically removes the protective chromium oxide layer and exposes the substrate. Subsequent SEM analysis reveals that severe grain boundary oxidation leads to grain boundary cracking and provides numerous sites for fatigue crack nucleation and growth.